Regulation method of generation of oxidized cellulose in ramie oxidizing and degumming process

A technology of oxidizing cellulose and oxidative degumming, which is applied in the direction of producing bast fiber by chemical method, so as to achieve the effect of optimizing control, saving energy and chemical consumption, and reducing fiber damage

Inactive Publication Date: 2016-01-13
DONGHUA UNIV
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are relatively few reports in relevant literature and patents on this aspect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Regulation method of generation of oxidized cellulose in ramie oxidizing and degumming process
  • Regulation method of generation of oxidized cellulose in ramie oxidizing and degumming process
  • Regulation method of generation of oxidized cellulose in ramie oxidizing and degumming process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for regulating the generation of oxidized cellulose in the process of oxidative degumming of ramie is as follows:

[0026] With hydrogen peroxide 1.0kg, sodium benzoate 0.5kg, urea 0.4kg, sodium tripolyphosphate 0.3kg, sodium polyacrylate 0.3kg, add 97.5kg water and be made into degumming liquid (the mass ratio of ramie hemp and degumming liquid is 1: 10). Immerse 10 kg of ramie raw material in the degumming solution, adjust the pH value of the degumming solution to 10.0 with 0.1 mol / L NaOH solution, and continuously stir the mixture of ramie raw material and degumming solution at a speed of 200 rpm with a magnetic stirrer. Raise the temperature from room temperature to 85°C at a rate of 2°C / min, keep it at this temperature for 100min, and use the oxidizing properties of peroxide to fully remove the gum in the raw ramie. As the reaction progressed, the ramie fibers in the degumming process were sampled at different time points, and the functional group content...

Embodiment 2

[0033] A method for regulating the generation of oxidized cellulose in the process of oxidative degumming of ramie is as follows:

[0034] With sodium percarbonate 0.2kg, acetanilide 0.05kg, urea 0.05kg, sodium dodecylbenzenesulfonate 0.05kg, sodium tartrate 0.05kg, add 99.6kg water and be made into degumming liquid (the mass ratio of ramie raw hemp and degumming liquid is 1:10). Immerse 10kg of ramie raw material in the degumming solution, adjust the pH value of the degumming solution to 14.0 with 0.1mol / L NaOH solution, and continuously stir the mixture of ramie raw material and degumming solution at a speed of 200rpm with a magnetic stirrer. Raise the temperature from room temperature to 50°C at a rate of 1°C / min, keep it at this temperature for 150min, and use the oxidizing property of peroxide to fully remove the gum in the raw ramie. As the reaction progressed, the ramie fibers in the degumming process were sampled at different time points, and the functional group cont...

Embodiment 3

[0039] A method for regulating the generation of oxidized cellulose in the process of oxidative degumming of ramie is as follows:

[0040] With urea peroxide 0.8kg, sodium citrate 0.4kg, thiourea 0.2kg, sodium metaphosphate 0.2kg, sodium polyacrylate 0.1kg, add 98.3kg water and be made into degumming liquid (the mass ratio of ramie hemp and degumming liquid is 1 : 10). Immerse 10kg of ramie raw material in the degumming solution, adjust the degumming solution with 0.1mol / L NaOH solution p H value to 8.0, continuously stir the mixture of ramie raw material and degumming solution with a magnetic stirrer at a speed of 200rpm. Raise the temperature from room temperature to 100°C at a rate of 5°C / min, keep it at this temperature for 40 minutes, and use the oxidizing property of peroxide to fully remove the gum in the raw ramie. As the reaction progressed, the ramie fibers in the degumming process were sampled at different time points, and the functional group content of the sampl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Strengthaaaaaaaaaa
Strengthaaaaaaaaaa
Strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a regulation method of generation of oxidized cellulose in a ramie oxidizing and degumming process. The regulation method includes the following steps: preparing a degumming liquid and mixing raw hemp of ramie with the degumming liquid; regulating the pH of the degumming liquid; heating and stirring the mixture to fully removal colloid through oxidizing property of peroxides; on-line detecting generation quantity of the oxidized cellulose; and optimizing and regulating the pH, reaction temperature, reaction time and chemical reagent concentration in real time to control the aldehyde group content in the oxidized cellulose to be 15-40 [mu]mol / g and the carboxyl group content to be 120-200 [mu]mol / g, so that the fiber crystallization degree, polymerization degree, strength, breaking elongation and fineness of the prepared fine dry ramie fiber are maximum and the degumming efficiency and the physical mechanical performance are best within the ranges of the parameters. The method can increase degumming efficiency and reduce fiber damage, achieves best degumming effect, achieves optimum control in the preparation process of the ramie fiber, and has important theoretical meaning and application value.

Description

technical field [0001] The invention relates to a method for regulating the generation of oxidized cellulose in the process of oxidative degumming of ramie, and belongs to the technical field of oxidative degumming of hemp fibers and characterization and regulation of cellulose oxidation in analytical chemistry in the field of textiles. Background technique [0002] With the continuous depletion of non-renewable resources such as oil, natural gas, and coal, people pay more and more attention to green and environmentally friendly materials. Cellulose and its derivatives are receiving more and more attention because of their wide distribution, high content, good biocompatibility, degradability, and environmental friendliness. Plant fibers are fibers obtained from seeds, fruits, stems, leaves and other parts of plants, and are natural renewable fibers. Among all kinds of plant fibers, ramie is a kind of hemp fiber with excellent quality. After the raw hemp is degummed and refi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01C1/02
Inventor 李召岭周佳佳孟超然郁崇文杨建平丁金花刘凤明
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com