A kind of low color difference polyester differential shrinkage composite yarn and its preparation method

A technology of different shrinkage and composite yarn, which is applied in the direction of single-component polyester rayon, dyeing method, rayon manufacturing, etc. It can solve the problems of troublesome dyeing and post-processing, hindering liquid flow circulation, and not easy to wash off, etc. Achieve the effects of eliminating aurora defects, excellent shading performance, and excellent dyeing performance

Active Publication Date: 2017-12-12
JIANGSU HENGLI CHEM FIBER
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the temperature drops, like dyes, the solubility of oligomers in water decreases sharply with the decrease of temperature, so they will crystallize and precipitate, and the precipitated dyes and oligomers are attached to the surface of the fiber and are not easy to wash off, thus affecting dyeing and post-processing. It brings a lot of trouble. During the dyeing process, the aggregated dyes and oligomers adhere to the surface of the fiber, and dye spots, spots, and color flowers appear.
Deposits in the pipes and valves of the dyeing machine, hindering the circulation of the liquid flow, resulting in difficulty in dyeing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low color difference polyester differential shrinkage composite yarn and its preparation method
  • A kind of low color difference polyester differential shrinkage composite yarn and its preparation method
  • A kind of low color difference polyester differential shrinkage composite yarn and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] A method for preparing low-chromatic-difference polyester different-shrinkage composite yarn, the main process comprising:

[0072] (1) Preparation of catalyst magnesium ethylene glycol:

[0073] Add ethylene glycol into the single-chamber electrolytic cell, the supporting electrolyte is magnesium chloride, the metal magnesium block is the anode, and the cathode is graphite; connect direct current, the initial voltage is 6V, the cathode current density is 150mA, and electrolyze for 10 hours at 50°C. Take out the electrode to obtain a white suspension; filter under reduced pressure, wash the white solid with absolute ethanol, and dry to obtain magnesium ethylene glycol;

[0074] (2) Preparation of polyester, including esterification reaction and polycondensation reaction:

[0075] Esterification reaction:

[0076] Use terephthalic acid and ethylene glycol as raw materials, the molar ratio of ethylene glycol to terephthalic acid is 1.2:1, add anti-ether agent sodium ace...

Embodiment 2

[0097] A method for preparing low-chromatic-difference polyester different-shrinkage composite yarn, the main process comprising:

[0098] (1) Preparation of catalyst magnesium ethylene glycol:

[0099] Add ethylene glycol into the single-chamber electrolytic cell, the supporting electrolyte is magnesium chloride, the metal magnesium block is the anode, and the cathode is graphite; connect direct current, the initial voltage is 10V, the cathode current density is 200mA, electrolyze at 60°C for 12 hours, after the electrolysis ends Take out the electrode to obtain a white suspension; filter under reduced pressure, wash the white solid with absolute ethanol, and dry to obtain magnesium ethylene glycol;

[0100] (2) Preparation of polyester, including esterification reaction and polycondensation reaction:

[0101] Esterification reaction:

[0102] Using terephthalic acid and ethylene glycol as raw materials, the molar ratio of ethylene glycol to terephthalic acid is 2.0:1, adding...

Embodiment 3

[0123] A method for preparing low-chromatic-difference polyester different-shrinkage composite yarn, the main process comprising:

[0124] (1) Preparation of catalyst magnesium ethylene glycol:

[0125] Add ethylene glycol into the single-chamber electrolytic cell, the supporting electrolyte is magnesium chloride, the metal magnesium block is the anode, and the cathode is graphite; connect direct current, the initial voltage is 7V, the cathode current density is 160mA, and electrolyze for 11 hours at 55°C. Take out the electrode to obtain a white suspension; filter under reduced pressure, wash the white solid with absolute ethanol, and dry to obtain magnesium ethylene glycol;

[0126] (2) Preparation of polyester, including esterification reaction and polycondensation reaction:

[0127] Esterification reaction:

[0128] Using terephthalic acid and ethylene glycol as raw materials, the molar ratio of ethylene glycol to terephthalic acid is 1.5:1, adding anti-ether agent sodiu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
coefficient of variationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a low-color difference polyester different-shrinkage composite yarn and a preparation method thereof. The low-color-difference polyester different-shrinkage composite yarn is obtained by compounding polyester POY yarn and polyester FDY yarn; the polyester POY yarn and polyester yarn Ester FDY yarn is obtained by spinning polyester after melting and washing. The breaking strength of the low-color difference polyester differential shrinkage composite yarn is ≥1.9cN / dtex, the elongation at break is 30.0±5.0%, and the crimp shrinkage rate is 2.50 ±3.0%, the degree of network is 20±5 / m; the color difference ΔE is less than 0.200; the magnesium ethylene glycol in the present invention is relatively mild, its thermal degradation coefficient is very small, the reduction of oligomers in the polymerization process, the dissolution and washing process The oligomers are further reduced, which reduces the occurrence of stains and streaks in polyester fiber dyeing and post-processing heat setting, and ensures fiber level dyeing and rubbing fastness. Different shrinkage composite yarn has excellent shading performance, excellent dyeing performance, high bulkiness and soft hand feeling, and because there are many loops on the surface of the fiber, it also eliminates the aurora defect of chemical fiber filaments.

Description

technical field [0001] The invention belongs to the technical field of polyester preparation, and relates to a low-chromatic-difference polyester different-shrinkage composite yarn and a preparation method thereof, in particular to a polycondensation catalyst using a mixture of ethylene glycol magnesium and ethylene glycol antimony, as well as polyester chips washed with water and Low-color-difference polyester different-shrinkage composite yarns boiled and washed with a solvent-washing agent at 120-130°C and 0.2-0.3 MPa and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) is a polymer with excellent properties. PET is widely used for its high modulus, high strength, crispness, good shape retention, purity and hygiene, and good barrier properties. In the fields of fiber, bottle packaging, film and sheet, etc., the output is increasing year by year, and the industry status has been significantly improved. [0003] PET is a symmetri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10C08G63/183C08G63/83C08G63/86D01D5/08D06P1/16D06P3/54D02G1/18C25B3/13
CPCC08G63/183C08G63/83C08G63/866D01D5/08D01F1/10D01F6/92D02G1/18D06P1/16D06P3/54C08G63/86D01F6/62C25B3/13
Inventor 金管范邵义伟张烨王力军卓怀智丁竹君
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com