A kind of method that uses phosphoric acid to make crystal seed to produce superfine aluminum hydroxide

A technology of ultra-fine aluminum hydroxide and aluminum hydroxide, which is applied in the preparation of alkali metal aluminate/aluminum oxide/aluminum hydroxide, etc., can solve the problems of high production cost of ultra-fine aluminum hydroxide and achieve supersaturation Low density, low decomposition rate and good particle size

Active Publication Date: 2018-06-22
SHANDONG LUBEI ENTERPRISE GROUP +1
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to ensure the high purity of ultra-fine aluminum hydroxide, the current production mainly uses expensive sintering sodium aluminate semen, so that the production cost of ultra-fine aluminum hydroxide remains high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method that uses phosphoric acid to make crystal seed to produce superfine aluminum hydroxide
  • A kind of method that uses phosphoric acid to make crystal seed to produce superfine aluminum hydroxide

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0024] Below by embodiment the present invention is further illustrated.

[0025] Example 1

[0026] Add 180g of Bayer-process aluminum hydroxide to 400ml caustic soda solution with a caustic concentration of 220g / L, and re-dissolve at 105°C, the α of the sodium aluminate solution k is 1.31. Under the condition of 40-45°C constant temperature water bath, add 2mol / L phosphoric acid and redissolved sodium aluminate solution into the seed tank in a homogeneous flow mode, the reaction time is 30min, and the pH of the reaction solution is 8.5-9.5 at the end of the control. 40 Aged at -45°C for 24 hours, separated, washed, and filtered to obtain highly active seed crystals (D50=1.00 μm). With the seed crystal coefficient as 10%, the above-mentioned seeds are added to the sodium aluminate solution after dilution (caustic alkali concentration is 120g / L, α k =1.34), in a 60°C hot water bath, the stirring speed is 360r / min, and the reaction time is controlled at 20h. After the react...

Embodiment 2

[0028] Add 200g of Bayer-process aluminum hydroxide to 500ml caustic soda solution with a caustic concentration of 220g / L, and re-dissolve at 105°C, the α of the sodium aluminate solution k is 1.38. Under the condition of 40-45°C constant temperature water bath, add 2mol / L phosphoric acid and redissolved sodium aluminate solution into the seed tank in a homogeneous flow mode, the reaction time is 45min, and the pH of the reaction solution at the end of the control is 8.5-9.40 Aged at -45°C for 24 hours, separated, washed, and filtered to obtain highly active seed crystals (D50=0.82 μm). With the seed crystal coefficient as 20%, the above-mentioned seed crystals are added to the sodium aluminate solution after dilution (caustic alkali concentration is 130g / L, α k =1.41), in a 60°C hot water bath, the stirring speed is 360r / min, and the reaction time is controlled at 20h. After the reaction is over, the liquid and solid are separated, the filter cake is washed with hot water u...

Embodiment 3

[0030] Add 200g of Bayer-process aluminum hydroxide to 500ml caustic soda solution with a caustic concentration of 220g / L, and re-dissolve at 105°C, the α of the sodium aluminate solution k is 1.44. Under the condition of 40-45°C constant temperature water bath, add 2mol / L phosphoric acid and redissolved sodium aluminate solution into the seed tank in a homogeneous flow mode, the feeding time is 60min, and the pH of the reaction solution at the end of the control is 8.5-9.40 Aged at -45°C for 24 hours, separated, washed, and filtered to obtain highly active seed crystals (D50=0.91 μm). Be that 30% with seed crystal coefficient add above-mentioned seed crystal to the sodium aluminate solution after dilution (caustic alkali concentration is 110g / L, α k =1.5), in a hot water bath at 60°C, the stirring speed is 360r / min, and the reaction time is controlled at 20h. After the reaction was completed, the liquid and solid were separated, and the filter cake was washed with hot water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
oil absorptionaaaaaaaaaa
oil absorptionaaaaaaaaaa
oil absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a seed crystal by utilizing phosphoric acid and producing superfine aluminum hydroxide. A semi-product, namely aluminum hydroxide, in a Bayer-process aluminum oxide process is used as a raw material to carry out alkali digestion; the seed crystal is prepared by utilizing the phosphoric acid, and a superfine aluminum hydroxide flame retardant product is produced. According to the method disclosed by the invention, the granularity of the product is uniform, the product is not agglomerated and a dispersant is not needed.

Description

technical field [0001] The invention relates to the technical field of aluminum hydroxide production, in particular to a method for producing superfine aluminum hydroxide by using phosphoric acid as seed crystals. Background technique [0002] Due to the good thermal stability of ultra-fine aluminum hydroxide and no secondary pollution during combustion, it is a green flame retardant product. In recent years, the demand for flame retardant ultra-fine aluminum hydroxide has increased sharply at home and abroad, and the research and development cost is low. The ultra-fine aluminum hydroxide flame retardant has broad market application prospects and economic benefits. At present, the preparation of ultra-fine aluminum hydroxide mainly includes mechanical pulverization and chemical methods. In order to reverse the aggregation of ultra-fine aluminum hydroxide, dispersant is often added to the ultra-fine aluminum hydroxide before drying to prevent powder agglomeration and serious ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F7/14
CPCC01F7/14C01P2004/51C01P2006/65
Inventor 吕天宝武文焕冯怡利王军堂刘尧
Owner SHANDONG LUBEI ENTERPRISE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com