Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Shuttering hardening agents

A technology of hardener and mold shell, applied in casting molding equipment, molds, cores, etc., can solve problems such as inability to completely overcome defects, and achieve the effect of shortening production cycle, not easy to delaminate, and increasing penetration speed.

Inactive Publication Date: 2016-02-10
TIANJIN RONGHENG GROUP
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Although the above-mentioned shell hardening agent uses crystalline aluminum chloride, it also uses ammonium chloride at the same time, so it cannot completely overcome the defects of using ammonium chloride as the shell hardening agent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Processing hardener 100kg:

[0028] Take 15 kg of hexahydrate crystalline aluminum chloride, 25 kg of dihydrate flake calcium chloride, 1.5 kg of anhydrous boric acid, 0.15 kg of penetrant and 1 kg of wetting agent.

[0029] Pour 57.35kg of clean water into the stirring tank, add the above-mentioned raw materials one by one under stirring and continue stirring for 30 minutes, then stop the machine, pour it into a large tank through the anticorrosive pump, and use it after 2 hours of melting reaction.

Embodiment 2

[0031] Processing hardener 100kg:

[0032] Take 10 kg of hexahydrate crystalline aluminum chloride, 22 kg of dihydrate flake calcium chloride, 2 kg of anhydrous boric acid, 0.1 kg of penetrant and 2 kg of wetting agent.

[0033] Inject 63.9kg of clean water into the stirring tank, add the above-mentioned raw materials one by one under stirring and continue stirring for 30 minutes, then stop the machine, pour it into a large tank through the anticorrosive pump, and use after 2 hours of melting reaction.

Embodiment 3

[0035] Processing hardener 100kg:

[0036] Take 12 kg of hexahydrate crystalline aluminum chloride, 21 kg of dihydrate flake calcium chloride, 1.75 kg of anhydrous boric acid, 0.125 kg of penetrant and 1.5 kg of wetting agent.

[0037] Pour 63.625kg of clean water into the stirring tank, add the above-mentioned raw materials one by one under stirring and continue stirring for 30 minutes, then stop the machine, pour it into a large tank through the anticorrosive pump, and use it after 2 hours of melting reaction.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to shuttering hardening agents. The shuttering hardening agents mainly include, by weight, 10-15% of hexahydrate crystallization of aluminum chloride, 22-25% of dihydrate flaky calcium chloride, 1.5-2% of anhydrous boric acid, 0.1-0.15% of permeating agents and the balance clear water. The hexahydrate crystallization of aluminum chloride and the dihydrate flaky calcium chloride serve as the main materials of the hardening agents, so that the defect that the work conditions are seriously worsened as ammonium chloride is used as the main materials of shuttering hardening agents is fundamentally overcome, and the other properties are better than those of the ammonium chloride hardening agents. The shuttering hardening agents have the characteristics of being high in hardening speed, shortening the process and shortening the production period, avoid environmental pollution and obviously improve economic benefits.

Description

Technical field [0001] The invention relates to a mold shell hardener for water glass investment casting. Background technique [0002] The precision casting industry is faced with two challenges: one is the continuous improvement of the quality of castings; the other is the increasingly stringent requirements for environmental protection, clean production and human health. Therefore, a higher level of hardener for precision casting molds is proposed. Claim. [0003] At present, most of the precision casting industry uses water glass as the binder, and ammonium chloride or magnesium chloride or aluminum chloride as the hardener. [0004] Ammonium chloride has severely deteriorated working conditions due to the production of ammonia gas, and the mold shell has poor bonding strength and quality cannot be effectively controlled; the viscosity of magnesium chloride solution is large, which affects the hardening and drying speed, and is easy to produce due to the high content of impuriti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C1/10B22C9/04
Inventor 庄朝荣庄合义庄朝勇董树东陈术国
Owner TIANJIN RONGHENG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com