Quick-drying environment-friendly special alcohol acid iron red antirust coating for steel structures

A quick-drying, iron alkyd technology, applied in the direction of anti-corrosion coatings, polyester coatings, coatings, etc., can solve the problems of slow drying time, poor hardness, poor anti-rust effect, etc., and achieve good connection and good adhesion Focus on the effect

Inactive Publication Date: 2017-03-08
JIANGSU CHAMPION TECHNOLOGY GROUP CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at technical problems such as slow drying time, poor hardness and poor anti-rust effect of existing anti-corrosion coatings proposed in the background tec

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0035] Example 1

[0036] A fast-drying type environmentally-friendly iron alkyd red anti-rust paint for steel structure, which is composed of the following components in weight percentage:

[0037] Vegetable oil modified anti-rust paint special resin 35%

[0038] Environmental protection 200# solvent 20%

[0039] Dispersant 0.3%

[0040] Iron oxide red 20%

[0041] Zinc phosphate 23%

[0042] Organic bentonite 0.7%

[0043] Methyl ethyl ketoxime 0.2%

[0044] High efficiency drier 0.8%.

[0045] Preparation Process:

[0046] First, mix the vegetable oil modified anti-rust paint special resin, environmental protection 200# solvent, dispersant, iron oxide red, zinc phosphate, and organic bentonite according to the proportion, and then grind to the fineness ≤ 30μm, then add the methyl ethyl ketoxime and efficient drying And mix well.

Example Embodiment

[0047] Example 2

[0048] A fast-drying type environmentally-friendly iron alkyd red anti-rust paint for steel structure, which is composed of the following components by weight percentage:

[0049] Vegetable oil modified anti-rust paint special resin 40%

[0050] Environmental protection 200# solvent 15%

[0051] Dispersant 0.3%

[0052] Iron oxide red 23%

[0053] Zinc phosphate 20%

[0054] Organic bentonite 0.8%

[0055] Methyl ethyl ketoxime 0.2%

[0056] High efficient drier 0.7%.

[0057] The preparation process is the same as in Example 1.

Example Embodiment

[0058] Example 3

[0059] A fast-drying type environmentally-friendly iron alkyd red anti-rust paint for steel structure, which is composed of the following components in weight percentage:

[0060] Vegetable oil modified antirust paint special resin 30%

[0061] Environmental protection 200# solvent 18%

[0062] Dispersant 0.5%

[0063] Iron oxide red 30%

[0064] Zinc phosphate 20%

[0065] Organic bentonite 0.5%

[0066] Methyl ethyl ketoxime 0.3%

[0067] High efficient drier 0.7%.

[0068] The preparation process is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses quick-drying environment-friendly special alcohol acid iron red antirust coating for steel structures. The quick-drying environment-friendly special alcohol acid iron red antirust coating comprises, by weight, 15%-50% of special plant-oil-modified resin for antirust paint, 10%-25% of environment-friendly No.200 solvents, 0.1%-0.5% of dispersing agents, 10%-30% of iron oxide red, 5%-30% of zinc phosphate, 0.5%-1% of organic bentonite, 0.1%-0.3% of methyl ethyl ketoxime and 0.5%-1% of efficient drying catalysts. The quick-drying environment-friendly special alcohol acid iron red antirust coating has the advantages that the quick-drying environment-friendly special alcohol acid iron red antirust coating is applicable to metal surfaces of the large steel structures and is generally used as antirust paint; the quick-drying environment-friendly special alcohol acid iron red antirust coating is good in adhesion, moisture resistance and priming and finish paint junction property and is particularly adaptable to atmospheric corrosion resistance.

Description

technical field [0001] The invention belongs to the technical field of chemical industry, and in particular relates to a quick-drying environmental-friendly alkyd iron red antirust paint specially used for steel structures. Background technique [0002] The anticorrosion paint of the prior art is prepared by grinding long-oil pentaerythritol, alkyd resin, iron oxide pigments, additives, etc., adding appropriate amount of aluminum powder slurry, cobalt, manganese, lead and other driers and organic solvents. There are technical problems such as slow drying time (generally it takes about 10 days to dry completely), poor hardness (grade F), and poor anti-rust performance. Contents of the invention [0003] Aiming at technical problems such as slow drying time, poor hardness and poor anti-rust effect of the existing anti-corrosion coatings proposed in the background technology, the purpose of the present invention is to provide a fast-drying environment-friendly alkyd iron red ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/08C09D5/08C09D7/12
Inventor 谢海
Owner JIANGSU CHAMPION TECHNOLOGY GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap