Method for preparing sulfydryl-rich keratin and promoting rapid gelating of silk fibroin and application
A technology for silk fibroin and keratin, which is applied to skin care preparations, pharmaceutical formulations, cosmetic preparations and other directions, can solve the problems of unfavorable silk fibroin biocompatibility, slow gelation speed and the like, and achieves a simple and convenient preparation method. , the effect of good applicability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] A kind of mercapto-rich keratin and its method for promoting rapid gelation of silk fibroin:
[0031] Weigh 5g of washed and shredded wool and add it into 50ml of a mixed solution containing 0.1M sodium sulfide, 8M urea and 0.2M sodium lauryl sulfate and stir at a speed of 60 rpm to dissolve 7 hours, after the wool reaction is completely filtered, dialyzed, concentrated and diluted to prepare a wool keratin aqueous solution with a concentration of 50 mg / mL carrying a large number of mercapto groups. Weigh 10 g of silkworm cocoons cut into pieces and put them into 2 L of 0.5% sodium bicarbonate solution, boil for 30 min and repeat twice, remove silk sericin and wash with deionized water 4 times. Weigh 5g of dried degummed silk and put it into 30mL lithium bromide solution with a concentration of 9.3M, place it at 50°C for 4 hours, take it out, dialyze it in a dialysis bag with a molecular weight of 3500D, dilute and filter to obtain Pure silk fibroin solution with a mas...
Embodiment 2
[0034] A kind of mercapto-rich keratin and its method for promoting rapid gelation of silk fibroin:
[0035] Weigh 4g of washed and shredded wool, add 60ml of mercaptoethanol with a concentration of 0.2M, urea with a concentration of 8M and sodium lauryl sulfate with a concentration of 0.3M and stir to dissolve at a speed of 50 rpm. Hours, after the wool reaction is completely filtered, dialyzed, concentrated and diluted, a wool keratin aqueous solution with a concentration of 40 mg / mL is prepared. Weigh 6g of dried degummed silk and put it into 30mL lithium bromide solution with a concentration of 9.3M, place it at 60°C and dissolve it for 6 hours, take it out, dialyze it with a dialysis bag with a molecular weight of 3500D, dilute and filter to obtain Pure silk fibroin solution with a mass concentration of 40mg / mL.
[0036] Measure 400 μL and 600 μL of the keratin solution and silk fibroin solution with a concentration of 50 mg / mL, respectively, with a pipette, mix well and...
Embodiment 3
[0038]The washed discarded human hair was stirred and dissolved with 4M sodium hydroxide and 0.2M mercaptoethanol, and after filtration, dialysis, concentration and dilution, an aqueous solution of human hair keratin with a concentration of 50 mg / mL was obtained. Weigh 10 g of silkworm cocoons cut into pieces and put them into 2 L of 0.5% sodium bicarbonate solution, boil for 30 min and repeat twice, remove silk sericin and wash with deionized water 4 times. Weigh 5g of dried degummed silk and put it into 30mL lithium bromide solution with a concentration of 9.3M, place it at 50°C for 4 hours, take it out, dialyze it in a dialysis bag with a molecular weight of 3500D, dilute and filter to obtain Pure silk fibroin solution with a mass concentration of 50mg / mL.
[0039] Measure 600 μL and 400 μL of keratin solution and silk fibroin solution with a concentration of 50 mg / mL, respectively, with a pipette, mix well and move them into a columnar mold. Let it stand for an hour, take...
PUM
Property | Measurement | Unit |
---|---|---|
shear modulus | aaaaa | aaaaa |
shear modulus | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap