High-toughness mobile phone charger shell

A mobile phone charger, high toughness technology, applied in the field of chargers, can solve the problems of high cost and poor toughness, and achieve the effect of large cross-linking degree, high pressure bearing capacity, and good packing tolerance

Inactive Publication Date: 2018-06-29
天长市优信电器设备有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of science and technology, mobile phones have become universal, and mobile phones are becoming more and more intelligent, and the more functions of mobile phones, the faster the power consumption, so mobile phones will often use mobile phone chargers to charge, and now mobile phone chargers are charged through charging data lines. The USB port is movably plugged on the charger shell. Due to the technical problems of poor toughness and high cost, the current charger shell has become a short board for the development of the charger shell.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness mobile phone charger shell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A high-toughness mobile phone charger shell, its raw materials include: polychlorotrifluoroethylene 30g, acrylonitrile-butadiene-styrene copolymer 18g, EPDM rubber 5g, glass fiber 8g, carbon nanotubes 2g, hard Quality pottery clay 5g, expanded perlite 2g, dibenzoyl peroxide 2g, oxidized polyethylene wax 1g, yttrium oxide 0.2g, cerium oxide 0.2g, antioxidant CA 1.5g, antioxidant BHT 0.2g.

Embodiment 2

[0014] A kind of high-toughness mobile phone charger casing, its raw material comprises: polychlorotrifluoroethylene 50g, acrylonitrile-butadiene-styrene copolymer 10g, EPDM rubber 15g, glass fiber 2g, carbon nanotube 6g, hard Quality pottery clay 1g, expanded perlite 8g, dibenzoyl peroxide 1g, oxidized polyethylene wax 2g, yttrium oxide 0.1g, cerium oxide 0.8g, antioxidant CA 0.5g, antioxidant BHT 1g.

Embodiment 3

[0016] A high-toughness mobile phone charger shell, its raw materials include: polychlorotrifluoroethylene 35g, acrylonitrile-butadiene-styrene copolymer 16g, EPDM rubber 8g, glass fiber 6g, carbon nanotube 3g, hard 4g clay, 4g expanded perlite, 1.8g dibenzoyl peroxide, 1.3g oxidized polyethylene wax, 0.18g yttrium oxide, 0.4g cerium oxide, 1.2g antioxidant CA, 0.4g antioxidant BHT.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-toughness mobile phone charger shell which is prepared from the following raw materials in parts by weight: 30-50 parts of polytrifluorochloroethylene, 10-18 parts of acrylonitrile-butadiene-styrene copolymer, 5-15 parts of ethylene propylene diene monomer, 2-8 parts of glass fiber, 2-6 parts of carbon nano tubes, 1-5 parts of hard clay, 2-8 parts of expanded perlite, 1-2 parts of dibenzoyl peroxide, 1-2 parts of oxidized polyethylene wax, 0.1-0.2 part of yttrium oxide, 0.2-0.8 part of cerium oxide, 0.5-1.5 parts of antioxidant CA and 0.2-1 part of antioxidant BHT. The high-toughness mobile phone charger shell disclosed by the invention is good in toughness, is not easy to bend when falling off or being impacted, is very high in pressure-bearing capability, and is very excellent in heat resistance and ageing resistance.

Description

technical field [0001] The invention relates to the technical field of chargers, in particular to a high-toughness mobile phone charger shell. Background technique [0002] With the development of science and technology, mobile phones have become universal, and mobile phones are becoming more and more intelligent, and the more functions of mobile phones, the faster the power consumption, so mobile phones will often use mobile phone chargers to charge, and now mobile phone chargers are charged through charging data lines. The USB port is movably plugged on the charger shell. Due to the technical problems of poor toughness and high cost, the current charger shell has become a short board for the development of the charger shell. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a high-toughness mobile phone charger shell, which is low in cost and good in toughness. Excellent aging resista...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/12C08L55/02C08L23/16C08L23/30C08K13/04C08K5/14C08K3/22C08K7/14C08K7/24C08K3/34C08K7/26
Inventor 董有朋
Owner 天长市优信电器设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com