PVC (polyvinyl chloride) home decorative sheet and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A decorative board and PVC resin powder technology, applied in the field of decorative boards, can solve problems such as short service life and application restrictions
Inactive Publication Date: 2017-02-08
江苏旺科新材料有限公司
View PDF4 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] With people's recognition of PVC products, as well as the enhancement of environmental protection awareness and tree protection awareness, the market demand for PVC home decoration boards is also increasing, but the existing PVC home decoration boards are generally brittle and have a short service life. Disadvantages make it limited in application
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0073] Embodiment 1, a kind of PVC home decorative board, it is made of the raw material of following weight ratio:
[0074] PVC resin powder 20;
[0075] Active Light Calcium Carbonate 10;
[0076] PVC recycled material 90;
[0077] Composite stabilizer 1.5;
[0078] Foam regulator 6;
[0079] Composite blowing agent 1;
[0080] Plasticizer 0.2;
[0081] Internal lubricant 0.5;
[0082] External lubricant 0.1;
[0083] Brightener 0.025;
[0084] The PVC recycled materials include PVC decorative template recycled materials, white PVC plastic-steel window recycled materials and white PVC pipe recycled materials;
[0085] The composite foaming agent is formed by mixing a white foaming agent and a yellow foaming agent.
Embodiment 2
[0086] Embodiment 2, a kind of PVC home decorative board, it is made of the raw material of following weight ratio:
[0087] PVC resin powder 30;
[0088] Active Light Calcium Carbonate 30;
[0089] PVC recycled material 150;
[0090] Composite Stabilizer 2.0;
[0091] Foam regulator 9;
[0092] Composite blowing agent 1.8;
[0093] Plasticizer 0.5;
[0094] Internal lubricant 0.7;
[0095] External lubricant 0.3;
[0096] Brightener 0.035;
[0097] The PVC recycled materials include PVC decorative template recycled materials, white PVC plastic-steel window recycled materials and white PVC pipe recycled materials;
[0098] The composite foaming agent is formed by mixing a white foaming agent and a yellow foaming agent.
Embodiment 3
[0099] Embodiment 3, a kind of PVC home decorative board, it is made of the raw material of following weight ratio:
[0100] PVC resin powder 23;
[0101] Active light calcium carbonate 12.5;
[0102] PVC recycled material 100;
[0103] Composite stabilizer 1.6;
[0104] Foam regulator 7;
[0105] Composite blowing agent 1.2;
[0106] Plasticizer 0.3;
[0107] Internal lubricant 0.5;
[0108] External lubricant 0.1;
[0109] Brightener 0.025;
[0110] The PVC recycled materials include PVC decorative template recycled materials, white PVC plastic-steel window recycled materials and white PVC pipe recycled materials;
[0111] The composite foaming agent is formed by mixing a white foaming agent and a yellow foaming agent.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
particle size
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a PVC (polyvinyl chloride) home decorative sheet which is prepared from the following raw materials according to a weight proportion: 20 to 30 of PVC resin powder; 10 to 30 of colloidal calcium carbonate; 90 to 150 of PVC recycled materials; 1.5 to 2.0 of composite stabilizer; 6 to 9 of foaming control agent; 1 to 1.8 of composite foaming agent; 0.2 to 0.5 of plasticizer, 0.5 to 0.7 of internal lubricant, 0.1 to 0.3 of external lubricant, and 0.025 to 0.035 of whitening agent. The PVC recycled materials comprise a PVC decorative template recycled material, a white PVC plastic steel window recycled material and a white PVC pipe recycled material; the composite foaming agent is formed by mixing a white foaming agent and a yellow foaming agent. The invention further discloses a preparation method of the PVC home decorative sheet. According to the PVC home decorative sheet and the preparation method thereof, which are disclosed by the invention, the PVC recycled materials are used as one of the main raw materials, wastes are changed into treasures, production cost is reduced, energy is saved, hardness and weather resistance of the product are improved, recycling times are increased, the recycling times can reach 35 times or above, moreover, the preparation method is easy to operate, and the prepared product is smooth and attractive in surface. The PVC home decorative sheet disclosed by the invention is energy-saving, environmental-friendly, low in production cost and long in service life.
Description
technical field [0001] The invention relates to a decorative board, in particular to a PVC family decorative board and a preparation method thereof. Background technique [0002] With people's recognition of PVC products, as well as the enhancement of environmental protection awareness and tree protection awareness, the market demand for PVC home decoration boards is also increasing, but the existing PVC home decoration boards are generally brittle and have a short service life. The disadvantages limit its application. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a PVC home decorative board with good hardness, strong rigidity and long service life in view of the deficiencies of the prior art. [0004] The present invention also provides a preparation method of the aforementioned PVC home decoration board. [0005] The technical problem to be solved in the present invention is achieved through the following t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more