Method for blending coking coal by using fat coal with medium and high sulfur content

A coking coal and fat coal technology, applied in the field of metallurgical coke production, can solve the problems that cannot meet the coke quality requirements of large blast furnaces, cannot guarantee the continuous reflectance of vitrinite and coke quality decline, and achieve the protection of high-quality coking Coal resources, coke quality is good, and the effect of reducing coking cost

Active Publication Date: 2016-06-29
ANGANG STEEL CO LTD
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If medium- and high-sulfur fertile coals are simply replaced with other coals in coking coal blending, the vitrinite reflectance of the blended coal cannot be guaranteed to be continuous. At the same time, the sulfur content in the coke made exceeds the standard, which will lead to a decline in the quality of the coke, which cannot meet the needs of large-scale blast furnaces. Coke Quality Requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) The components and weight percentages of coking coal are:

[0024] 1 / 3 coking coal: 14%; medium and high sulfur fat coal: 12%; other fat coal: 15%; caking index G≥78 coking coal 1 # : 10%; caking index G≥78 coking coal 2 # : 8%; caking index 75≤G<78 coking coal: 30%; lean coal: 11%.

[0025] (2) Coal quality indicators of medium and high-sulfur rich coal: average maximum reflectance of vitrinite: 1.195%; volatile matter: 28.44%; process performance indicators: cohesion index G value 92.2, colloidal layer thickness Y value 25.4mm , S td : 2.33%.

[0026] (3) Coal quality index of coking coal: caking index G value: 81.2; colloid layer thickness Y value: 15.5mm; S td : 1.03%.

[0027] (4) The quality of coke made in a coke oven above 6 meters: coke crushing strength M 40 : 88.73%; coke strength CSR after reaction: 62.00%; coke S td : 0.78%.

Embodiment 2

[0029] (1) Coking coal composition and weight percentage:

[0030] 1 / 3 coking coal: 17%; medium and high sulfur fat coal: 16%; other fat coal: 10%; caking index G≥78 coking coal 1 # : 10%; caking index G≥78 coking coal 2 # : 10%; caking index 75≤G# : 10%; caking index 75≤G# : 10%; lean coal: 17%.

[0031] (2) Coal quality indicators of medium and high-sulfur rich coal: average maximum reflectance of vitrinite: 1.167%; volatile matter: 28.36%; process performance indicators: cohesion index G value 91.0, colloidal layer thickness Y value 21.0mm , S td : 2.60%.

[0032] (3) Coal quality index of coking coal: caking index G value: 84.2; colloid layer thickness Y value: 16.9mm; S td : 0.86%.

[0033] (4) The quality of coke made in a coke oven above 6 meters: coke crushing strength M 40 : 89.06%; coke strength CSR after reaction: 66.92%; coke S td : 0.83%.

Embodiment 3

[0035] (1) Coking coal composition and weight percentage:

[0036] 1 / 3 coking coal: 10%; medium and high sulfur fat coal: 18%; other fat coal: 8%; caking index G≥78 coking coal: 30%; caking index 75≤G# : 14%; caking index 75≤G# : 10%; lean coal: 10%.

[0037] (2) Coal quality indicators of medium and high-sulfur rich coal: average maximum reflectance of vitrinite: 1.024%; volatile matter: 31.48%; process performance indicators: cohesive index G value 90.5, colloidal layer thickness Y value 21.0mm , S td : 1.67%.

[0038] (3) Coal quality index of coking coal: caking index G value: 80.4; colloid layer thickness Y value: 17.8mm; S td : 0.78%.

[0039] (4) The quality of coke made in a coke oven above 6 meters: coke crushing strength M 40 : 88.76%; coke strength CSR after reaction: 63.38%; coke S td : 0.66%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
cohesion indexaaaaaaaaaa
cohesion indexaaaaaaaaaa
reflectanceaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for blending coking coal by using fat coal with medium and high sulfur content. The coking coal comprises the following components in percentages by weight: 8%-18% of 1 / 3 coking coal, 10%-20% of fat coal with medium and high sulfur content, 8%-29% of fat coal, 16%-35% of coking coal with coking index G greater than or equal to 78, 19%-36% of coking coal with coking index G greater than or equal to 75 and smaller than 78, and 8%-22% of lean coal. G value of the coking index of the coking coal is 80-85, Y value is 15-19 mm, and Std is 0.65%-1.15%. The coal properties of the fat coal with medium and high sulfur content are as follows: the mean maximum reflectance of vitrinite is 0.90%-1.10%, and volatiles are 26%-32%. Technological performance indexes are as follows: the G value of the coking index is greater than or equal to 86, the Y value of the thickness of a gel layer is greater than or equal to 20 mm, and Std is 1%-3%. The content of produced coke sulfur is below 1.0%, and reaches the level higher than the level of third-level coke, demands of coke using of a large blast furnace can be met completely, the purposes of fully utilizing the coal with medium and high sulfur and protecting high-quality coking coal resources are achieved, and coking cost can be reduced greatly.

Description

technical field [0001] The invention belongs to the technical field of metallurgical coke production, and in particular relates to a coking coal-rock coal blending method using medium- and high-sulfur fertile coal. Background technique [0002] With the increasing application proportion of large-scale blast furnaces, the demand for high-quality coke is also increasing. Therefore, it is required to mix a large amount of moderately metamorphic fat coal and coking coal in coal blending. According to the classification of coal types in my country, coking coal accounts for 27.65%, and non-coking coal accounts for 72.35%. Among coking coals, gas coal: 13.75%, fat coal: 3.53%, main coking coal: 5.81%, lean coal: 4.01%, and other unclassified coal: 0.55%. It can be seen that fat coal is the coal with the least reserves in coking coal in my country, and in the actual coking coal blending process, fat coal and coking coal are mainly used. Therefore, effective utilization of fat coal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10B57/04
Inventor 庞克亮唐复平王明国赵恒波马银华刘冬杰栗红王超李志
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com