Ice skate blade provided with alloy coating and used for skating shoes

A technology of alloy coating and ice skates, which is applied in metal material coating technology, skates, coatings, etc., can solve the problems of skating impact, time-consuming and laborious, skate wear and other problems, and achieve good hardness, oxidation resistance, and high wear resistance properties, the effect of small surface roughness

Active Publication Date: 2017-11-17
HUAINAN BAIBANG PNEUMATIC TECH CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the wear and tear of skates is the main reason for the loss of skates, and it will have a great impact on skating. Although repeated sharpening can continue to be used in a short period of time, it is time-consuming and laborious.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A skate with an alloy coating for skates, characterized in that: the skate includes a base blade and an alloy coating covered on the base blade; the raw material of the alloy coating is alloy cladding powder, and the alloy The particle size of the cladding powder is 100 μm; the alloy cladding powder contains the following element composition: C: 2.50%, Si: 0.50%, Zr: 3.30%, Cu: 2.50%, Hf: 0.05%, Ni: 4.50%, Al : 1.50%, B: 0.20%, the balance is Fe and unavoidable impurities, and the above-mentioned percentages are percentages by mass; the tensile strength of the skates for skates with an alloy coating reaches 240MPa, the hardness reaches 60HRC, and the wear resistance 3 times higher than the base blade.

[0018] The preparation method of described ice blade comprises the following steps:

[0019] (1) Heat treatment of the base blade: carry out quenching treatment and tempering treatment on the base blade, the quenching temperature is 400°C, and the tempering temperature ...

Embodiment 2

[0023] A skate with an alloy coating for skates, characterized in that: the skate includes a base blade and an alloy coating covered on the base blade; the raw material of the alloy coating is alloy cladding powder, and the alloy The particle size of the cladding powder is 120 μm; the alloy cladding powder contains the following element composition: C: 2.80%, Si: 0.70%, Zr: 3.00%, Cu: 1.70%, Hf: 0.07%, Ni: 5.20%, Al : 1.00%, B: 0.15%, the balance is Fe and unavoidable impurities, and the above-mentioned percentages are percentages by mass; the tensile strength of the skates for skates with an alloy coating reaches 245MPa, and the hardness reaches 63HRC. 5 times higher than the base blade.

[0024] The preparation method of described ice blade comprises the following steps:

[0025] (1) Heat treatment of the base blade: carry out quenching treatment and tempering treatment on the base blade, the quenching temperature is 500°C, and the tempering temperature is 200°C; The part ...

Embodiment 3

[0029] A skate with an alloy coating for skates, characterized in that: the skate includes a base blade and an alloy coating covered on the base blade; the raw material of the alloy coating is alloy cladding powder, and the alloy The particle size of the cladding powder is 150 μm; the alloy cladding powder contains the following element composition: C: 3.50%, Si: 0.80%, Zr: 2.80%, Cu: 1.50%, Hf: 0.10%, Ni: 5.50%, Al : 1.00%, B: 0.10%, the balance is Fe and unavoidable impurities, and the above-mentioned percentages are percentages by mass; the tensile strength of the skate with alloy coating reaches 250MPa, the hardness reaches 65HRC, and the wear resistance 3~5 times higher than that of the base blade.

[0030] The preparation method of described ice blade comprises the following steps:

[0031] (1) Heat treatment of the base blade: carry out quenching treatment and tempering treatment on the base blade, the quenching temperature is 500°C, and the tempering temperature is 30...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an ice skate blade provided with an alloy coating and used for skating shoes. A matrix blade of the ice skate blade is subjected to heat treatment, different hardness degrees required by different parts of the ice skate blade are obtained, so that after being coated with the coating, the ice skate blade body has rigidity and toughness of resisting and transmitting ice push-off power, and a cutting edge can be wear-resistant enough and has surface roughness as small as possible. Besides, alloy coated powder of the skate blade alloy coating adopts a specific alloy element composition proportion, so that the hardness of the alloy coating is remarkably improved, and the ice skate blade has quite high wear resistance, good hardness and oxidation resistance.

Description

technical field [0001] The invention relates to the field of cutting tool materials, in particular to a skate blade for skates with an alloy coating. Background technique [0002] Ice skating is a sport that combines personal strength and technology with skates with skates as a tool. Ice skating is one of the main events of the Winter Olympic Games. The most important factor affecting the level of competition is the performance of the skates on the skates, in addition to the personal skills of the skaters. For example, the ability to transmit ice pedaling force, resistance to plastic deformation, resistance to brittle fracture and long-term wear resistance, etc. In the mechanical structure of ice skates, the physical characteristics and mechanical properties of the blade are one of the main factors that determine the quality of the ice blade, which involves the overall strength of the blade, the hardness of the blade, and the surface roughness of the ice-touching surface. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A63C1/30A63C1/42C23C24/10C22C37/10C21D1/18C21D9/20
Inventor 周君
Owner HUAINAN BAIBANG PNEUMATIC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap