PVC (polyvinyl chloride) advertisement template and preparation method thereof

A technology of PVC resin powder and template, applied in the field of advertising template, can solve the problems of application limitation, poor impact resistance, etc.

Inactive Publication Date: 2017-01-25
江苏旺科新材料有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With people's recognition of PVC products, as well as the enhancement of environmental awareness and tree protection awareness, the market demand for PVC advertising templates is also increasing. However, the existing PVC advertising templates generally have disadvantages such as poor impact resistance and brittleness. , making it limited in application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] Embodiment 1, a PVC advertising template, the template is made of the following raw materials in weight ratio:

[0077] PVC resin powder 60;

[0078] PVC recycled material 20;

[0079] Active Light Calcium Carbonate 30;

[0080] Composite stabilizer 2.5;

[0081] Foam regulator 5;

[0082] Composite blowing agent 1.2;

[0083] Plasticizer 0.2;

[0084] Lubricant 0.7;

[0085] Titanium dioxide 0.3;

[0086] Brightener 0.01;

[0087] The composite foaming agent is formed by mixing an inorganic foaming agent and an organic foaming agent;

[0088] The lubricant is formed by mixing PE wax, stearic acid and internal lubricant ZB-60.

Embodiment 2

[0089] Embodiment 2, a PVC advertising template, the template is made of the following raw materials in weight ratio:

[0090] PVC resin powder 90;

[0091] PVC recycled material 50;

[0092] Active Light Calcium Carbonate 60;

[0093] Composite stabilizer 4;

[0094] Foam regulator 12;

[0095] Composite blowing agent 2.25;

[0096] Plasticizer 0.6;

[0097] lubricant 1.5;

[0098] Titanium dioxide 1;

[0099] Brightener 0.04;

[0100] The composite foaming agent is formed by mixing an inorganic foaming agent and an organic foaming agent;

[0101] The lubricant is formed by mixing PE wax, stearic acid and internal lubricant ZB-60.

Embodiment 3

[0102] Embodiment 3, a PVC advertising template, which is made of the following raw materials in weight ratio:

[0103] PVC resin powder 70;

[0104] PVC recycled material 30;

[0105] Active Light Calcium Carbonate 40;

[0106] Composite stabilizer 3;

[0107] Foam regulator 6;

[0108] Composite blowing agent 1.5;

[0109] Plasticizer 0.3;

[0110] Lubricant 0.9;

[0111] Titanium dioxide 0.5;

[0112] Brightener 0.01;

[0113] The composite foaming agent is formed by mixing an inorganic foaming agent and an organic foaming agent;

[0114] The lubricant is prepared by mixing PE wax, stearic acid and internal lubricant ZB-60 in a mass ratio of 8:6:6.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a PVC (polyvinyl chloride) advertisement template. The PVC advertisement template is prepared from, by weight, 60-90 parts of PVC resin powder, 20-50 parts of PVC reclaimed materials, 30-60 parts of active light calcium carbonate, 2.5-4 parts of compound stabilizer, 5-12 parts of foaming control agent, 1.2-2.25 parts of compound foaming agent, 0.2-0.6 part of plasticizer, 0.7-1.5 parts of lubricant, 0.3-1 part of titanium dioxide and 0.01-0.04 part of brightening agent, wherein the compound foaming agent is formed by mixing an inorganic foaming agent with an organic foaming agent, and the lubricant is formed by mixing PE wax, stearic acid and an internal lubricant ZB-60. The invention further provides a preparation method of the PVC advertisement template. The PVC advertisement template and the preparation method thereof have the advantages that since the PVC reclaimed materials are used as one of main raw materials, turning waste into wealth, production cost reduction and energy saving are achieved, hardness and weather fastness of the PVC advertisement template are improved, the number of recycling times can be increased and reach more than 35, and the PVC advertisement template is smooth and attractive in surface; the preparation method is easy to operate.

Description

technical field [0001] The invention relates to an advertisement template, in particular to a PVC advertisement template and a preparation method thereof. Background technique [0002] With people's recognition of PVC products, as well as the enhancement of environmental awareness and tree protection awareness, the market demand for PVC advertising templates is also increasing. However, the existing PVC advertising templates generally have disadvantages such as poor impact resistance and brittleness. , making it limited in application. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a PVC advertising template with good hardness, strong rigidity and long service life in view of the deficiencies of the prior art. [0004] The present invention also provides a preparation method of the aforementioned PVC advertisement template. [0005] The technical problem to be solved in the present invention is achieved throug...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K13/06C08K3/26C08K3/22C08K5/09C08J9/08C08J9/10B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704C08J9/08C08J9/103C08J2203/02C08J2203/04C08J2203/184C08J2327/06C08J2427/06C08L27/06C08L2203/14C08L2205/025C08L2205/035C08L2207/20C08K13/06C08K2003/265C08K2003/2241C08K5/09Y02P70/10
Inventor 王泽王兴成王加标
Owner 江苏旺科新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com