Self-healing material

A technology of composite materials and composite materials, applied in the field of self-healing materials, can solve the problems of high manufacturing cost, difficult to popularize, complex structure, etc., and achieve the effects of low cost, simple manufacturing process and remarkable self-healing performance.

Inactive Publication Date: 2016-04-20
CHONGQING LEHU TECH CO LTD
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The main disadvantages of current self-healing materials are complex structures, high manufacturing costs, and difficulty in popularization.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1 self-healing material formula

[0023] The self-healing material of the present invention mainly consists of the following raw materials: 20g of diatomite; 40g of paraffin; 70g of polymer composite material made of carbon, glass and resin; 70g of dicyclopentadiene liquid; 10g of Grubbs catalyst .

Embodiment 2

[0024] Embodiment 2 self-healing material formula

[0025] The self-healing material of the present invention mainly consists of the following raw materials: 50g of diatomite; 80g of paraffin; 100g of polymer composite material made of carbon, glass and resin; 100g of dicyclopentadiene liquid; 30g of Grubbs catalyst .

Embodiment 3

[0026] Embodiment 3 self-healing material formula

[0027] The self-healing material of the present invention mainly consists of the following raw materials: 40g of diatomite; 60g of paraffin; 70g of polymer composite material made of carbon, glass and resin; 60g of dicyclopentadiene liquid; 20g of Grubbs catalyst .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a self-healing material which is mainly prepared from a porous material, paraffin, a polymer composite material, dicyclopentadiene liquid and a Grubbs' catalyst, wherein the polymer composite material is prepared from carbon, glass and resin. The porous material fully absorbs the dicyclopentadiene liquid, the porous material containing the dicyclopentadiene liquid is wrapped in the paraffin to be prepared into microcapsules, the microcapsules are doped into the polymer composite material containing the Grubbs' catalyst, and the self-healing material is obtained. The self-healing material has the advantages that cost is low, the manufacturing technology is simple, and the self-healing performance is remarkable.

Description

technical field [0001] The present invention designs building materials, and in particular relates to a self-healing material. Background technique [0002] Existing self-healing materials mainly include three parts: 1. Composite materials, most of which are epoxy polymer composite materials. 2. Repairing agent sealed with microcapsules, which is an adhesive used in the repair of micro-cracks formed on composite materials. The repair compound is a liquid called dicyclopentadiene, or DCPD. The fluid is encapsulated with small blisters that can be diffused throughout the composite. Catalyst In order for polymerization to occur, the repair agent must come into contact with a catalyst. Catalyst has a patented product called Grubb Catalyst for this self-healing material. It is important that the catalyst and repair compound be separated before they can be used to close cracks. When a microcrack forms in a composite material, it spreads across the surface of the material. So...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L101/00C08L91/06C08K13/06C08K9/04C08K3/34C08K3/04C08K3/40
CPCC08L101/00
Inventor 蒋小辉
Owner CHONGQING LEHU TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products