Preparation method of inorganic filler used in production of wood-plastic material
A technology of wood-plastic materials and inorganic fillers, applied in the field of inorganic fillers, can solve the problems of narrow utilization range and difficulty in the utilization of titanium gypsum, and achieve the effect of improving hardness and strength and reducing raw material costs of wood-plastic products
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0012] Example 1: Take 1 liter of titanium gypsum slurry obtained by adding lime to titanium dioxide produced by sulfuric acid method, add a certain amount of calcium carbide slag under stirring to adjust the slurry, measure the pH value with a pH meter, and stop adding when the pH value reaches 8; After filtering, the obtained filter cake is dried and dehydrated at 400°C for 50 minutes to obtain dried titanium gypsum; the dried titanium gypsum is added to the coupling agent according to the mass ratio of 1:0.01, and mixed uniformly; the mixture obtained in the previous step After ball milling and passing through an 800-mesh sieve, modified gypsum powder that can be used as an inorganic filler for wood-plastic materials is obtained.
Embodiment 2
[0013] Example 2: Take 1 liter of titanium gypsum slurry obtained by adding lime to titanium dioxide produced by sulfuric acid method, add a certain amount of calcium carbide slag under stirring to adjust the slurry, measure the pH value with a pH meter, and stop adding when the pH value reaches 8; After filtering, the obtained filter cake was dried and dehydrated at 500°C for 30 minutes to obtain dried titanium gypsum; the dried titanium gypsum was added to the coupling agent according to the mass ratio of 1:0.03, and mixed uniformly; the mixture obtained in the previous step After ball milling and passing through an 800-mesh sieve, modified gypsum powder that can be used as an inorganic filler for wood-plastic materials is obtained.
Embodiment 3
[0014] Example 3: Take 1 liter of titanium gypsum slurry obtained by adding lime to titanium dioxide produced by sulfuric acid method, add a certain amount of calcium carbide slag or red mud to adjust the slurry under stirring conditions, measure the pH value with a pH meter, and stop adding when the pH value reaches 8.5; The slurry is filtered, and the obtained filter cake is dried and dehydrated at 450°C for 40 minutes to obtain the dried titanium gypsum; the dried titanium gypsum is added to the coupling agent according to the mass ratio of 1:0.05, and the mixture is evenly mixed; The obtained mixture is ball milled and passed through an 800-mesh sieve to obtain modified gypsum powder that can be used as an inorganic filler for wood-plastic materials.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap