Marble glaze ceramic product and preparation method thereof

A technology for ceramic products and marble, applied in the field of marble glaze ceramic products and their preparation, can solve problems such as peeling, corrugation, cracking, etc., and achieve the effects of reducing cracking, simple preparation method and solving environmental pollution

Active Publication Date: 2018-04-20
福建省德化新奇丽工艺有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation of marble glazed ceramic products is not so simple. The expansion coefficient of the bod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] Marble glaze ceramic products. The raw material of the glaze is the waste marble slurry produced in the marble production process. The ceramic body includes the following raw materials in parts by mass: 15 parts of kaolin, 18 parts of calcite, 12 parts of limestone, 8 parts of quartz, waste porcelain 6 parts of powder, 3 parts of calcium oxide, 2 parts of titanium dioxide, 2 parts of pigment.

[0029] The preparation method of the marble glaze ceramic product includes the following steps:

[0030] 1) Weigh and mix each raw material component of the ceramic body according to the formula, add it to a ball mill, add water accounting for 50% of the material mass, ball mill for 12 hours, and screen the slurry fineness to pass a 300-mesh sieve;

[0031] 2) Perform magnetic separation to remove iron impurities contained in the mud;

[0032] 3) Press and filter the mud obtained in the previous step, and the water content of the mud after the press filter is 21%, and t...

Example Embodiment

[0037] Example 2

[0038] Marble glaze ceramic products. The raw material of the glaze is the waste marble slurry produced in the marble production process. The ceramic body includes the following raw materials in parts by mass: 18 parts of kaolin, 21 parts of calcite, 15 parts of limestone, 10 parts of quartz, waste porcelain 8 parts of powder, 5 parts of calcium oxide, 3 parts of titanium dioxide, 4 parts of pigment.

[0039] The preparation method of the marble glaze ceramic product includes the following steps:

[0040] 1) First select the calcite to remove impurities, and crush it to a particle size of less than 4mm, then weigh the raw material components of the ceramic body according to the formula, mix and add to the ball mill, and then add 60% of the material mass, ball mill 12h, slurry The fineness can be screened according to the standard of 400 mesh sieve;

[0041] 2) Perform magnetic separation to remove iron impurities contained in the mud;

[0042] 3) Press and filter th...

Example Embodiment

[0047] Example 3

[0048] Marble glaze ceramic products. The raw material of the glaze is the waste marble slurry produced in the marble production process. The ceramic body includes the following raw materials in parts by mass: 21 parts of kaolin, 25 parts of calcite, 16 parts of limestone, 12 parts of quartz, waste porcelain 10 parts of powder, 7 parts of calcium oxide, 4 parts of titanium dioxide, 5 parts of pigment.

[0049] The preparation method of the marble glaze ceramic product includes the following steps:

[0050] 1) First select the calcite to remove impurities, and crush it to a particle size of less than 4mm, then weigh the raw material components of the ceramic body according to the formula, mix and add to the ball mill, and then add 60% of the material mass, ball mill 12h, slurry The fineness can be screened according to the standard of 400 mesh sieve;

[0051] 2) Perform magnetic separation to remove iron impurities contained in the mud;

[0052] 3) Press filter the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a marble glaze ceramic product and a preparation method thereof, and belongs to the technical field of ceramics. A glaze raw material of the marble glaze ceramic product is waste marble pulp produced in the process of marble production. A ceramic body includes the following raw materials by mass: 15 to 21 parts of kaolin, 18 to 25 parts of calcite, 12 to 16 parts of limestone, 8 to 12 parts of quartz, 6 to 10 parts of waste porcelain powder, 3 to 7 parts of calcium oxide, 2-4 parts of titanium dioxide and 2 to 5 parts of a color material. The marble glaze ceramic product prepared by the invention has beautiful glaze surface, high glaze layer strength, good thermal stability, energy saving and emission reduction, and environmental friendliness.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a marble glaze ceramic product and a preparation method thereof. Background technique [0002] Marble originally refers to the white limestone with black patterns produced in Dali, Yunnan Province. Later, the name gradually developed into a name for all limestones with various color patterns. Marble is very beautiful after being polished. It is mainly used for processing into various shapes and plates for the walls, floors, platforms, and columns of buildings. It is also often used as materials for monumental buildings such as monuments, towers, and statues. Marble can also be carved into practical arts such as arts and crafts, stationery, lamps, and utensils. The beauty, elegance, and strength of marble make it more and more widely used. For example, it can be used as a glaze for ceramic vessels, which has both artistic value and practical storage. [0003] But pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/057C04B35/622C03C8/00C03C1/00C04B41/86
CPCC03C1/002C03C8/00C04B35/057C04B35/62204C04B41/5022C04B41/86C04B2235/3232C04B2235/3418C04B2235/349C04B2235/656C04B41/4539C04B41/0072
Inventor 马策新
Owner 福建省德化新奇丽工艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap