Sunscreen cream and preparation method thereof

A technology of sunscreen lotion and dimethylsiloxane, which is applied in the directions of pharmaceutical formulations, cosmetic preparations, cosmetic preparations, etc., can solve the problems of strong irritation and poor skin feeling of sunscreen lotion, so as to improve the skin feel and improve the Quality and performance, the effect of increasing the SPF value

Inactive Publication Date: 2018-06-22
广州市韵丽生物科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is that the e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sunscreen cream and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0095] 1. Example One

[0096] Polydimethylsiloxane PEG-10 / 15 cross-linked polymer, polydimethylsiloxane 3.5 parts,

[0097] 3 parts of polydimethylsiloxane / vinyl polydimethylsiloxane cross-linked polymer / cyclopentadimethylsiloxane,

[0098] 1.5 parts of cetyl PEG / PPG-10 / 1 polydimethylsiloxane,

[0099] 9 parts of cyclopentadimethylsiloxane,

[0100] 5 parts of diphenylsiloxyphenyl trimethylsiloxane,

[0101] 3 copies of SunCat MTA,

[0102] 3 parts of titanium dioxide,

[0103] 1 part of Shark Glycol,

[0104] 0.5 part of phenoxyethanol,

[0105] 70.5 parts of water.

Example Embodiment

[0106] 2. Example two

[0107] Polydimethylsiloxane PEG-10 / 15 cross-linked polymer, polydimethylsiloxane 3 parts,

[0108] 3.5 parts of polydimethylsiloxane / vinyl polydimethylsiloxane cross-linked polymer / cyclopentadimethylsiloxane,

[0109] 1 part of cetyl PEG / PPG-10 / 1 polydimethylsiloxane,

[0110] 10 parts of cyclopentadimethylsiloxane,

[0111] 4 parts of diphenylsiloxyphenyl trimethylsiloxane,

[0112] SunCat MTA 4 copies,

[0113] 2 parts of titanium dioxide,

[0114] 1.5 parts of Shark Glycol,

[0115] 0.3 parts of phenoxyethanol,

[0116] 70.7 parts of water.

Example Embodiment

[0117] 3. Example Three

[0118] Polydimethylsiloxane PEG-10 / 15 cross-linked polymer, polydimethylsiloxane 4 parts,

[0119] 2.5 parts of polydimethylsiloxane / vinyl polydimethylsiloxane cross-linked polymer / cyclopentadimethylsiloxane,

[0120] 2 parts of cetyl PEG / PPG-10 / 1 polydimethylsiloxane,

[0121] 8 parts of cyclopentadimethylsiloxane,

[0122] 6 parts of diphenylsiloxyphenyl trimethicone,

[0123] 2 copies of SunCat MTA,

[0124] 4 parts of titanium dioxide,

[0125] 0.5 part of Shark Glycol,

[0126] 0.7 parts of phenoxyethanol,

[0127] 70.3 parts of water.

[0128] 4. Example Four

[0129] Polydimethylsiloxane PEG-10 / 15 cross-linked polymer, polydimethylsiloxane 3 parts,

[0130] 3 parts of polydimethylsiloxane / vinyl polydimethylsiloxane cross-linked polymer / cyclopentadimethylsiloxane,

[0131] 1 part of cetyl PEG / PPG-10 / 1 polydimethylsiloxane,

[0132] 8.2 parts of cyclopentasiloxane,

[0133] 4 parts of diphenylsiloxyphenyl trimethylsiloxane,

[0134] SunCat MTA 4 copies,

[0135] 2 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses sunscreen cream and a preparation method thereof. The sunscreen cream is prepared from the following raw materials in parts by weight: a polydimethylsiloxane PEG-10/15 cross-linked polymer, 3-4 parts of polydimethylsiloxane, 2.5-3.5 parts of polydimethylsiloxane/vinyl polydimethylsiloxane cross-linked polymer/decamethylcyclopentasiloxane, 1-2 parts of cetyl PEG/PPG-10/1 polydimethylsiloxane, 8-10 parts of decamethylcyclopentasiloxane, 4-6 parts of diphenylsiloxy phenyl trimethicone, 2-4 parts of SunCat MTA, 2-4 parts of titanium dioxide, 0.5-1.5 parts of shark glycol, 0.3-0.7 part of phenoxyethanol and 68-73 parts of water. SunCat MTA is matched with titanium dioxide, so that a higher SPF value can be achieved with fewer sunscreen ingredients and lower concentrations, the addition amount of the traditional sunscreen agent is reduced, and the processing cost is reduced; shark glycol is used for inhibiting skin inflammation caused by ultraviolet light, the chemical sunscreen agent is wrapped in a double-layer phospholipid film for shark glycol, and the skin feeling of the sunscreen cream is greatly improved.

Description

technical field [0001] The invention relates to skin care and sunscreen, in particular to a sunscreen and a preparation method thereof. Background technique [0002] Ultraviolet rays in the sun are the first killer of the skin. Ultraviolet rays can not only tan the skin, but also sunburn the skin, accelerate skin aging, and produce wrinkles. People, especially women, have taken sun protection as an important prerequisite for skin care. Today's sunscreen products come in a variety of varieties, with different SPF values, and with different skin feel. Many of these sunscreens or lotions contain chemical ingredients that are very easy to irritate the skin and cause a tingling sensation after sweating, and it is easy to cause skin sensitivity, redness, itching or tingling when removing makeup. [0003] Therefore, the "sunscreen containing liposome components of pearl hydrolyzed liquid" provided by Chinese patent CN101278894B uses liposomes to wrap pearl aqueous solution to redu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/40A61K8/35A61K8/37A61K8/29A61K8/14A61Q17/04A61Q19/00
CPCA61K8/14A61K8/29A61K8/345A61K8/35A61K8/37A61K8/40A61Q17/04A61Q19/004
Inventor 张应贤
Owner 广州市韵丽生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap