Non-graphitic water-soluble lubricant used for plasticity working, and preparation method thereof

A plastic processing, non-graphite technology, used in lubricating compositions, petroleum industry, etc., can solve the problems of complex production process and poor lubricating performance, and achieve the effect of hard film, good lubricating performance and inhibiting cracking

Inactive Publication Date: 2017-11-17
MORESCO HANANO DIE CASTING COATING SHANGHAI CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The applicant aims at the disadvantages of poor lubricating performance and complex manufacturing process in the above-mentioned existing lubricants, and provides a non-graphite water-soluble lubricant for plastic processing and a preparation method, the lubricity of which has reached the level of non-graphite lubricants. At the same level, the lubricating film has good followability, excellent lubricating performance, and does not contain graphite, which can greatly improve the working environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-graphitic water-soluble lubricant used for plasticity working, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Add sodium hydroxide to water to make a solution, stir and heat to 80°C, add isophthalic acid to neutralize, after the isophthalic acid is dissolved, add carboxyethyl cellulose sodium salt, keep stirring at 80°C to dissolve, then cool To room temperature, embodiment 1 is prepared with a lubricant for water-soluble plastic processing.

Embodiment 2～5 and comparative example 2～4

[0043] Add sodium hydroxide to water to make a solution, stir and heat to 80°C, add polymaleic acid resin to neutralize, after the polymaleic acid resin is completely dissolved, then add sodium hydroxide, keep stirring at 80°C and add to various carboxylic acids And, then, cooling to room temperature, embodiment 2~5 and comparative example 2~4 are prepared with the lubricant for water-soluble plastic working.

[0044] The strength and lubricity of the sprayed coatings of the water-soluble plastic working lubricants of Examples and Comparative Examples were evaluated by the following methods.

[0045]Spray coating film strength: under the conditions of pressure 0.3KPa, spraying distance 300mm, and spraying speed 4cc / 10sec, spray the lubricant composition for water-soluble plastic processing of Examples and Comparative Examples onto an iron mold heated to 200°C, Then, lower the sprayed mold to room temperature, wipe the lubricating film attached to the mold with a special cloth,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
friction coefficientaaaaaaaaaa
Login to View More

Abstract

The invention discloses a non-graphitic water-soluble lubricant used for plasticity working The lubricant comprises an alkali metal salt of m-phthalic acid, a water-soluble polymer and water. The used alkali metal salt of m-phthalic acid has a good lubricating performance in a strict warm or hot plasticity working environment. A condensate formed by combining crystals of the alkali metal salt of m-phthalic acid and the water-soluble polymer of alkali metal salt or fiber derivative of polymaleic acid resin adheres to the surface of a die and forms a lubricating film, and the lubricating film has a same strength with a high-temperature spray film formed by a graphite lubricant, is heatproof, hard and solid, and has a small friction coefficient, so the non-graphitic water-soluble lubricant can be used for the warm or hot plastic working of iron or aluminum alloy materials, makes the part processing quality good, contains no graphite, and can greatly improve the working environment.

Description

technical field [0001] The invention relates to the technical field of lubricants for metal temperature or thermal plastic processing, in particular to a non-graphite water-soluble lubricant for plastic processing and a preparation method. Background technique [0002] For a long time, the lubricants used for metal temperature or thermal plastic processing mainly include graphite lubricants made of graphite dispersed in water, oil lubricants such as mineral oil, and non-graphite lubricants. During the use of graphite lubricants, graphite powder is easy to scatter, easily pollute the environment, and cause damage to the health of workers; graphite is a good conductor of electricity, and graphite dispersed in the air is likely to cause electrical accidents; after treatment with graphite lubricants The surface of high-quality forgings is not easy to clean, and it takes a lot of manpower and material resources. The use of oil-based lubricants presents a fire hazard. Chinese pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02C10N30/06C10N40/24C10N30/08
CPCC10M173/02C10N2030/06C10N2030/08C10N2040/24C10N2040/242C10N2040/245C10N2040/246C10N2040/247
Inventor 浜岛研太郎曽田孝雄
Owner MORESCO HANANO DIE CASTING COATING SHANGHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com