Preparing method for rosin pentaerythritol
A technology of rosin pentaerythritol ester and pentaerythritol, which is applied in the field of preparation of rosin pentaerythritol ester, can solve the problems of limited popularization and application of rosin pentaerythritol ester, low purity of rosin pentaerythritol ester, and achieve the effect of high softening point and high purity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] This rosin pentaerythritol ester comprises the following preparation steps:
[0020] A, raw material 100kg rosin is evacuated and decompressed and distilled to obtain refined rosin;
[0021] B. Under stirring, put the refined rosin obtained in step A into the reactor, and add 0.0001 kg of sodium phosphite, 5 kg of xylene, 4,4`-thiobis(6-tert-butyl-3 - methyl phenol) 0.001kg, pentaerythritol 15kg and cobalt acetate 0.02kg, then under the pressure of 0MPa, heated to 220°C, stirred at constant temperature, and reacted for 2 hours;
[0022] C. Put the material obtained in step B into a distillation tower, and carry out distillation at a pressure of 0 MPa and a temperature of 280° C. to obtain rosin pentaerythritol ester.
[0023] The softening point of the rosin pentaerythritol ester prepared in this example is as high as 120° C., and the purity is as high as 98%.
Embodiment 2
[0025] This rosin pentaerythritol ester comprises the following preparation steps:
[0026] A, raw material 100kg rosin is evacuated and decompressed and distilled to obtain refined rosin;
[0027] B. Under stirring, put the refined rosin obtained in step A into the reactor, and add 0.00016 kg of sodium phosphite, 6 kg of xylene, 4,4`-thiobis(6-tert-butyl-3 - methyl phenol) 0.0015kg, pentaerythritol 25kg and cobalt acetate 0.017kg, then under the pressure of 0.01MPa, heated to 200°C, stirred at constant temperature, and reacted for 4 hours;
[0028] C. Put the material obtained in step B into a distillation tower, and carry out distillation at a pressure of 0.01 MPa and a temperature of 270° C. to obtain rosin pentaerythritol ester.
[0029] The softening point of the rosin pentaerythritol ester prepared in this example is as high as 125° C., and the purity is as high as 98.1%.
Embodiment 3
[0031] This rosin pentaerythritol ester comprises the following preparation steps:
[0032] A, raw material 100kg rosin is evacuated and decompressed and distilled to obtain refined rosin;
[0033] B. In the stirring state, put the refined rosin obtained in step A into the reactor, and add 0.0002kg of sodium phosphite, 8kg of xylene, 4,4`-thiobis(6-tert-butyl-3 - methyl phenol) 0.002kg, pentaerythritol 20kg and cobalt acetate 0.01kg, then under the pressure of 0.005MPa, heated to 205°C, stirred at constant temperature, and reacted for 3 hours;
[0034] C. Put the material obtained in step B into a distillation tower, and carry out distillation at a pressure of 0.005 MPa and a temperature of 275° C. to obtain rosin pentaerythritol ester.
[0035] The softening point of the rosin pentaerythritol ester prepared in this example is as high as 120° C., and the purity is as high as 98.5%.
PUM
Property | Measurement | Unit |
---|---|---|
softening point | aaaaa | aaaaa |
softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap