Inorganic transparent polymerized anti-leakage waterproof nano adhesive

A technology of anti-seepage, waterproof and nano-adhesive, which is applied in the field of materials, can solve the problems of environmental protection, toxicity, acid and alkali resistance, frost resistance, ultraviolet resistance, rust resistance, pollution resistance and self-cleaning, etc., to achieve shortening The construction period and the effect of improving construction efficiency

Inactive Publication Date: 2016-10-12
赵先芝
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing waterproof materials for large-scale infrastructure projects such as: copper waterstops and rubber waterstops cannot have the advantages of corrosion resistance and high temperature resistance at the same time, while polyurea materials are not ideal in UV resistance and aging resistance, and the materials themselves are toxic, odorous and irritating. Strong substance, not in line with the slogan of environmental friendliness, green material, green construction
None of the above materials have the function of environmental protection, strong penetration into the concrete building body of 30MM, and do not have strong and durable anti-acid and alkali, anti-freeze, anti-ultraviolet, anti-rust, anti-fouling and self-cleaning technical functions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An inorganic transparent polymeric anti-seepage and waterproof adhesive, the main raw materials in parts by weight are: 30 parts of nano-silicon dioxide, 5 parts of carbon nanotubes, 15 parts of LDW302A, 5 parts of polyacrylamide, 15 parts of methanol, and 0.5 parts of ammonium chloride part, 0.1 part of pentaerythritol; the preparation method of the nano-silicon dioxide: first cut the silicon dioxide film into 1cm×1cm fragments, then implant ions into the fragments, use argon as the working gas, and the vacuum degree of the sputtering chamber 2.0×10 -4 Pa, the discharge voltage is 65V, the beam voltage is 1500V, and the growth beam current is 8mA. After sputtering, silicon dioxide clusters are obtained, and then deionized water is added and ultrasonic treatment is performed. The ultrasonic power is 3000W, the temperature is 800°C, and the time for 15 minutes, after the ultrasonic wave is over, silicon dioxide nanoparticles are obtained, then a titanate coupling agent i...

Embodiment 2

[0021] An inorganic transparent polymeric anti-seepage and waterproof adhesive, the main raw materials in parts by weight are: 33 parts of nano-silica, 6 parts of carbon nanotubes, 18 parts of LDW302A, 5 parts of polyacrylamide, 20 parts of methanol, 0.5 parts of ammonium chloride part, 0.1 part of pentaerythritol; the preparation method of the nano-silicon dioxide: first cut the silicon dioxide film into 1cm×1cm fragments, then implant ions into the fragments, use argon as the working gas, and the vacuum degree of the sputtering chamber 2.0×10 -4 Pa, the discharge voltage is 65V, the beam voltage is 1500V, and the growth beam current is 8mA. After sputtering, silicon dioxide clusters are obtained, and then deionized water is added and ultrasonic treatment is performed. The ultrasonic power is 3000W, the temperature is 800°C, and the time for 15 minutes, after the ultrasonic wave is over, silicon dioxide nanoparticles are obtained, then a titanate coupling agent is added for s...

Embodiment 3

[0025] An inorganic transparent polymeric anti-seepage and waterproof adhesive, the main raw materials in parts by weight are: 35 parts of nano-silica, 8 parts of carbon nanotubes, 21 parts of LDW302A, 8 parts of polyacrylamide, 23 parts of methanol, and 0.8 parts of ammonium chloride part, 0.4 part of pentaerythritol; the preparation method of the nano-silicon dioxide: first cut the silicon dioxide film into 1cm×1cm fragments, then implant ions into the fragments, use argon as the working gas, and the vacuum degree of the sputtering chamber 2.0×10 -4 Pa, the discharge voltage is 65V, the beam voltage is 1500V, and the growth beam current is 8mA. After sputtering, silicon dioxide clusters are obtained, and then deionized water is added and ultrasonic treatment is performed. The ultrasonic power is 3000W, the temperature is 900°C, and the time It was 57min, after the ultrasonic was finished, silicon dioxide nanoparticles were obtained, then a titanate coupling agent was added t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an inorganic transparent polymeric anti-seepage and waterproof adhesive. The main raw materials of the inorganic transparent polymeric anti-seepage and waterproof adhesive are: 30-40 parts of nano silicon dioxide, 5-5 parts of carbon nanotubes 10 parts, 15-25 parts of LDW302A, 5-10 parts of polyacrylamide, 15-30 parts of methanol, 0.5-1.0 parts of ammonium chloride, and 0.1-0.5 parts of pentaerythritol; the product prepared by the present invention has fast curing requirements on the environmental conditions of construction. Low, it is convenient to improve the construction quality of waterproof and anti-corrosion coatings, and the material itself is non-toxic and harmless, which is conducive to improving construction efficiency and shortening the construction period.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to an inorganic transparent polymeric anti-seepage and waterproof adhesive. Background technique [0002] Existing waterproof materials for large-scale infrastructure projects such as: copper waterstops and rubber waterstops cannot have the advantages of corrosion resistance and high temperature resistance at the same time, while polyurea materials are not ideal in UV resistance and aging resistance, and the materials themselves are toxic, odorous and irritating. Strong substance, not in line with the slogan of environmental friendliness, green material, green construction. None of the above materials has the function of environmental protection, strong penetration into the concrete building body of 30MM, and does not have strong and durable anti-acid and alkali, anti-freeze, anti-ultraviolet, anti-rust, anti-fouling and self-cleaning technical functions. Therefore, there is an u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/08C09D5/16C09D7/12
CPCC09D1/00C09D5/08C09D5/1687
Inventor 赵先芝
Owner 赵先芝
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap