Castable special for 5000T cement kiln coal-injection duct

A castable and coal injection pipe technology, applied in the field of high temperature materials for building materials, can solve problems such as poor workability, castable segregation, uneven organizational structure, etc., to improve corrosion resistance, prolong service life, and improve thermal shock resistance. Effect

Inactive Publication Date: 2016-08-03
张婷
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a castable for coal injection pipe, which can improve the uneven structure of the current castable, and solve the poor workability and the segregation of the castable caused by the poor workability, many pores, and uneven distribution of pores Defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Castable special for 5000T cement kiln coal-injection duct

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A special castable for coal injection pipe of 5000T cement kiln, the weight percentage of its components is:

[0060] Zinc Aluminum Spinel 25%

[0061] Synthetic moissanite 20%

[0062] Brown fused alumina 25%

[0063] Strontium Titanate Powder 8%

[0064] Zirconium carbonate powder 5%

[0065] Andalusite powder 1%

[0066] Zinc silicate 3%

[0067] Alumina powder 5%

[0068] Pure calcium aluminate cement 6%

[0069] Terbium oxide 2%

[0070] C 5 H 10 N 6 O 2 0.2%

[0071] Heat-resistant steel fiber 0.5%

[0072] Sulfonated styrene-maleic anhydride copolymer 0.05%

[0073] Polyether polycarboxylic acid 0.1%

Embodiment 2

[0075] A special castable for coal injection pipe of 5000T cement kiln, the weight percentage of its components is:

[0076] Zinc Aluminum Spinel 15%

[0077] Synthetic moissanite 20%

[0078] Brown fused alumina 30%

[0079] Strontium Titanate Powder 10%

[0080] Zirconium carbonate powder 8%

[0081] Andalusite powder 2%

[0082] Zinc silicate 3%

[0083] Alumina powder 5%

[0084] Pure calcium aluminate cement 6%

[0085] Terbium oxide 1%

[0086] C 5 H 10 N 6 O 2 0.2%

[0087] Heat-resistant steel fiber 0.5%

[0088] Sulfonated styrene-maleic anhydride copolymer 0.05%

[0089] Polyether polycarboxylic acid 0.1%.

Embodiment 3

[0091] A special castable for coal injection pipe of 5000T cement kiln, the weight percentage of its components is:

[0092] Zinc Aluminum Spinel 20%

[0093] Synthetic moissanite 15%

[0094] Brown fused alumina 30%

[0095] Strontium Titanate Powder 10%

[0096] Zirconium carbonate powder 8%

[0097] Andalusite powder 2%

[0098] Zinc silicate 3%

[0099] Alumina powder 5%

[0100] Pure calcium aluminate cement 5%

[0101] Terbium oxide 2%

[0102] C 5 H 10 N 6 O 2 0.2%

[0103] Heat-resistant steel fiber 0.5%

[0104] Sulfonated styrene-maleic anhydride copolymer 0.05%

[0105] Polyether polycarboxylic acid 0.1%

[0106] Tc 2 O 7 0.05.

[0107] The components used in the above embodiments are products well-known to those skilled in the art, and are available on the market. The addition of synthetic moissanite, strontium titanate, brown corundum, and steel fiber is beneficial to the wear resistance of the castable And thermal shock; andalusite has micro-expansion; the introduction of zirconium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention aims at providing a castable special for a 5000T cement kiln coal-injection pipe. The castable can improve an existing uneven organization structure of an existing castable, and the defects of poor constructability and castable segregation, multiple pores and uneven pore distribution brought by the poor constructability are overcome. By the adoption of the measures, the phenomenon that a kilneye is not abraded, undergoes chip off-falling, is not resistant to corrosion and the like can be effectively improved, and the service life of the kilneye of a cement kiln can be remarkably prolonged.

Description

Technical field [0001] The invention relates to the field of high-temperature materials for building materials, in particular to a special castable for a 5000T cement kiln coal injection pipe. Background technique [0002] At present, my country's new dry process cement production line is developing rapidly, and cement production capacity has been seriously surplus. Therefore, cement production enterprises improve unit production efficiency and reduce production costs are the only way to maximize profits. Increasing the operation rate of cement production lines is an important condition for improving the production efficiency of cement kilns. However, the life of the cement kiln coal injection pipe has an important impact on the operation cycle of the entire production line. The coal injection pipes of cement kilns are used in harsh conditions. In addition to withstanding the high temperature in the kiln up to 1400℃, they also bear the erosion of cement kiln clinker, the therma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66
CPCC04B35/66
Inventor 张婷
Owner 张婷
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap