Li-containing flame-retardant wear-resisting high-thermal-conductivity Zn-Li alloy

A high thermal conductivity, lithium alloy technology, applied in the field of alloys, can solve problems such as limitations in the research, development and application of zinc-lithium alloys, easy flux inclusions in castings, complex equipment, etc. Life extension effect

Inactive Publication Date: 2018-04-27
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method has the disadvantages of high cost to varying degrees, flux inclusions in castings, and complicated equipment.
Therefore, the research, development and application of zinc-lithium alloys are limited.
Therefore, in the industrial and national defense fields that urgently need large-scale use of zinc-lithium alloys, there has always been a status quo that needs to be overcome urgently, such as low output, cumbersome processes, and high costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A zinc-lithium alloy with 450-degree smelting, Li-containing, flame-retardant, high wear-resistant and high thermal conductivity. By weight percentage, the chemical composition is: Li:1.4wt.%, Si:8.6wt.%, Ba:0.3wt.%, Ge:0.6wt.%, Mo:0.4wt.%, Y:0.8wt.%. , V:0.3wt.%, Nd:0.1wt.%, Yb:0.2wt.%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the induction furnace under the atmospheric environment, and use a silicon carbide crucible. Induction heating to 450 degrees to form an alloy solution, and use the electromagnetic effect to fully stir for about 10 minutes. The alloy liquid is kept at 450 degrees for 10 minutes and poured into the equipment at the same level as the hot top for semi-continuous casting, and the ingot moving speed is 10m / min. The ingot is deformed at room temperature, and the amount of rolling in each pass is 12%; every 3 passes of rolling requires an intermediate heat treatment to eliminate work hardenin...

Embodiment 2

[0020]A zinc-lithium alloy with 480-degree smelting, Li-containing, flame-retardant, high wear-resistant and high thermal conductivity. By weight percentage, the chemical composition is: Li: 1.2wt.%, Si: 6.8wt.%, Ba: 0.3wt.%, Ge: 0.6wt.%, Mo: 0.4wt.%, Y: 0.9wt.%. , V:0.3wt.%, Nd:0.1wt.%, Yb:0.2wt.%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the induction furnace under the atmospheric environment, and use a silicon carbide crucible. Induction heating to 480 degrees to form an alloy solution, and use the electromagnetic effect to fully stir for about 10 minutes. The alloy liquid is kept at 480 degrees for 10 minutes and poured into the equipment at the same level as the hot top for semi-continuous casting, and the ingot moving speed is 9m / min. The cast ingot is deformed at room temperature, and the amount of rolling in each pass is 14%; every 3 passes of rolling require an intermediate heat treatment to eliminate work ...

Embodiment 3

[0022] A zinc-lithium alloy with 490-degree smelting, Li-containing, flame-retardant, high wear-resistant and high thermal conductivity. In terms of weight percentage, the chemical composition is: Li:0.9wt.%, Si:8.2wt.%, Ba:0.3wt.%, Ge:0.5wt.%, Mo:0.3wt.%, Y:0.9wt.%. , V:0.3wt.%, Nd:0.1wt.%, Yb:0.2wt.%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the induction furnace under the atmospheric environment, and use a silicon carbide crucible. Induction heating to 490 degrees to form an alloy solution, and use the electromagnetic effect to fully stir for about 10 minutes. The alloy liquid is kept at 490 degrees for 10 minutes and poured into the equipment at the same level as the hot top for semi-continuous casting, and the ingot moving speed is 10m / min. The ingot is deformed at room temperature, and the amount of rolling in each pass is 12%; every 3 passes of rolling requires an intermediate heat treatment to eliminate work...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Li-containing, flame-retardant, high-wear-resistant, and high-thermal-conduction zinc-lithium alloy. In terms of weight percentage, the chemical composition of the alloy is: Li:0.6‑1.8wt.%, Si:4.2‑10.6wt.%, Ba:0.2‑0.5wt.%, Ge:0.4‑0.8wt.%, Mo:0.2‑ 0.5wt.%, Y: 0.5‑1.0wt.%, V: 0.2‑0.4wt.%, Nd: 0.1‑0.2wt.%, Yb: 0.2‑0.3wt.%, the balance is zinc. Compared with traditional zinc alloys, this material has excellent wear resistance and thermal conductivity.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a zinc alloy. Background technique [0002] Zinc alloy is a cheap, energy-saving and high-quality new material that has been widely used at home and abroad in recent decades. It has the advantages of high tensile strength and hardness, good damping, good wear resistance, small friction coefficient, low friction temperature rise, and low material and manufacturing costs. At the same time, it also has good process performance, not only can be used for die casting, but also suitable for sand mold, metal mold, graphite mold, continuous casting, etc. Moreover, the source of raw materials is wide, the price is low, the energy consumption is low when melting, no pollution, and the service life is long. It is a new type of alloy that is developing rapidly at home and abroad. At present, it has been used in industry to partially replace structural materials such as bronze, brass, cast ir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C18/00C22F1/16
CPCC22C18/00C22F1/165
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com