Polyamide composite material

A composite material and polyamide technology, applied in the field of polyamide composite materials, can solve problems such as poor dimensional stability, poor impact resistance, insufficient heat resistance, etc., to reduce friction coefficient, improve wear resistance, and improve stability Effect

Inactive Publication Date: 2018-03-30
黄巧萍
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, polyamide also has many disadvantages, such as high water absorption, easy embrittlement at low temperature and dry state, poor impact resistance, poor dimensional stability and insufficient heat resistance, etc. These problems make the use of polyamide restricted. Therefore, it is necessary to modify polyamides to overcome these shortcomings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A polyamide composite material, in parts by weight, comprises the following components:

[0018] 100 parts of aliphatic polyamide, 21 parts of polyolefin elastomer, 34 parts of diatomaceous earth, 5 parts of silicone rubber, 7 parts of filler, 16 parts of nanomaterials, 3 parts of polyethylene glycol-4000, 2 parts of silane coupling agent, 1 part of maleic anhydride graft compatibilizer;

[0019] The nanomaterial is a mixture of nano-zinc borate, nano-zinc sulfide and nano-molybdenum disulfide with a mass ratio of 2:1:3; the aliphatic polyamide is a mixture of polyamide 6 and polyamide 46 with a mass ratio of 5:2; the filler is mica powder or montmorillonite.

Embodiment 2

[0021] A polyamide composite material, in parts by weight, comprises the following components:

[0022] 100 parts of aliphatic polyamide, 37 parts of polyolefin elastomer, 42 parts of diatomaceous earth, 17 parts of silicone rubber, 9 parts of filler, 23 parts of nanomaterials, 5 parts of polyethylene glycol-4000, 5 parts of silane coupling agent, 2 parts of maleic anhydride graft compatibilizer;

[0023] The nanomaterial is a mixture of nano-zinc borate, nano-zinc sulfide and nano-molybdenum disulfide with a mass ratio of 2:1:3; the aliphatic polyamide is a mixture of polyamide 6 and polyamide 46 with a mass ratio of 5:2; the filler is mica powder or montmorillonite.

Embodiment 3

[0025] A polyamide composite material, in parts by weight, comprises the following components:

[0026] 100 parts of aliphatic polyamide, 21 parts of polyolefin elastomer, 42 parts of diatomaceous earth, 5 parts of silicone rubber, 9 parts of filler, 16 parts of nanomaterials, 5 parts of polyethylene glycol-4000, 2 parts of silane coupling agent, 2 parts of maleic anhydride graft compatibilizer;

[0027] The nanomaterial is a mixture of nano-zinc borate, nano-zinc sulfide and nano-molybdenum disulfide with a mass ratio of 2:1:3; the aliphatic polyamide is a mixture of polyamide 6 and polyamide 46 with a mass ratio of 5:2; the filler is mica powder or montmorillonite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyamide composite material. The polyamide composite material comprises the following components in parts by weight: 100 parts of aliphatic polyamide, 21-37 parts of polyolefin elastomer, and 34-42 parts of diatomaceous earth , 5-17 parts of silicone rubber, 7-9 parts of filler, 16-23 parts of nanomaterials, 3-5 parts of polyethylene glycol, 2-5 parts of coupling agent, 1-2 parts of compatibilizer; the polyamide composite The material has good wear resistance, excellent impact resistance and good thermal stability, and is very suitable for use as auto parts.

Description

technical field [0001] The invention relates to a polyamide composite material. Background technique [0002] Polyamide (PA) is obtained by polycondensation of dibasic acid and diamine or amino acid, and is a general term for resins containing repeated amide groups in the molecular chain. Polyamides can be divided into three groups according to their structure: aliphatic polyamides, aliphatic-aromatic polyamides and aromatic polyamides. Among them, there are many varieties of aliphatic polyamides, large output and wide application. The name of this type of polyamide is mainly determined by the specific number of carbon atoms in the synthetic monomer. Polyamide synthesis methods can be divided into three main types: melt polycondensation, interfacial polycondensation, and solid-state polymerization. [0003] Polyamide has good mechanical properties, heat resistance, wear resistance, chemical resistance, flame retardancy and self-lubrication, and is easy to process and has a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L77/06C08L23/08C08L83/04C08K13/02C08K3/34C08K3/38C08K3/30
CPCC08L77/02C08K2003/3009C08K2003/3036C08K2003/387C08K2201/011C08L2201/08C08L2205/02C08L2205/035C08L77/06C08L23/0815C08L83/04C08K13/02C08K3/34C08K3/38C08K3/30
Inventor 黄巧萍
Owner 黄巧萍
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com