A kind of preparation method and application of cow dung biochar

A technology of biochar and cow dung, which is applied in the direction of carbon preparation/purification, chemical instruments and methods, and other chemical processes, can solve the problems of adsorption performance and stability limitations, limited adsorption sites, etc., and achieve far-reaching social significance and Effects of economic value, improvement of adsorption performance, and simple preparation method

Active Publication Date: 2018-04-10
SOUTH CHINA INST OF ENVIRONMENTAL SCI MEP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, hydrothermal biochar itself has limited surface adsorption sites, so its adsorption performance and stability are greatly limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and application of cow dung biochar
  • A kind of preparation method and application of cow dung biochar
  • A kind of preparation method and application of cow dung biochar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1 A kind of preparation method of cow dung biochar

[0031] 1) Naturally air-dry the cow dung, pulverize it, and pass through a sieve above 40 mesh;

[0032] 2) Place the sieved powder in a vacuum tube furnace, seal it, and pyrolyze it under the condition of isolating the air; the specific process of pyrolysis is divided into: a heating section, a heat preservation section and a cooling section; 20℃min -1 The heating rate is raised to 200-500°C; the heat preservation section is for 2-5 hours at 200-500°C; the cooling section is natural cooling; nitrogen is used as a protective gas during the entire pyrolysis process, and the gas flow rate is 100mL min -1 .

[0033] 3) Mix the pyrolyzed product with granular potassium hydroxide, add water, and stir at 180rpm for 180min, filter, and take the filter residue;

[0034] Wherein, the mass ratio of pyrolyzed product to granular potassium hydroxide is 1:1.

[0035] 4) Wash the filter residue with water and dry at ...

Embodiment 2

[0036] Embodiment 2 A kind of preparation method of cow dung biochar

[0037] 1) Naturally air-dry the cow dung, pulverize it, and pass through a sieve above 40 mesh;

[0038] 2) Place the sieved powder in a vacuum tube furnace, seal it, and pyrolyze it under the condition of isolating the air; the specific process of pyrolysis is divided into: a heating section, a heat preservation section and a cooling section; min -1 The heating rate is raised to 500°C; the heat preservation section is at 500°C for 3 hours; the temperature drop section is natural cooling; nitrogen is used as a protective gas during the entire pyrolysis process, and the gas flow rate is 100mL min -1 .

[0039] 3) Mix the pyrolyzed product with sodium hydroxide, add water, and stir at 160rpm for 6h, filter, and take the filter residue;

[0040] Wherein, the mass ratio of pyrolyzed product to sodium hydroxide is 1:0.5.

[0041] 4) Wash the filter residue with water and dry at 80°C to obtain cow dung biocha...

Embodiment 3

[0042] Embodiment 3 A kind of preparation method of cow dung biochar

[0043] 1) Naturally air-dry the cow dung, pulverize it, and pass through a sieve above 40 mesh;

[0044] 2) Place the sieved powder in a vacuum tube furnace, seal it, and pyrolyze it under the condition of isolating the air; the specific process of pyrolysis is divided into: a heating section, a heat preservation section and a cooling section; min -1 The heating rate is raised to 400°C; the heat preservation section is at 400°C for 5 hours; the temperature drop section is natural cooling; nitrogen is used as a protective gas during the entire pyrolysis process, and the gas flow rate is 100mL min -1 .

[0045] 3) Mix the pyrolyzed product with granular potassium hydroxide, add water, and stir at 200rpm for 2h, filter, and take the filter residue;

[0046] Wherein, the mass ratio of pyrolyzed product to granular potassium hydroxide is 1:0.5.

[0047] 4) Wash the filter residue with water and dry at 100°C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method and application of cow dung biological carbon. The method comprises the following steps: naturally air-drying, crushing and sieving with a sieve of more than 40 meshes cow dung; performing pyrolysis under an air-free condition; mixing a product obtained by pyrolysis and a strong alkaline solution, adding water for rapid and uniform stirring, performing clarifying and filtering, and extracting filter residues; performing washing and drying to obtain activated cow dung biological carbon. According to the preparation method and the application, adsorption and removal effects of the cow dung biological carbon on aqueous solutions of heavy metals lead, cadmium, zinc, copper, nickel and the like are greatly improved, better fixing effects on lead, cadmium, zinc, copper, nickel and the like in soil are achieved, acid soil can be improved, organic matters of the soil are improved, and soil carbon fixation is facilitated. The preparation method is simple, and has far-reaching social significance and economic value, conditions are mild, industrial production is facilitated, additional environmental hazards can be avoided, the utilization efficiency of biomass resources is improved, and the problem of difficulty in degradation and reutilization of agricultural and forestry biomass residues is solved.

Description

technical field [0001] The invention relates to a preparation method and application of cow dung biochar. Background technique [0002] At present, the preparation of biochar mainly focuses on the preparation of biochar by using sludge, agricultural waste, wood chips and other raw materials, and few reports have been made on the preparation of biochar from cow dung. [0003] With the rapid development of my country's cattle breeding industry, it is urgent to expand new resource utilization methods and approaches of cow dung to solve the problem of environmental pollution caused by excess cow dung. Therefore, the use of low-cost and abundant high-quality biomass resources such as cow dung to prepare biochar for the remediation of heavy metal pollution in water has gradually attracted people's attention. There are also some literatures on the adsorption of heavy metals in water by cow dung biochar, but the prepared cow dung biochar is not good in adsorption performance and st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/30C01B32/05B09C1/00B09C1/08
CPCB01J20/20B01J2220/4887B09C1/00B09C1/08
Inventor 陈志良袁志辉刘敏超王欣戴玉蒋晓璐
Owner SOUTH CHINA INST OF ENVIRONMENTAL SCI MEP