A kind of preparation method and application of perovskite film

A perovskite and thin-film technology, applied in the field of solar cells, can solve the problems of scarcity of technology and achieve the effects of good film quality, controllable perovskite grain size, and low production cost

Active Publication Date: 2017-04-12
上海黎元新能源科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the technology for preparing perovskite light-absorbing layers is still relatively rare, especially the technology that considers the cost of preparation mechanization, production time, material utilization and the quality of the prepared perovskite light-absorbing layers still needs further development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and application of perovskite film
  • A kind of preparation method and application of perovskite film
  • A kind of preparation method and application of perovskite film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] This embodiment provides a method for preparing a perovskite light-absorbing layer for a perovskite solar cell, which specifically includes the following steps:

[0042] (1) Preheating the substrate, specifically:

[0043] The substrate is composed of a substrate and an adhesion layer attached to the substrate. The substrate is made of glass (with a roughness of 10nm). A conductive layer and a hole transport layer are attached to the glass in sequence. The conductive layer is SnO doped with fluorine. 2 Layer, the hole transport layer is a nickel oxide layer (thickness is 20nm);

[0044] Place the substrate on the heating plate to preheat, the preheating temperature is 220°C, and the preheating time is 30s;

[0045] (2) Form a tight sandwich structure with the substrate as the bottom layer and the dragged film as the top layer, with the perovskite precursor liquid sandwiched between the two, specifically:

[0046] a. Configure perovskite precursor liquid

[0047] Solu...

Embodiment 2

[0069] This embodiment provides a method for preparing a perovskite light-absorbing layer for a perovskite solar cell, which specifically includes the following steps:

[0070] (1) Preheating the substrate, specifically:

[0071] The substrate is composed of a substrate and an adhesion layer attached to the substrate. The substrate is made of glass (with a roughness of 30nm), and a conductive layer and a hole transport layer are attached to the glass in sequence. The conductive layer is SnO doped with fluorine. 2 Layer, the hole transport layer is a titanium oxide layer (thickness is 100nm);

[0072] Place the substrate on the heating plate to preheat, the preheating temperature is 180°C, and the preheating time is 20min;

[0073] (2) Form a tight sandwich structure with the substrate as the bottom layer and the dragged film as the top layer, with the perovskite precursor liquid sandwiched between the two, specifically:

[0074] a. Configure perovskite precursor liquid

[0...

Embodiment 3

[0084] This embodiment provides a method for preparing a perovskite light-absorbing layer for a perovskite solar cell, which specifically includes the following steps:

[0085] (1) Preheating the substrate, specifically:

[0086] The substrate is composed of a substrate and an adhesion layer attached to the substrate. The substrate is made of glass (with a roughness of 50nm), and a conductive layer and a hole transport layer are sequentially attached to the glass. The conductive layer is SnO doped with fluorine. 2 Layer, the hole transport layer is a titanium oxide layer (thickness is 200nm);

[0087] Place the substrate on the heating plate to preheat, the preheating temperature is 180°C, and the preheating time is 20min;

[0088] (2) Form a tight sandwich structure with the substrate as the bottom layer and the dragged film as the top layer, with the perovskite precursor liquid sandwiched between the two, specifically:

[0089] a. Configure perovskite precursor liquid

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method and application of a perovskite thin film. The preparation method of the perovskite thin film comprises the following steps: (1) forming a kind of tight sandwich structure with the substrate as the bottom layer and the dragged film as the top layer, and the perovskite precursor solution between the two; (2) under the heating condition Next, the dragged film is gradually peeled off, so that the perovskite precursor solution on the substrate is gradually exposed to the environmental medium; (3) after the solvent in the perovskite precursor solution on the substrate evaporates, a perovskite film is formed on the substrate. The perovskite thin film made by the preparation method of the perovskite thin film provided by the present invention has good film-forming performance, controllable perovskite grain size (100nm-3 μm), controllable film thickness (50nm-2 μm), etc. advantage.

Description

technical field [0001] The invention relates to the technical field of solar cells, in particular to a preparation method and application of a perovskite thin film. Background technique [0002] Organic-inorganic hybrid metal ABX 3 With the characteristics of narrow band gap, high molar extinction coefficient, and high carrier mobility, solar cells based on this material are called perovskite solar cells. As a rising star in the third generation of solar cells, perovskite solar cells have developed rapidly in the past five years, and the current photoelectric conversion efficiency has reached 21%. [0003] The perovskite light-absorbing layer is the core film layer of the perovskite solar cell, and its preparation process has a decisive impact on the perovskite light-absorbing layer, and even determines the performance of the perovskite solar cell. At present, there are many problems in the process of perovskite solar cells from laboratory research to large-scale practical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L51/48
CPCH10K71/00Y02E10/549
Inventor 韩礼元叶飞陈汉杨旭东
Owner 上海黎元新能源科技有限公司