A kind of anti-aging modified natural rubber composite material

A technology of natural rubber and composite materials, applied in the field of rubber materials, can solve the problems of rubber sticking, cracking, application limitation, etc., and achieve the effect of reducing compression set, increasing aging resistance, and improving vulcanization performance.

Active Publication Date: 2019-04-30
苏州技佳橡塑有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the chemical composition of natural rubber is mainly cis-1,4-polyisoprene, which contains a large number of unsaturated double bonds, which is easy to carry out autocatalytic reaction with oxygen in the air, causing molecular chain scission or excessive crosslinking, Viscosity and cracks occur in rubber, which greatly limits its application in practice

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of anti-aging modified natural rubber composite material proposed by the present invention, its raw material comprises by weight: 100 parts of natural rubber, 35 parts of butadiene rubber, 20 parts of styrene-butadiene rubber, 25 parts of nitrile rubber, epoxidized natural rubber 2 parts, 4 parts of nano-zinc oxide, 1 part of stearic acid, 1 part of sulfur, 0.2 parts of dicumyl peroxide, 0.2 parts of triallyl trimellitate, 0.1 parts of p-tert-butylphenolic resin, nano-carbonic acid 15 parts of calcium, 5 parts of precipitated white carbon black, 20 parts of purple carbon black, 3 parts of nano-microcrystalline cellulose, 15 parts of nano-silicon dioxide, 0.5 parts of anti-aging agent, 0.5 parts of potassium isopropyl xanthate, dibenzyl 0.2 parts of amine, 1 part of tetrahydrofurfurylamine, 0.5 parts of isopropyl trioleoyl titanate, 2 parts of vinyl tris (β-methoxyethoxy) silane, 1 part of diethylene glycol diester distearate , 3 parts of polyethylene adipate.

Embodiment 2

[0019] A kind of anti-aging modified natural rubber composite material proposed by the present invention, its raw material comprises by weight: 100 parts of natural rubber, 20 parts of butadiene rubber, 40 parts of styrene-butadiene rubber, 5 parts of nitrile rubber, epoxidized natural rubber 5 parts, 1 part of nano-zinc oxide, 3 parts of stearic acid, 0.1 part of sulfur, 1.5 parts of dicumyl peroxide, 0.01 part of triallyl trimellitic acid, 0.5 parts of p-tert-butylphenolic resin, nano-carbonic acid 3 parts of calcium, 15 parts of precipitated white carbon black, 5 parts of purple carbon black, 12 parts of nano-microcrystalline cellulose, 3 parts of nano-silicon dioxide, 2,2'-ethylenebis(4,6-di-tert-pentamyl 2.5 parts of potassium isopropyl xanthate, 0.1 part of potassium isopropyl xanthate, 0.5 parts of dibenzylamine, 0.2 parts of tetrahydrofurfurylamine, 2.5 parts of isopropyl trioleoyl titanate, 2.5 parts of vinyl tris(β-methoxyethyl 0.3 parts of oxy)silane, 2.5 parts of d...

Embodiment 3

[0021] A kind of aging-resistant modified natural rubber composite material proposed by the present invention, its raw material comprises by weight: 100 parts of natural rubber, 33 parts of butadiene rubber, 27 parts of styrene-butadiene rubber, 21 parts of nitrile rubber, epoxidized natural rubber 3 parts, 3.5 parts of nano-zinc oxide, 1.9 parts of stearic acid, 0.8 parts of sulfur, 0.6 parts of dicumyl peroxide, 0.15 parts of triallyl trimellitic acid, 0.4 parts of p-tert-butylphenolic resin, nano-carbonic acid 9 parts of calcium, 11 parts of precipitated white carbon black, 14 parts of purple carbon black, 12 parts of nano-microcrystalline cellulose, 10 parts of nano-silicon dioxide, 2.1 parts of thiourea anti-aging agent, 0.2 parts of potassium isopropyl xanthate , 0.42 parts of dibenzylamine, 0.46 parts of tetrahydrofurfurylamine, 2.2 parts of isopropyl trioleoyl titanate, 1.2 parts of vinyl tris (β-methoxyethoxy) silane, diethylene glycol distearate 2.2 parts of ester, 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-aging modified natural rubber composite material. The anti-aging modified natural rubber composite material is prepared from natural rubber, butadiene rubber, butadiene styrene rubber, butadiene-acrylonitrile rubber, epoxidized natural rubber, nano-zinc oxide, stearic acid, sulfur, dicumyl peroxide, triallyl trimellitate, p-tert-butyl-phenolic resin, nano calcium carbonate, precipitated silica, carbon black purple, nano-microcrystalline cellulose, nano-silicon dioxide, an anti-aging agent, potassium iso-propyl xanthate, dibenzylamine, tetrahydrofurfurylamine, isopropyl trioleoyl titanate, vinyltris(beta-methoxyethoxy)silane, diethylene glycol distearate and polyethyl dialcohol adipate. The anti-aging modified natural rubber composite material is high in strength, good in heat resistance and aging resistance and capable of meeting the usage requirements of multiple fields of cables, rubber pipes and the like.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to an aging-resistant modified natural rubber composite material. Background technique [0002] Natural rubber has high elasticity at room temperature, slightly plastic, very good mechanical strength, low hysteresis loss, low heat generation during multiple deformations, so its flex resistance is also very good, and its shock resistance and drop The noise effect is obvious. At present, it has been widely used in cables, pipes and other fields. However, the chemical composition of natural rubber is mainly cis-1,4-polyisoprene, which contains a large number of unsaturated double bonds, which is easy to carry out autocatalytic reaction with oxygen in the air, causing molecular chain scission or excessive crosslinking, Viscosity and cracks occur in rubber, which greatly limits its practical application. Contents of the invention [0003] Based on the technical problems in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/00C08L9/06C08L9/02C08L15/00C08L1/04C08L67/02C08K13/02C08K3/22C08K5/09C08K3/06C08K5/14C08K3/26C08K3/36
CPCC08K2201/003C08K2201/011C08L7/00C08L2201/08C08L2203/18C08L2203/202C08L2205/02C08L2205/035C08L9/00C08L9/06C08L9/02C08L15/00C08L1/04C08L67/02C08K13/02C08K2003/2296C08K5/09C08K3/06C08K5/14C08K2003/265C08K3/36
Inventor 刘洋王雅新陈雷刘晓燕姜雨虹寇蔷薇杨景海
Owner 苏州技佳橡塑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com