Method for leaching spodumene based on combination of microwave and pressure field

A technology of spodumene and pressure field, which is applied in the field of joint leaching of spodumene based on microwave and pressure field, can solve the problems of narrow transformation temperature range and low transformation rate of spodumene raw ore, and reduce the hidden danger of melting rings, The effect of short process and short technological process

Active Publication Date: 2018-06-15
INST OF MULTIPURPOSE UTILIZATION OF MINERAL RESOURCES CHINESE ACAD OF GEOLOGICAL SCI
View PDF11 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this patent, the transformation temperature range of spodumene raw ore is narrow, that is, 930-1050°C, and the transformation rate is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for leaching spodumene based on combination of microwave and pressure field
  • Method for leaching spodumene based on combination of microwave and pressure field

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A method based on microwave and pressure field combined leaching spodumene, comprising the steps:

[0034] 1) Grinding: use spodumene concentrate as raw material, grind, add coal powder of 2% of the total mass of raw material, mix evenly, and obtain a mixture;

[0035] 2) Crystal transformation

[0036] Using the silicon carbide lining the rotary kiln as the heat source carrier, heat the mixture obtained in step 1) to 1000°C under the condition of microwave power of 1500w, and then use microwave irradiation to transform the crystal form at a constant temperature of 1000°C 15min, then cooled to room temperature to obtain β-type spodumene;

[0037] 3) Leaching

[0038] Grind the β-type spodumene obtained in step 2), and add water to make a slurry to obtain a slurry; put the slurry into an autoclave, then add sulfuric acid with a concentration of 2%, and under the conditions of a pressure of 0.2Mpa and 120°C, the stirring speed is 500r / min, leaching for 20min to obtain ...

Embodiment 2

[0041] A method based on microwave and pressure field combined leaching spodumene, comprising the steps:

[0042] 1) Grinding: use spodumene concentrate as raw material, grind, add coal powder with 8% of the total mass of raw material, mix evenly, and obtain a mixture;

[0043] 2) Crystal transformation

[0044] Using the silicon carbide lining the rotary kiln as the heat source carrier, the mixture obtained in step 1) is heated to 1180°C under the condition of microwave power of 4000w, and then the crystal form is transformed under the constant temperature condition of 1180°C by microwave irradiation. 120min, then cooled to room temperature to obtain β-type spodumene;

[0045] 3) Leaching

[0046] Grind the β-type spodumene obtained in step 2), and add water to make a slurry to obtain a slurry; put the slurry into an autoclave, then add sulfuric acid with a concentration of 10%, and under the conditions of a pressure of 1.6Mpa and 200°C, the stirring speed is 1800r / min, le...

Embodiment 3

[0049] A method based on microwave and pressure field combined leaching spodumene, comprising the steps:

[0050] 1) Grinding: use spodumene concentrate as raw material, grind, add coal powder with 5% of the total mass of raw material, mix evenly, and obtain a mixture;

[0051] 2) Crystal transformation

[0052] Using the silicon carbide lining the rotary kiln as the heat source carrier, heat the mixture obtained in step 1) to 1100°C under the condition of microwave power of 2500w, and then use microwave irradiation to transform the crystal form under the constant temperature condition of 1100°C 60min, then cooled to room temperature to obtain β-type spodumene;

[0053] 3) Leaching

[0054] Grind the β-type spodumene obtained in step 2), and add water to make a slurry to obtain a slurry; put the slurry into an autoclave, then add sulfuric acid with a concentration of 6%, and under the conditions of a pressure of 0.8Mpa and 160°C, the stirring speed is 1100r / min, leaching fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for leaching spodumene based on combination of a microwave and a pressure field, and belongs to the production technology field of lithium salt extracted from spodumene in chemical metallurgy. The method comprises the steps of (1) grinding ore; (2) transforming an out-field irradiation crystal form; (3) pressure leaching; and (4) separating and purifying. Accordingto the technical scheme, microwave irradiation is adopted on the spodumene, so that a crystal form transformation temperature range is expanded; and then a direct sulfuric acid leaching process is carried out on the irradiated spodumene, valuable metals such as lithium are leached into lithium sulfate under the conditions of heating and pressurizing, then the lithium sulfate is separated and purified, a solution is recovered, and a final product i.e. the lithium salt is obtained, so that an application range of a complicated spodumene raw material is further expanded. The technical scheme hasthe advantages of short flow, energy conservation, emission reduction, excellent current joining process and the like.

Description

technical field [0001] The invention specifically relates to a method for leaching spodumene combined with microwave and pressure field, and belongs to the technical field of production of lithium salt extracted from spodumene in chemical metallurgy. Background technique [0002] Spodumene (LiAlSi 2 o 6 ) ore is an important chemical raw material, and it is also the main raw material for preparing other lithium salts and lithium metal, generally containing Li 2 O1~2%, Li after beneficiation and enrichment 2 O content can reach 5% to 7%. Rock-type lithium deposits are mainly pegmatite-type, and are concentrated in Altai, Xinjiang, and Jiaka, western Sichuan. Among them, the proven lithium oxide resources in western Sichuan are about 3.6 million tons, accounting for the nationally proven lithium resources. (containing salt lake lithium and hard rock lithium), accounting for more than 7.8% of the world's proven lithium resources. Chen Yuedi from Xinjiang Haoxin Lithium Sal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B26/12C22B3/08C22B1/02
CPCC22B1/02C22B3/08C22B26/12Y02P10/20
Inventor 翼成庆沈明伟朱昌洛蔡旺李可及周雄廖祥文
Owner INST OF MULTIPURPOSE UTILIZATION OF MINERAL RESOURCES CHINESE ACAD OF GEOLOGICAL SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com