Electric heating alloy material with excellent high-temperature oxidation resistance and preparing method for material

A technology for resisting high temperature oxidation and electrothermal alloys, applied in the field of steel alloy materials, can solve the problems of high price and difficult to meet the service temperature, and achieve the effects of improving oxidation resistance, overcoming high temperature embrittlement, and enhancing high temperature corrosion resistance.

Active Publication Date: 2015-12-16
江苏金达电热电器有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If Ni-Cr alloy is used instead of Fe-Cr-Al alloy, the service temperature is difficult to meet; if it is replaced by refractory metal or non-metal electric heating element, the price is expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric heating alloy material with excellent high-temperature oxidation resistance and preparing method for material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] In this embodiment, the composition and mass percentage of the electrothermal alloy material with excellent high-temperature oxidation resistance are as follows:

[0016] Cr21.23%

[0017] Al6.03%

[0018] Co1.33%

[0019] Zr0.14%

[0020] Rare earth Y0.04%

[0021] Nb0.43%

[0022] Mn0.23%

[0023] Si0.18%

[0024] C0.016%

[0025] N0.015%

[0026] S0.008%

[0027] P0.009%

[0028] Fe balance

[0029] Vacuum induction smelting is adopted, after comprehensive measurement calculation and batching smelting, casting and molding, and then hot forging, hot rolling, recrystallization heat treatment, cold rolling and cold drawing, and finally obtained Zr and rare earth Y alloy elements with excellent high temperature resistance An electrothermal alloy material with oxidation performance, its oxidation weight gain is about 6.98mg / cm after isothermal oxidation at 1300°C for 360 hours 2 , and its oxidation weight gain curve follows a parabolic law.

Embodiment 2

[0031] In this embodiment, the electrothermal alloy material does not contain Zr and rare earth Y alloy elements, and the composition and weight percentage of the electrothermal alloy material are as follows:

[0032] Cr21.34%

[0033] Al5.98%

[0034] Co1.41%

[0035] Nb0.48%

[0036] Mn0.21%

[0037] Si0.19%

[0038] C0.016%

[0039] N0.017%

[0040] S0.009%

[0041] P0.007%

[0042] Fe balance

[0043] Vacuum induction smelting is adopted, after comprehensive measurement and batching smelting, casting and forming, and then hot forging, hot rolling, recrystallization heat treatment, cold rolling and cold drawing, and finally the electrothermal alloy material without Zr and rare earth Y alloy elements is obtained. , its oxidation weight gain is about 12.17mg / cm after isothermal oxidation at 1300°C for 360 hours 2 , and its oxidation weight gain curve also follows the parabolic law.

[0044] see figure 1 As shown, the oxidation weight gain of the electrothermal all...

Embodiment 3

[0046] In this embodiment, the composition and mass percentage of the electrothermal alloy material with excellent high-temperature oxidation resistance are as follows:

[0047] Cr22.65%

[0048] Al5.68%

[0049] Co0.6%

[0050] Zr0.18%

[0051] Rare earth Y0.04%

[0052] Nb0.12%

[0053] Mn0.33%

[0054] Si0.18%

[0055] C0.029%

[0056] N0.015%

[0057] S0.008%

[0058] P0.009%

[0059] Fe balance

[0060] Vacuum induction smelting is adopted. After comprehensive measurement calculation and batch smelting, casting is formed, and then hot forging, hot rolling, recrystallization heat treatment, cold rolling and cold drawing are finally obtained. It contains Zr and rare earth Y alloy elements with excellent high temperature resistance. An electrothermal alloy material with oxidation performance, its oxidation weight gain is about 7.39mg / cm after isothermal oxidation at 1300°C for 360 hours 2 , and its oxidation weight gain curve follows a parabolic law.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an electric heating alloy material with excellent high-temperature oxidation resistance and a preparing method for the material. The electric heating alloy material comprises, by mass percent, not larger than 0.06% of C, 19.5% to 23.5% of Cr, 5.5% to 6.5% of Al, not larger than 0.03% of N, not larger than 0.5% of Si, not larger than 0.5% of Mn, not larger than 0.03% of P, not larger than 0.03% of S, 0.5% to 2.5% of Co, 0.1% to 1.0% of Nb, 0.1% to 0.25% of Zr, 0.02% to 0.2% of Y and the balance Fe and inevitable impurities. A vacuum induction smelting technology is adopted, casting moulding is achieved after smelting, and the material is finally prepared through hot forging, hot rolling, recrystallizing heat treatment, cold rolling and cold drawing. The electric heating alloy material overcomes high-temperature embrittlement of an existing Fe-Cr-Al alloy and improves oxidation resistance, heat resistance of the material is improved, the high-temperature oxidation resistance is enhanced, and the excellent comprehensive performance of the material is achieved.

Description

technical field [0001] The invention belongs to the technical field of iron and steel alloy materials, and in particular relates to an electrothermal alloy material and a preparation method thereof. Background technique [0002] Fe-Cr-Al electric heating alloy belongs to ultra-high temperature electric heating alloy, because the alloy contains a large amount of chromium and aluminum elements, the alloy has excellent high temperature oxidation resistance. Fe-Cr-Al electrothermal alloy is the most widely used electrothermal alloy in my country. It has good heat resistance, high temperature oxidation resistance, large resistivity coefficient, small resistance temperature coefficient, stable power, and forms dense The Al2O3 and Cr2O3 oxide films play a good protective role and are low in price. They are mainly used to manufacture various medium and high temperature electric furnace heating elements. High resistivity can effectively convert electrical energy into thermal energy, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/30C22C33/06C21D8/00
Inventor 倪高金肖学山刘青欢
Owner 江苏金达电热电器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap