Production process for laminating and coating adhesive film

A production process and film technology, which is applied in the production process field of lamination coating adhesive film, can solve problems such as poor control of personnel, uneven glue coating, and uncontrollable film formation, so as to improve bonding efficiency and ensure effect of effect

Inactive Publication Date: 2017-05-10
TIANJIN SUNRAY PLASTIC PROD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing lamination coating generally uses hot-melt glue or glue, which is labor-intensive and time-consuming to produce, and the glue coating is uncontrollable
Therefore, it produces a solution that can solve the problems of uneven glue coating, poor control of personnel and cumbersome operation, control the fluidity of raw materials and uncontrollable film formation, and replace glue to solve the lamination of wool, sponge and nylon bonding technology It is especially necessary to apply adhesive film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] (1) The step of preparing the masterbatch, the masterbatch base material adopts EMAA with a melt index of 1.5g / 10min at 190°C, adopts polymer wax as a dispersant, and extrudes with a twin-screw extruder;

[0012] (2) The step of mixing the EVA resin and the coupling agent uniformly, the melt index of the EVA resin is 6g / 10min at 190°C;

[0013] (3) The step of using three-layer co-extrusion cast film forming process to produce laminated coating adhesive film, with EMAA resin on both sides and EVA resin in the middle. The extrusion temperature of EMAA screw is 95 ° C, and the extrusion temperature of EVA screw is controlled at 65°C;

[0014] (4) In the step of embossing, the water temperature of the rubber rollers of the embossing forming equipment is controlled at 9°C, the rubber rollers are made of integrated silicone material, the hardness is controlled at 65A, and the grain size of the rubber rollers is 15 meshes; the water temperature of the steel rollers is Contro...

Embodiment 2

[0017] (1) The step of preparing the masterbatch, the masterbatch base material adopts EMAA with a melt index of 3.5g / 10min at 190°C, adopts polymer wax as a dispersant, and extrudes with a twin-screw extruder;

[0018] (2) The step of mixing the EVA resin and the coupling agent evenly, the melt index of the EVA resin is 10g / 10min at 190°C;

[0019] (3) The step of using three-layer co-extrusion casting film forming process to produce laminated coating adhesive film, with EMAA resin on both sides and EVA resin in the middle. The extrusion temperature of EMAA screw is 100 ℃, and the extrusion temperature of EVA screw is controlled at 75°C;

[0020] (4) In the step of embossing forming, the water temperature of the rubber rollers of the embossing forming equipment is controlled at 10°C, the rubber rollers are made of integrated silicone material, the softness and hardness are controlled at 75A, and the grain size of the rubber rollers is 16 mesh; the water temperature of the ste...

Embodiment 3

[0023] (1) The step of preparing the masterbatch, the masterbatch base material adopts EMAA with a melt index of 4.5g / 10min at 190°C, adopts polymer wax as a dispersant, and extrudes with a twin-screw extruder;

[0024] (2) The step of mixing the EVA resin and the coupling agent uniformly, the melt index of the EVA resin is 14g / 10min at 190°C;

[0025] (3) The step of using three-layer co-extrusion casting film forming process to produce laminated coating adhesive film, with EMAA resin on both sides and EVA resin in the middle. The extrusion temperature of EMAA screw is 120 ℃, and the extrusion temperature of EVA screw is controlled at 90°C;

[0026] (4) In the step of embossing forming, the water temperature of the rubber rollers of the embossing forming equipment is controlled at 11°C, the rubber rollers are made of integrated silicone material, the softness and hardness are controlled at 80A, and the grain size of the rubber rollers is 17 meshes; the water temperature of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production process for a laminating and coating adhesive film. The production process comprises the following steps: firstly, preparing master match; adopting EMAA (Ethylene Methacrylic Acid) of which a melt index at the temperature of 190DEG C is 0.5 to 5g / 10min as a master batch base material, adopting polymeric paraffin as a dispersing agent, and extruding by adopting a twin-screw extruder; secondly, uniformly mixing EVA (Ethylene-Vinyl Acetate) resin with a coupling agent, wherein a melt index of the EVA resin at the temperature of 190DEG C is 5 to 15g / 10min; thirdly, generating the laminating and coating adhesive film by adopting a three-layer co-extrusion casting film forming technique, wherein two sides of the laminating and coating adhesive film are EMAA resin, the middle of the laminating and coating adhesive film is the EVA resin, the extrusion temperature of an EMAA screw is 90 to 130DEG C, and the extrusion temperature of an EVA screw is controlled at 60 to 90DEG C; fourthly, carrying out embossing forming; controlling the water temperature of a rubber roller of embossing forming equipment to be 8 to 12DEG C, wherein the rubber roller is made of an integrated silica gel material, the hardness is controlled at 60 to 80A, the grained roughness of the rubber roller is 14 to 18 meshes, the water temperature of a steel roller is controlled at 40 to 50DEG C, and the depth of patterns is 0.06 to 0.15mm.

Description

technical field [0001] The invention relates to a production process of a lamination coated adhesive film. Background technique [0002] Car polishing discs, wool discs, and sponge discs were originally bonded with nylon and wool with hot melt glue and were uncontrollable. Existing lamination coating generally uses hot-melt glue or glue, which is labor-intensive and time-consuming to produce, and the glue coating is uncontrollable. Therefore, it produces a solution that can solve the problems of uneven glue coating, poor control of personnel and cumbersome operation, control the fluidity of raw materials and uncontrollable film formation, and replace glue to solve the lamination of wool, sponge and nylon bonding technology It is especially necessary to apply adhesive film. Contents of the invention [0003] In order to solve the technical problems in the known technology, the present invention provides a production process of lamination coating adhesive film that replace...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/08B32B27/30
CPCB32B27/08B32B27/30B32B27/306
Inventor 崔九峰
Owner TIANJIN SUNRAY PLASTIC PROD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com