Phosphate-containing cross-linked polymer palladium-loaded nano-catalyst and preparation and application thereof
A technology of cross-linked polymers and palladium nanometers, which is applied in the direction of organic compound/hydride/coordination complex catalysts, physical/chemical process catalysts, nanotechnology, etc., can solve the problems of few preparation and catalytic applications, and achieve large-scale The effect of market application value and broad development space
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1 Preparation of phosphoric acid-containing crosslinked polymer supported nano-palladium catalyst
[0031] In a three-necked flask, add divinylbenzene (DVB) (2.0g, 15mmol), acrylic acid (AA) (0.360g, 5mmol), diphenyl p-styryl phosphine (DPPS) (1.4416g, 5mmol), even Nitrogen diisobutyronitrile (0.07g) and ethyl acetate (30ml), protected by nitrogen. The reaction was carried out at 100°C for 24 hours without stirring. After the reaction, the solvent was dried to obtain 2.5 g of white powder as a copolymer of divinylbenzene, acrylic acid and diphenyl p-styryl phosphine (PDVB-AA-DPPS).
[0032] Dip 200mg of the above white powder into ammonium tetrachloropalladate ((NH 4 ) 2 PdCl 4 ) (10mg) methanol solution (10mL), stirred vigorously for 16h, centrifuged, washed with methanol, put into the methanol solution (10mL) of sodium borohydride (20mg), stirred vigorously for 6h, centrifuged, washed with methanol to obtain phosphoric acid-containing crosslinks The polymer suppor...
Example
[0033] Examples 2-7
[0034] The method of Example 1 was used to prepare the phosphoric acid-containing cross-linked polymer supported nano-palladium catalyst. The difference was that the molar ratio of DVB to AA and DPPS and (NH) were changed during the synthesis of PDVB-AA-DPPS. 4 ) 2 PdCl 4 The dosage, see Table 1:
Example
[0035] Examples 8-11
[0036] The method of Example 1 was used to prepare the phosphoric acid-containing cross-linked polymer supported nano-palladium catalyst, except that the type of phosphine-containing monomer in the synthesized cross-linked polymer was changed, as shown in Table 2:
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap