Dirt-proof and antibacterial textile fabric and preparation method thereof

A textile fabric and anti-fouling technology, applied in the direction of cellulose/protein conjugated artificial filament, conjugated synthetic polymer artificial filament, etc., can solve the problem of difficult removal of stains, achieve cheap raw materials, good application prospects, suitable The effect of large-scale industrial application

Inactive Publication Date: 2017-09-19
SUZHOU DANFANG TEXTILE R & D
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Natural fibers will inevitably be stained during normal use, but these attached stains are often difficult to remove

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dirt-proof and antibacterial textile fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Weigh 5 parts of polyester yarn, 10 parts of mugwort fiber, 10 parts of soybean fiber, 5 parts of polylactic acid fiber, 15 parts of water-absorbing fiber, 8 parts of polyacrylonitrile fiber, and 10 parts of polyethylene terephthalate by weight. 1 part of hexamethylcyclotrisiloxane, 2 parts of polyvinylpyrrolidone, 1 part of alkaline pectinase, 2 parts of tung oil anhydride, 1 part of tea saponin, 2 parts of benzoyl peroxide butyl acetate, acetyl 1 part of tri-n-hexyl citrate, 3 parts of potassium chloride, 1 part of 3-acrylic acid propyltrimethoxysilane, 2 parts of oleic acid acyl, 2 parts of zinc palmitate;

[0026] (2) Soak polyester yarn, mugwort fiber, soybean fiber, alkaline pectinase, tung oil anhydride, and tea saponin in 3% hydrogen peroxide for disinfection and activation, soak for 2 hours, dry at 60°C, and ultrasonically pulverize for 30 minutes , the ultrasonic power is 200KW;

[0027] (3) Add polylactic acid fiber, water-absorbing fiber, polyacrylonitr...

Embodiment 2

[0034] (1) Weigh 7 parts of polyester yarn, 13 parts of mugwort fiber, 12 parts of soybean fiber, 6 parts of polylactic acid fiber, 16 parts of water-absorbing fiber, 10 parts of polyacrylonitrile fiber, and 12 parts of polyethylene terephthalate by weight. Parts, 2 parts of hexamethylcyclotrisiloxane, 3 parts of polyvinylpyrrolidone, 1 part of alkaline pectinase, 3 parts of tung oil anhydride, 2 parts of tea saponin, 2 parts of butyl peroxide benzoyl acetate, acetyl 1 part of tri-n-hexyl citrate, 4 parts of potassium chloride, 2 parts of N-2 (aminoethyl) 3-aminopropylmethyldimethoxysilane, 3 parts of glyceryl tristearate, lauric acid Calcium 2 parts;

[0035] (2) Soak polyester yarn, mugwort fiber, soybean fiber, alkaline pectinase, tung oil anhydride, and tea saponin in 3% hydrogen peroxide for disinfection and activation, soak for 2.4 hours, dry at 62°C, and ultrasonically pulverize for 30 minutes , the ultrasonic power is 220KW;

[0036] (3) Polylactic acid fiber, absorb...

Embodiment 3

[0043](1) Weigh 9 parts of polyester yarn, 17 parts of mugwort fiber, 16 parts of soybean fiber, 13 parts of polylactic acid fiber, 19 parts of water-absorbing fiber, 13 parts of polyacrylonitrile fiber, and 14 parts of polyethylene terephthalate by weight. 3 parts, 3 parts of hexamethylcyclotrisiloxane, 4 parts of polyvinylpyrrolidone, 2 parts of alkaline pectinase, 4 parts of tung oil anhydride, 3 parts of tea saponin, 3 parts of benzoyl peroxide butyl acetate, acetyl 2 parts of tri-n-hexyl citrate, 5 parts of potassium chloride, 3 parts of N-2 (aminoethyl) 3-aminopropylmethyltrimethoxysilane, 4 parts of hexenylbisstearamide, naphthenic acid Barium 3 parts;

[0044] (2) Soak polyester yarn, mugwort fiber, soybean fiber, alkaline pectinase, tung oil anhydride, and tea saponin in 3% hydrogen peroxide for disinfection and activation, soak for 2.7 hours, dry at 64°C, and ultrasonically pulverize for 30 minutes , the ultrasonic power is 240KW;

[0045] (3) Polylactic acid fiber...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses dirt-proof and antibacterial textile fabric and a preparation method thereof. The textile fabric is prepared from raw materials in parts by weight as follows: 5-10 parts of polyester yarn and 10-20 parts of folium artemisiae argyi fiber, 10-18 parts of soybean fiber, 5-15 parts of polylactic acid fiber, 15-20 parts of water-absorptive fiber, 8-15 parts of polyacrylonitrile fiber, 10-15 parts of polyethylene terephthalate, 1-4 parts of hexamethyl cyclotrisiloxane, 2-5 parts of polyvinylpyrrolidone, 1-2 parts of alkaline pectinase, 2-5 parts of tung oil anhydride, 1-3 parts of tea saponin, 2-3 parts of benzoyl peroxide butyl acetate, 1-2 parts of acetyl tri-n-hexyl citrate, 3-6 parts of potassium chloride, 1-4 parts of a coupling agent, 2-5 parts of a dispersant and 2-3 parts of a heat stabilizer. The prepared dirt-proof and antibacterial spinning fabric has an oil rub resistance characteristic and is high in strength, durable and broad in application range; besides, the invention further discloses a corresponding preparation method.

Description

technical field [0001] The invention relates to the field of textile materials, in particular to an antifouling and antibacterial textile fabric and a preparation method thereof. Background technique [0002] With the improvement of living standards, people have higher and higher requirements for clothing, not only have high requirements for aesthetics, but also have higher expectations for safety, environmental protection and comfort. Natural fibers exist in nature and can be obtained directly. According to their sources, they are divided into three categories: plant fibers, animal fibers and mineral fibers. Due to the good comfort, flexibility and breathability of natural fibers, it has received widespread attention. Natural fibers will inevitably be stained during normal use, but these attached stains are often difficult to remove. Among them, the antifouling processing of cotton textiles is generally done by fluorine resin to make the textiles have oil repellency, so a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/14D01F8/02D01F8/08D01F1/10
CPCD01F8/14D01F1/10D01F1/103D01F8/02D01F8/08
Inventor 何晓东
Owner SUZHOU DANFANG TEXTILE R & D
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap