High-strength and high-plasticity high manganese steel material and machining method thereof

A processing method and high manganese steel technology, applied in high manganese steel, high plasticity high manganese steel materials and their processing, high strength fields, can solve problems such as plasticity decline, achieve tensile strength and plasticity improvement, easy to achieve, The effect of simple processing technology

Active Publication Date: 2015-12-30
YANSHAN UNIV
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Initial research found that the nano-grain can improve the strength of the material, but the plasticity is greatly reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and high-plasticity high manganese steel material and machining method thereof
  • High-strength and high-plasticity high manganese steel material and machining method thereof
  • High-strength and high-plasticity high manganese steel material and machining method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~ Embodiment 5

[0031] The composition of the high manganese steel described in Example 1 is calculated by weight percentage: Mn34.5, C0.04%, S≤0.01%, P≤0.008%, and the rest is Fe and unavoidable impurities. The content of sulfur and phosphorus is restrictive. The specific processing steps are:

[0032] A. According to the above-mentioned component distribution ratio of high manganese steel, calculate the feeding ratio, melt the ingredients in a power frequency electric induction furnace, and smelt the ingredients into steel ingots in a positive argon pressure environment in the furnace to prevent Mn from volatilizing during the smelting process.

[0033] B. Post-treatment of steel ingots: keep the steel ingots in step A for heat treatment at 1150°C~1200°C for 2~4 hours, then transfer to room temperature, and homogeneously complete solution treatment in a water quenching pool; after solution treatment, The full dissolution of each phase in the ingot is conducive to improving the toughness an...

Embodiment 6~ Embodiment 9

[0051] Different from Example 1, the composition ratio of high manganese steel in step A is: Mn32, C0.04%, S≤0.01%, P≤0.008%, and the rest are different from Fe and unavoidable impurities; in step D, The annealing temperature is different, see Table 2 for details. According to the XRD test, they are all austenite structure.

[0052] Table 2 embodiment 6~10 test data

[0053]

[0054] From Examples 6 to 10, it can be seen that partial recrystallization is used to obtain a mixed structure of coarse grains (grain size greater than about 5 microns) and ultrafine grains (size less than 1 micron), and the volume fraction of ultrafine grains is controlled at 20 ~30%, the plasticity of the strength of high manganese steel not only did not decrease but increased, which increased the strength and plasticity of high manganese steel.

Embodiment 11~14

[0056] A. According to the weight percentage of high manganese steel, it is Mn30%, C0.15%, S≤0.008%, P≤0.008%, Si≤0.01%, Cr7%, Ni0.25%, and the rest is Fe; calculate the feeding ratio and smelt into steel ingots; and electroslag remelting treatment.

[0057] B. Post-treatment of steel ingots: heat-treat the steel ingots in step A at 1150°C~1200°C for 2~4 hours, then transfer to room temperature, and homogenize in a water quenching pool to complete solution treatment.

[0058] C. Blanking and rolling into plates: the steel ingots treated in step B are heated to 900~1000°C, and then hot-rolled into rough sheets with a thickness of 10~20mm. The final rolling temperature is not lower than 900°C; Keep at ℃~1100℃ for 1~2 hours, then transfer to room temperature and water quenching tank for homogenization. Homogenization after hot rolling can eliminate stress concentration points caused by hot rolling.

[0059] Step D: the rough plate after hot rolling is cold-rolled at room temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength and high-plasticity high manganese steel material and a machining method thereof. The weight percentage of manganese in high manganese steel is 30-36%, and ultra-fine grains with the grain size smaller than 1 micrometer in the high manganese steel account for 20-30% of the total grain volume. With the help of the annealing treatment technology, mixed microstructure of coarse grains with the grain size larger than about 5 micrometers and ultra-fine grains with the grain size smaller than 1 micrometer is obtained, the grain boundary strengthening effect is rapidly enhanced, and the enhancement effect is improved by 10 times compared with the expected grain nano-crystallization effect; while the strengthening effect is rapidly enhanced, plasticity of the material is improved instead of being lowered.

Description

Technical field [0001] The invention is a field of steel materials and its processing and preparation, involving a kind of high -manganese steel, especially a high -strength, high -plastic high manganese steel material and its processing methods. Background technique [0002] It is well known that refining grains is an important way to improve the strength of steel materials, reduce the toughness and crispy transformation temperature, and increase toughness.An important strategy for the research and exploration of low -temperature manganese steel is to refine the grain to optimize the organization and performance under the premise of unchanging composition.Early research found that grain nanochamction can achieve improvement of material strength, but plasticity has decreased significantly.This shows that simply refining grains cannot work. Invention content [0003] The technical problem to be solved by the present invention is to provide a method that improves the strength and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/58C21D8/02
Inventor 王玉辉黄晓旭王天生彭艳
Owner YANSHAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap