Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Low-heat cement capable of efficiently utilizing industrial waste gypsum

A technology of industrial waste gypsum and low-heat cement, which is applied in the field of cement materials, can solve the problems of rare production and application, low early strength of low-heat cement, and difficulty in meeting the construction speed, etc., to overcome low early strength, good early strength, and realize The effect of resource utilization

Active Publication Date: 2016-02-10
宁夏赛马水泥有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Low-heat cement has such excellent performance, but it is rarely produced and applied in my country's building materials industry at present. The main reason is that the early strength of low-heat cement is lower than that of general-purpose Portland cement, which is difficult to meet the requirements of construction speed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-heat cement capable of efficiently utilizing industrial waste gypsum

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A low-heat cement capable of efficiently utilizing industrial waste gypsum, the preparation method of which is as follows:

[0019] 1. Preparation of cement raw meal:

[0020] Dosing according to the following mass parts: 55 parts of limestone, 0.5 part of bauxite, 5 parts of clay, 0.5 part of sulfuric acid slag, 0.2 part of fluorite, 3 parts of barium slag, 8 parts of processed industrial waste gypsum, and various The components are uniformly mixed and ground to 150-200 mesh to obtain cement raw meal. The treatment method of the treated industrial waste gypsum is as follows: drying at a high temperature of 350° C. for 30 minutes.

[0021] 2. Preparation of cement clinker

[0022] The mixed cement raw meal is placed in a rotary kiln for calcination, the calcination temperature is 1330°C, and the calcination time is 100min to obtain cement clinker;

[0023] 3. Preparation of cement

[0024] Take 70 parts of burnt cement clinker, add 20 parts of industrial waste gypsu...

Embodiment 2

[0026] A low-heat cement capable of efficiently utilizing industrial waste gypsum, the preparation method of which is as follows:

[0027] 1. Preparation of cement raw meal:

[0028] Dosing according to the following mass parts: 75 parts of limestone, 3 parts of bauxite, 15 parts of clay, 1.5 parts of sulfuric acid slag, 0.6 part of fluorite, 8 parts of barium slag, 10 parts of processed industrial waste gypsum, various The components are uniformly mixed and ground to 150-200 mesh to obtain cement raw meal. The treatment method of the treated industrial waste gypsum is: drying at a high temperature of 350° C. for 40 minutes.

[0029] 2. Preparation of cement clinker

[0030] Put the mixed cement raw meal in a rotary kiln for calcination, the calcination temperature is 1350°C, and the calcination time is 90min to obtain cement clinker;

[0031] 3. Preparation of cement

[0032] Take 80 parts of burnt cement clinker, add 15 parts of industrial waste gypsum and 0.5 part of re...

Embodiment 3

[0034] A low-heat cement capable of efficiently utilizing industrial waste gypsum, the preparation method of which is as follows:

[0035] 1. Preparation of cement raw meal:

[0036] Dosing according to the following mass parts: 90 parts of limestone, 4.5 parts of bauxite, 15 parts of clay, 1.5 parts of sulfuric acid slag, 0.6 part of fluorite, 8 parts of barium slag, 10 parts of processed industrial waste gypsum, and various The components are uniformly mixed and ground to 150-200 mesh to obtain cement raw meal. The treatment method of the treated industrial waste gypsum is: drying at a high temperature of 350° C. for 45 minutes.

[0037] 2. Preparation of cement clinker

[0038] Put the mixed cement raw meal in a rotary kiln for calcination, the calcination temperature is 1350°C, and the calcination time is 90min to obtain cement clinker;

[0039] 3. Preparation of cement

[0040] Take 85 parts of burnt cement clinker, add 20 parts of industrial waste gypsum and 0.6 part o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses low-heat cement capable of efficiently utilizing industrial waste gypsum. The cement is prepared through the steps of preparing cement raw materials from limestone, bauxite, clay, pyrite cinder, fluorite, barium dregs and the processed industrial waste gypsum according to a certain mass ratio, evenly mixing the materials, grinding the materials into raw material powder, sintering the raw material powder, and adding industrial waste gypsum and an adjusting agent to sintered cement clinker. The utilization rate of the industrial waste gypsum in cement production is greatly increased; in the product formed through a formula, the C3S content is decreased, the C2S content is increased, and therefore hydration heat is low; meanwhile, by introducing early-strengthen type sulphoaluminate minerals and adding appropriate amounts of the industrial waste gypsum and the adjusting agent, hydration is promoted, high early strength is achieved, the defect that ordinary low-heat cement is low in early strength is overcome, and the application range of the low-heat cement is widened.

Description

technical field [0001] The invention belongs to the technical field of cement materials, in particular to a low-heat cement capable of efficiently utilizing industrial waste gypsum. Background technique [0002] With the continuous development of my country's industry, the consumption of natural gypsum and other resources continues to rise. Due to the limited reserves of natural gypsum, its storage capacity is getting smaller and smaller, and its price is also increasing year by year. Industrial waste gypsum is the industrial waste residue in the process of industrial production. There are many types. The waste residue produced by using phosphate ore and sulfuric acid to produce phosphoric acid is phosphogypsum; the flue gas generated after the combustion of sulfur-containing fuels (coal, oil, etc.) is desulfurized and purified. The industrial by-product gypsum obtained after treatment is desulfurized gypsum; the citric acid produced by industrial microbial fermentation main...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/21
CPCY02P40/10
Inventor 芦令超刘博王守德宫晨琛程新
Owner 宁夏赛马水泥有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com