Moisture-absorbing and heat-discharging finishing agent for cotton and preparation method of moisture-absorbing and heat-discharging finishing agent
A heat finishing and finishing agent technology, which is applied in fiber treatment, textiles, papermaking, plant fibers, etc., can solve the problems of poor stability and achieve good shear resistance, not easy to absorb dust, and good hydrophilic and antistatic properties. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] A method for preparing a moisture-absorbing and heat-discharging finishing agent for cotton, comprising the following steps:
[0034] (1) Weighing: Inspect various raw materials according to the requirements, and weigh them according to the proportion of the formula for later use;
[0035] (2) Add 20% by weight of new-type amino-modified polysiloxane and 10% of ABn block polysilicon into the reaction kettle equipped with a stirring device in turn, and adjust the temperature of the reaction kettle to 40°C. After stabilization, turn on the stirring device, the speed of the stirring device is 100rpm, and the stirring time is 20min until the stirring is uniform;
[0036] (3) After the stirring is completed, add 5% by weight polymer surfactant into the reactor, turn on the stirring device, the stirring device rotates at 300 rpm, and the stirring time is 20 minutes until the stirring is uniform;
[0037] (4) Add glacial acetic acid with a weight percentage of 0.5% into the r...
Embodiment 2
[0042] A method for preparing a moisture-absorbing and heat-discharging finishing agent for cotton, comprising the following steps:
[0043] (1) Weighing: Inspect various raw materials according to the requirements, and weigh them according to the proportion of the formula for later use;
[0044] (2) Add 23.6% by weight of new amino-modified polysiloxane and 13.5% of ABn block polysilicon into the reaction kettle equipped with a stirring device in turn, and adjust the temperature of the reaction kettle to 45°C. After stabilization, turn on the stirring device, the rotating speed of the stirring device is 200rpm, and the stirring time is 25min until the stirring is uniform;
[0045] (3) After the stirring is completed, add 6.5% alkyl glycoside by weight into the reactor, start the stirring device, the stirring device rotates at 350 rpm, and the stirring time is 25 minutes until the stirring is uniform;
[0046] (4) Add glacial acetic acid with a weight percentage of 0.88% into...
Embodiment 3
[0050] A method for preparing a moisture-absorbing and heat-discharging finishing agent for cotton, comprising the following steps:
[0051] (1) Weighing: Inspect various raw materials according to the requirements, and weigh them according to the proportion of the formula for later use;
[0052] (2) Add 25% by weight of new-type amino-modified polysiloxane and 15% of ABn block polysilicon into the reaction kettle equipped with a stirring device in turn, and adjust the temperature of the reaction kettle to 50°C. After stabilization, turn on the stirring device, the rotating speed of the stirring device is 300rpm, and the stirring time is 30min, until the stirring is uniform;
[0053] (3) After the stirring is completed, add 10% by weight polymer surfactant into the reaction kettle, start the stirring device, the stirring device rotates at 400 rpm, and the stirring time is 30 minutes until the stirring is uniform;
[0054] (4) Add glacial acetic acid with a weight percentage o...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com