High-performance foamed-concrete cement material and preparing method thereof
A technology of foamed concrete and cement materials, applied in the field of chemical materials, can solve the problems of large variation coefficient of fly ash quality, poor concrete effect, poor concrete workability, etc., achieve excellent fire performance, meet clean production and environmental protection requirements, The effect of reducing the amount of cement
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1
[0025] A high-performance foamed concrete cement material, in parts by weight, it contains the following components: 30 parts of mineral admixture, 50 parts of cement, 3 parts of retarder, 9 parts of foaming agent, 2 parts of cell wall Reinforcing agent, 2 parts of foaming speed regulator, 7.5 parts of magnesium hydroxide, 7.5 parts of aluminum hydroxide and 10 parts of building mortar admixture;
[0026] Wherein, the mineral admixture is fly ash, tailings powder, mineral powder, stone powder, sludge powder, silica fume, phosphogypsum and calcium carbonate according to 2:1:1:2:2:1:1:1 The weight ratio of the mixed powder obtained by uniformly mixing, the cement is Portland cement, the retarder is boric acid, lithium carbonate, nitrite, chromate, urea according to 2:1:1:1: A mixed powder obtained by uniformly mixing at a weight ratio of 2, the foaming agent is a mixed powder obtained by uniformly mixing magnesium powder, aluminum powder and sodium bicarbonate acc...
Example Embodiment
[0028] Example 2
[0029] A high-performance foamed concrete cement material, in parts by weight, it contains the following components: 20 parts of mineral admixture, 35 parts of cement, 2 parts of retarder, 6 parts of foaming agent, 1 part of cell wall Reinforcing agent, 1 part foaming speed regulator, 5 parts magnesium hydroxide, 5 parts aluminum hydroxide and 5 parts building mortar admixture;
[0030] Wherein, the mineral admixture is fly ash, tailings powder, mineral powder, stone powder, sludge powder, silica fume, phosphogypsum, calcium carbonate according to 3:1:2:1:2:1:1:2 The mixed powder obtained by uniformly mixing the weight ratio of the cement, the cement is Portland cement and the slag cement uniformly mixed according to the weight ratio of 3:1, and the retarder is boric acid, lithium carbonate, nitrite, Chromate and urea are mixed uniformly according to the weight ratio of 3:1:1:1:2, and the foaming agent is magnesium powder, aluminum powder and sodium bicarbonate ...
Example Embodiment
[0032] Example 3
[0033] A high-performance foamed concrete cement material, in parts by weight, it contains the following components: 40 parts of mineral admixture, 65 parts of cement, 4 parts of retarder, 12 parts of foaming agent, 3 parts of cell wall Reinforcing agent, 3 parts foaming speed regulator, 10 parts magnesium hydroxide, 10 parts aluminum hydroxide and 15 parts building mortar admixture;
[0034] Wherein, the mineral admixture is fly ash, tailings powder, mineral powder, stone powder, sludge powder, silica fume, phosphogypsum, calcium carbonate according to 1:1:1:1:1:1:1:1 The mixed powder obtained by uniformly mixing the weight ratio of the cement, the cement is Portland cement and the slag cement uniformly mixed according to the weight ratio of 2:1, and the retarder is boric acid, lithium carbonate, nitrite, Chromate and urea are mixed uniformly according to the weight ratio of 1:1:1:1:1, and the foaming agent is magnesium powder, aluminum powder and sodium bicarb...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap