Mold pressing process for high-strength composite OSB plate
A composite board and high-strength technology, applied in the field of boards, can solve problems such as easy cracking and deformation of concave and convex parts, affect the production quality of boards, reduce the qualified rate of boards, etc., and achieve the effect of reducing the difficulty of processing technology, small deformation and long service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A molding process for OSB high-strength composite boards, comprising the steps of:
[0025] a. Ammonia immersion and health preservation of OSB board
[0026] Soak the OSB board in ammonia water for 5 minutes, and then cover and seal the soaked OSB board with a sealing film, allowing the ammonia water to permeate naturally for 65 hours until the ammonia water is evenly distributed in the OSB board;
[0027] b. OSB board molding
[0028] Place the OSB board on the mold of the hot press machine, the upper and lower molds of the mold are attached to the upper and lower sides of the OSB board, the mold temperature is 160 degrees, and after 100s of heat preservation, perform multi-pass compression molding; the reduction of each pass is 2mm , the pressure of each pass is 10MPa, and the pressing is carried out for 2 passes; after pressing and forming, it is naturally cooled to room temperature;
[0029] c. Technology veneer and 0SB board molded into one
[0030] Use a glue ...
Embodiment 2
[0034] A molding process for OSB high-strength composite boards, comprising the steps of:
[0035] a. Ammonia immersion and health preservation of OSB board
[0036] Soak the OSB board in ammonia water for 8 minutes, and then cover and seal the soaked OSB board with a sealing film, allowing the ammonia water to permeate naturally for 72 hours until the ammonia water is evenly distributed in the OSB board;
[0037] b. OSB board molding
[0038] Place the OSB board on the mold of the hot press machine, the upper and lower molds of the mold are attached to the upper and lower sides of the OSB board, the mold temperature is 165 degrees, and multi-pass compression molding is carried out after heat preservation for 120s; the reduction of each pass is 5mm , the pressure of each pass is 12MPa, and the pressing is carried out for 3 passes; after pressing and forming, it is naturally cooled to room temperature;
[0039] c. Technology veneer and 0SB board molded into one
[0040] Use ...
Embodiment 3
[0044] A molding process for OSB high-strength composite boards, comprising the steps of:
[0045] a. Ammonia immersion and health preservation of OSB board
[0046] Soak the OSB board in ammonia water for 10 minutes, and then cover and seal the soaked OSB board with a sealing film, allowing the ammonia water to permeate naturally for 80 hours until the ammonia water is evenly distributed in the OSB board;
[0047] b. OSB board molding
[0048] Place the OSB board on the mold of the hot press machine, the upper and lower molds of the mold are attached to the upper and lower sides of the OSB board, the mold temperature is 170 degrees, and after 150s of heat preservation, multi-pass compression molding is carried out; the reduction of each pass is 7mm , the pressure of each pass is 15MPa, and 4 passes of pressing are carried out; after pressing and forming, it is naturally cooled to room temperature;
[0049] c. Technology veneer and 0SB board molded into one
[0050]Use a gl...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
density | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap