Aluminum oxide ceramic sheet processing technology

A kind of alumina ceramics, processing technology, applied in chemical instruments and methods, cleaning methods and utensils, cleaning methods using liquids, etc. Firmness and other issues, to achieve the effect of strong surface adsorption, light weight, and prolong the service life of the equipment

Inactive Publication Date: 2016-05-18
解全义
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much superior. Ordinary ceramic sheets and rubber cannot be bonded together. After using glue, the bond is not firm, and the ceramic sheets need to be processed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A process for treating alumina ceramic sheets, the steps are as follows:

[0023] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0024] (2) Ketone washing: Soak the cleaned ceramic sheet in 50% acetone for half an hour and dry it;

[0025] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 60% sodium carbonate solution for half an hour and dry it.

Embodiment 2

[0027] A process for treating alumina ceramic sheets, the steps are as follows:

[0028] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0029] (2) Ketone washing: Soak the cleaned ceramic sheet in 55% acetone for half an hour and dry it;

[0030] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 65% sodium carbonate solution for half an hour and dry it.

Embodiment 3

[0032] A process for treating alumina ceramic sheets, the steps are as follows:

[0033] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0034] (2) Ketone washing: Soak the cleaned ceramic sheet in 60% acetone for half an hour and dry it;

[0035] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 70% sodium carbonate solution for half an hour and dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an aluminum oxide ceramic sheet processing technology. The aluminum oxide ceramic sheet processing technology comprises the following steps: (1) washing with distilled water: washing the ceramic sheet in 100% pure water, and drying; (2) washing with acetone: immersing the washed ceramic sheet in 50% to 60% acetone, and drying; and (3) washing with alkali: immersing the ceramic sheet washed with the acetone in 60% to 70% sodium carbonate solution, and drying. The aluminum oxide ceramic sheet processing technology has the beneficial effects that the hardness is high, the abrasion resistance is extremely good, the weight is light, the surface adsorption capacity is high and is 10 to 20 of that of the ceramic sheet which is not processed, and the aluminum oxide ceramic sheet is firm and durable after being bonded to rubber by virtue of glue.

Description

technical field [0001] The invention relates to the technical field of alumina ceramic sheet processing, in particular to an alumina ceramic sheet processing process. Background technique [0002] Alumina ceramics: high alumina content, relatively dense structure, and special properties, so it is called special ceramics. Al 2 o 3 The ceramic material is a close-packed hexagonal structure composed of oxygen ions, and aluminum ions fill two-thirds of the octahedral gaps, which is the same stable α-Al as natural corundum. 2 o 3 Structure, so ceramics have high melting point, high hardness, and excellent wear resistance. The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much sup...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/80B08B3/04B08B3/08
CPCC04B41/00B08B3/04B08B3/08C04B41/009C04B41/80
Inventor 解全义
Owner 解全义
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap