Plastic-wood material for producing door jambs and preparation method of plastic-wood material

A kind of technology of plastic wood material and door cover

Inactive Publication Date: 2017-03-15
FOSHAN JUYE TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of this, the present invention provides a wood-plastic material for making door covers and a preparation method thereof, which can effectively improve the problem of poor scratch resistance of the wood-plastic material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plastic-wood material for producing door jambs and preparation method of plastic-wood material
  • Plastic-wood material for producing door jambs and preparation method of plastic-wood material
  • Plastic-wood material for producing door jambs and preparation method of plastic-wood material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] In parts by weight, the composition of the wood-plastic material used to make the door cover and the preparation method thereof of the present embodiment is as follows:

[0025]

[0026] The model of the high foaming aid is DLP-100, the model of the micro foaming aid is K128P, and the particle size of the calcium powder is 200-400 mesh.

Embodiment 2

[0028] In parts by weight, the composition of the wood-plastic material used to make the door cover and the preparation method thereof of the present embodiment is as follows:

[0029]

[0030] The model of the high foaming aid is DLP-100, the model of the micro foaming aid is K128P, and the particle size of the calcium powder is 250-450 mesh.

Embodiment 3

[0032] In parts by weight, the composition of the wood-plastic material used to make the door cover and the preparation method thereof of the present embodiment is as follows:

[0033]

[0034]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

An embodiment of the invention discloses a plastic-wood material for producing door jambs and a preparation method of the plastic-wood material; the plastic-wood material is prepared from, by weight, 40-60 parts of polyvinyl chloride, 40-60 parts of calcium powder, 10-15 parts of wood powder, 1-3 parts of a stabilizer, 1-3 parts of chlorinated polyethylene, 0.5-1.5 parts of AC foaming agent, 0.1-0.5 part of NC foaming agent, 0.2-0.8 part of stearic acid, 1.5-5 parts of a foaming aid, and 0.2-0.6 part of polyethylene. The plastic-wood material for producing door jambs and the preparation method of the plastic-wood material have the advantages that the scratch resistance of a door jamb produced with the plastic-wood material is excellent, and the door jamb is free of environmental pollution, has good quality and has promising market value.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a plastic-wood material used for making a door cover and a preparation method thereof. Background technique [0002] With the development of society, composite materials are widely used in various industries. Among them, plastic wood material is a kind of composite material. Because WPC has both the water resistance and anti-corrosion characteristics of plastic and the texture of wood, it has become an outdoor building material with excellent performance and durability; it can also replace wooden components used in ports, docks, etc., and can also be used to replace wood to make various products. There are many kinds of packaging, pallets, warehouse pads, etc., and they are extremely versatile. Combining the advantages of plant fibers and plastic polymer materials, plastic wood panels can replace wood in large quantities, and can effectively alleviate the contradictions of my...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08L23/28C08L23/06C08L23/08C08K13/02C08K3/26C08K5/09C08J9/10
CPCC08L27/06C08J9/103C08J2203/04C08J2327/06C08J2497/02C08L2203/14C08L2205/035C08L2207/066
Inventor 戴炬枫
Owner FOSHAN JUYE TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com