China-hemp blended surface layer material for hygienic products and preparation method of material

A technology for surface materials and hygiene products, applied in textiles, papermaking, non-woven fabrics, etc., can solve the problems of dryness, air permeability and skin-friendly properties, and achieve the effect of soft and comfortable fabrics and good natural antibacterial properties

Inactive Publication Date: 2017-10-27
XINLONG HLDG GROUP
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is the problem of poor dryness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • China-hemp blended surface layer material for hygienic products and preparation method of material

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example 1

[0032] The method for preparing hemp blended surface layer material for sanitary products in this embodiment includes the following steps:

[0033] Hemp fiber and raw cotton fiber are fed, coarsely opened, blended, pre-carded, blended, combed, laid, drafted, spunlaced, and dried to obtain the hemp blended surface for sanitary products. Layer material.

[0034] (1) Raw material preparation: Hemp fiber and raw cotton fiber are selected. The average length of hemp fiber is 32mm and the average size is 2.4D. The average length of raw cotton fiber is 38mm and the average size is 1.4D. The initial quantitative is scheduled to be 32g / m 2 , The mass percentage of hemp fiber is 30%, and the mass percentage of raw cotton fiber is 70%.

[0035] (2) Cotton feeding and rough opening: the hemp fiber and raw cotton fiber are sent to the rough opening machine by the automatic cotton feeder for opening, so that the fiber block and the large cotton mass are separated, mixed and full...

Example Embodiment

[0065] Example 2

[0066] The method for preparing hemp blended surface layer material for sanitary products in this embodiment includes the following steps:

[0067] Hemp fiber and Lyocell fiber are fed, coarsely opened, blended, pre-carded, blended, combed, laid, drafted, spunlaced, and dried to obtain the hemp blended surface for sanitary products. Layer material.

[0068] (1) Raw material preparation: Hemp fiber and Lyocell fiber are selected. The average length of hemp fiber is 32mm and the average fineness is 2.4D. The average length of Lyocell fiber is 38mm and the average fineness is 1.5D. The initial quantitative is scheduled to be 25g / m 2 , The mass percentage of hemp fiber is 50%, and the mass percentage of raw cotton fiber is 50%.

[0069] (2) Cotton feeding and rough opening: The hemp fiber and Lyocell fiber are sent to the rough opening machine by the automatic cotton feeder for opening, so that the fiber blocks are separated, mixed and fully opened. After rough openin...

Example Embodiment

[0099] Example 3

[0100] The method for preparing hemp blended surface layer material for sanitary products in this embodiment includes the following steps:

[0101] Hemp fiber and viscose fiber are fed, coarsely opened, blended, pre-carded, blended, combed, laid, drafted, spunlaced, and dried to obtain the hemp blended fabric for sanitary products. Surface material.

[0102] (1) Raw material preparation: Hemp fiber and viscose fiber are selected. The average length of hemp fiber is 32mm and the average fineness is 2.4D. The average length of viscose fiber is 38mm and the average fineness is 1.4D. The initial quantitative is scheduled to be 40g / m 2 , The mass percentage of hemp fiber is 40%, and the mass percentage of viscose fiber is 60%.

[0103] (2) Cotton feeding and rough opening: The hemp fiber and viscose fiber are sent to the rough opening machine by the automatic cotton feeder for opening, so that the fiber block and the large cotton mass are separated, mixed and fully open...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Finenessaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a China-hemp blended surface layer material for hygienic products. The China-hemp blended surface layer material for the hygienic products comprises, by mass, 20-50% of China hemp fiber and 50-80% of one of or combination of raw cotton fiber, Lyocell fiber, viscose fiber, polyester fiber and the polypropylene fiber.

Description

technical field [0001] The invention relates to a hemp blended surface layer material for sanitary products and a preparation method thereof. The hemp blended surface layer material can be used as sanitary napkins, tampons, baby diapers, adult diapers, diapers, and urine-separating pads and other surface materials. Background technique [0002] According to the preliminary market survey, there are various materials used for sanitary napkins, baby diapers, and adult diaper surface materials, such as pure cotton, polypropylene, polyethylene, etc. Each has its own different characteristics. The pure cotton material uses natural cotton as the raw material, which has the characteristics of skin-friendly, soft, and non-irritating; chemical materials such as polypropylene and polyethylene have the characteristics of breathability and dryness. However, each has its own shortcomings. The dryness of pure cotton material is poor, and the feeling of humidity is obvious; chemical materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/425D04H1/4258D04H1/435D04H1/4291D04H1/492D04H1/70
CPCD04H1/425D04H1/4258D04H1/4291D04H1/435D04H1/492D04H1/70
Inventor 杨晓伟朱永号贾耀芳陈喆谭卫东谢国诗王仕飞
Owner XINLONG HLDG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap