Polyurethane internal wall building mildew-proof paint

A polyurethane and anti-mildew technology, applied in polyurea/polyurethane coatings, fireproof coatings, antifouling/underwater coatings, etc., can solve the problems of poor gloss, insufficient water resistance, and poor self-thickening properties of latex films, and achieve long-lasting color , simple maintenance, soft color effect

Inactive Publication Date: 2017-05-24
广西宾阳县荣良农业科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Polyurethane has good tensile strength and impact strength, excellent flexibility and good wear resistance, but the anti-mildew effect of a single polyurethane coating is poor, the solid content is low, the self-thickening property is poor, and the gloss of the latex film is poor , insufficient water resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane internal wall building mildew-proof paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] In the mixer, add 5 parts of water, 10 parts of titanium dioxide, 9 parts of additives (including 1 part of chain extender, 2 parts of leveling agent, 3 parts of dispersant, 1 part of thickener, 0.5 parts of defoamer, 1 part of dustproof agent), 12 parts of filler (ultrafine talc powder: mica powder = 1:1), stir evenly, grind the resulting solution through a sander to a particle size of less than 40 microns, and then put the solution back into the mixer, Dissolve the mixed solvent with the antifungal agent and the leveling agent in the mixed solvent to obtain the antifungal solvent for later use; put the silane adhesion promoter, water-curable polyurethane and water-based acrylic resin into the mixer, and step (2) and ( 3) Mix the solution and anti-mildew solvent in , stir evenly, and you get it.

Embodiment 2

[0055] Add 8 parts of water, 6 parts of titanium dioxide and 13 parts of additives (including 3 parts of chain extender, 2 parts of leveling agent, 1 part of dispersant, 3 parts of thickener, 1.5 parts of defoamer, 2 parts of dust agent), 16 parts of filler (ultrafine talc powder: mica powder = 1:1), stir well, and grind the resulting solution through a sander to a particle size of less than 40 microns, and then put the solution back into the mixer. Dissolve the mixed solvent with the antifungal agent and the leveling agent in the mixed solvent to obtain the antifungal solvent for later use; put the silane adhesion promoter, water-curable polyurethane and water-based acrylic resin into the mixer, and step (2) and (3) ) solution, anti-mold solvent, mixed, stirred evenly, that is.

Embodiment 3

[0057] Add 6 parts of water, 7 parts of titanium dioxide, 8 parts of additives (including 1 part of chain extender, 1 part of leveling agent, 2 parts of dispersant, 1 part of thickener, 1 part of defoamer, 1 part of dustproof agent), 14 parts of filler (ultrafine talc powder: mica powder = 1:1), stir evenly, grind the resulting solution through a sander to a particle size of less than 40 microns, and then put the solution back into the mixer, Dissolve the mixed solvent with the antifungal agent and the leveling agent in the mixed solvent to obtain the antifungal solvent for later use; put the silane adhesion promoter, water-curable polyurethane and water-based acrylic resin into the mixer, and step (2) and ( 3) Mix the solution and anti-mildew solvent in , stir evenly, and you get it.

[0058] According to GB / T1723-93, GB / T 1724-89, GB / T 1731-93, GB / T 1732-93, GB / T1733-93, GB / T 1734-93 standards, the results are listed in the table below.

[0059]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses polyurethane internal wall building mildew-proof paint. The polyurethane internal wall building mildew-proof paint is mainly prepared from water-cured polyurethane, water-based acrylic resin and a mildew-proof agent; disadvantages of single polyurethane or single polyacrylic resin, such as poor stability, white thickening property and gloss retention of a film, high solid content and a narrow application range, are overcome; the main components have a complementary action on properties. The composite paint combines advantages of the polyurethane and the acrylic resin and has the characteristics of mildew prevention, wearing resistance, corrosion resistance and brightness, softness and elasticity, good water resistance and mechanical properties, excellent weather resistance and the like, and also has high glossiness, high elasticity and excellent weather resistance. Compared with other traditional polyurethane paint, the polyurethane internal wall building mildew-proof paint has the advantages of convenience for construction, no toxin and no pollution, and is more environment-friendly and the like.

Description

technical field [0001] The invention relates to a building coating, in particular to a polyurethane building anti-mildew coating. Background technique [0002] Due to the increasingly developed world industry and the destruction of nature by humans, energy conservation and consumption reduction has attracted the attention and attention of countries all over the world. my country's building energy consumption accounts for more than 30% of human energy consumption. Improve the thermal insulation performance of buildings and improve The use function of buildings, energy saving and consumption reduction are another important considerations in the design of building material selection. In the field of architectural coatings, the development goals at home and abroad are also developing in the direction of high efficiency, energy and resource saving, harmlessness and pollution-free. The architectural heat-reflecting and heat-insulating coatings developed in recent years are not onl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/08C09D133/12C09D131/04C09D5/16C09D7/00C09D7/12
CPCC09D175/08C08L2201/08C08L2205/035C09D5/1687C09D5/18C09D7/20C08L33/12C08L31/04C08K13/02C08K5/54C08K5/17C08K3/346C08K2003/2241
Inventor 陈明贤谢彤
Owner 广西宾阳县荣良农业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap