Preparation method of high-purity spherical nano molybdenum disulfide

A nano-molybdenum disulfide, spherical technology, applied in the direction of molybdenum sulfide, nanotechnology, nanotechnology, etc., can solve the problem of uneven surface of molybdenum disulfide spheres, and achieve the effects of uniform size, simple reaction process and regular morphology.

Active Publication Date: 2017-09-26
PETROCHINA CO LTD +1
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the surfactant molecules that have not formed micelles in the system exist in the form of ions and are adsorbed on the surface of molybdenum disulfide, resulting in uneven surface of molybdenum disulfide spheres and a wide range of particle size distribution (such as comparative example 1)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-purity spherical nano molybdenum disulfide
  • Preparation method of high-purity spherical nano molybdenum disulfide
  • Preparation method of high-purity spherical nano molybdenum disulfide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The mixed solution (V 无水乙醇 / V 去离子水 =1 / 19), add 2 mL of hydrazine hydrate after stirring evenly, transfer the solution into a high-pressure reactor with a volume of 100 mL after mixing evenly, seal it and place it in a 200°C incubator, keep it warm for 24 hours, cool to room temperature, and use After washing with deionized water and absolute ethanol, place it in a vacuum oven at 70°C for 8 hours to obtain the high-purity spherical nanomolybdenum disulfide required in this case.

[0034] Depend on figure 1 It can be seen that the product is composed of nanospheres with a particle size of about 400nm, the particle size distribution range of the spheres is narrow, the spherical structure is complete, and the dispersibility of the spheres is good.

[0035] Depend on figure 2 The XRD shows that the structure of molybdenum disulfide is 2H-MoS 2 .

Embodiment 2

[0037] The mixed solution (V 无水乙醇 / V 去离子水 =3 / 17), after stirring evenly, add 2mL of hydrazine hydrate, after mixing evenly, move the solution into a 100mL autoclave, seal it and place it in a 200°C incubator, keep it warm for 24h, cool to room temperature, and use After washing with deionized water and absolute ethanol, place it in a vacuum oven at 70°C for 8 hours to obtain the high-purity spherical nanomolybdenum disulfide required in this case. For the experimental results, see image 3 .

Embodiment 3

[0039] The mixed solution (V 无水乙醇 / V 去离子水 =1 / 3), after stirring evenly, add 2mL of hydrazine hydrate, after mixing evenly, transfer the solution into a 100mL autoclave, seal it and place it in a 180°C incubator, keep it warm for 12h, cool to room temperature, and use After washing with deionized water and absolute ethanol, place it in a vacuum oven at 70°C for 8 hours to obtain the spherical nanomolybdenum disulfide required in this case. For the experimental results, see Figure 4 .

[0040] According to the SEM image, the spherical structure of the prepared nanomolybdenum disulfide is complete, and the size distribution is narrow at about 400nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of high-purity spherical molybdenum disulfide. The method comprises the following steps: dissolving ammonium heptamolybdate, thioacetamide, and a surfactant into a solvent, and mixing uniformly; after adding a reducing agent, moving the prepared solution into an autoclave, sealing the autoclave, and The sealed high-pressure reaction kettle is placed in a constant temperature box at 120-250°C, and kept for 3-72 hours; cooled to room temperature, filtered, washed, and dried to obtain spherical nanomolybdenum disulfide. The high-purity nano molybdenum disulfide prepared by the invention has regular shape, uniform and adjustable size, high sphericity, good dispersibility, simple synthesis process, mild conditions, low cost and simple synthesis device. The high-purity nano-spherical molybdenum disulfide prepared by the invention is widely used in the fields of electrode materials, lubricating materials and catalysis, and is expected to be used in industrial production.

Description

technical field [0001] The present invention relates to inorganic nano material molybdenum disulfide (MoS 2 ) preparation field, especially a preparation method of spherical nanomolybdenum disulfide. Background technique [0002] Molybdenum disulfide has good optical, electrical, lubricating, catalytic and other properties, so it has good application potential in electronic detection, solid lubrication, heterogeneous catalysis, gas storage materials and petrochemical industries. Molybdenum disulfide has a typical layered structure, and the layers are combined by weak van der Waals force, which is easy to peel off, and ions are easily inserted between the layers. Each molybdenum atom in the monoatomic layer is surrounded by six sulfur atoms, in the shape of a triangular prism, exposing many Mo-S facets, which can be used as catalytic active centers. Nano-sized molybdenum disulfide has the advantages of quantum size effect, surface effect, and more exposed active centers, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01G39/06B82Y30/00
Inventor 田志坚李敏王冬娥周志远马怀军赵愉生曲炜阎立军
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products