Magnetic-powder healthcare vamp and manufacturing method thereof

A production method and magnetic powder technology, applied in magnetic therapy, footwear, shoe uppers, etc., can solve the problems of small holes on the surface of the color paste layer, easy to produce defective products, and unevenness, so as to achieve the goal of not falling off easily, activating cell metabolism, The effect of improving disease resistance

Inactive Publication Date: 2018-08-28
泉州冠拓鞋材有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The pattern of this method can have a three-dimensional effect, but there will be small holes and unevenness on the surface of the foamed color paste layer after foaming, which is easy to produce defective products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The manufacturing method of the above-mentioned magnetic powder health-care vamp: comprises the following steps:

[0022] 1) Cut the base fabric layer into the shape of the shoe upper;

[0023] 2) Stir the PU resin and the magnetic powder evenly at a ratio of 10:100 to obtain a surface layer mixture of the magnetic powder and the PU resin;

[0024] 3) Print a layer of PU resin layer on the base fabric layer having the shape of the shoe upper;

[0025] 4) Send the PU resin layer into an oven for baking until the surface layer is dry, and leave the oven; the temperature of the oven is 40°C, and it is dried for 8 minutes.

[0026] 5) Print the surface mixture obtained in the above step 2) on top of the surface-dried PU resin layer to obtain a magnetic powder PU resin layer; print a magnetic powder PU resin layer on the surface-dried PU resin layer to make the two layers firmly bonded , it is not easy to produce the effect of delamination, if the drying is too much, the c...

Embodiment 2

[0030] 1) Cut the base fabric layer into the shape of the shoe upper;

[0031] 2) Stir the PU resin and the magnetic powder evenly at a ratio of 8:105 to obtain a surface layer mixture of the magnetic powder and the PU resin;

[0032] 3) Print a layer of PU resin layer on the base fabric layer having the shape of the shoe upper;

[0033] 4) Send the PU resin layer into an oven for baking until the surface layer is dry, and leave the oven; the temperature of the oven is 30°C, and it is dried for 10 minutes.

[0034] 5) Print the surface mixture obtained in the above step 2) on top of the surface-dried PU resin layer to obtain a magnetic powder PU resin layer; print a magnetic powder PU resin layer on the surface-dried PU resin layer to make the two layers firmly bonded , it is not easy to produce the effect of delamination, if the drying is too much, the combination between the two is not good.

[0035] 6) When the magnetic powder resin layer is dried to 3 to 40% dry, that is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a magnetic-powder healthcare vamp which is good in three-dimensional effect, has a healthcare and physical therapy effect and is flat and bright in surface and a manufacturingmethod thereof. The manufacturing method includes the steps of firstly, cutting a base cloth layer; secondly, manufacturing a magnetic powder-PU resin surface layer mixed material; thirdly, printing aPU resin layer on the base cloth layer with a vamp shape; fourthly, baking the PU resin layer in a drying oven until the surface layer is dried, and taking the dried PU resin layer out of the dryingoven; fifthly, printing the surface layer mixed material obtained in the second step at the top of the surface-layer-dried PU resin layer to obtain a magnetic power-PU resin layer; sixthly, drying themagnetic power-PU resin layer until 30-40% of the magnetic power-PU resin layer is dried, that is to say, the PU resin layer is in a contraction state, placing a magnetic die above the magnetic power-PU resin layer to attract magnetic powder in the magnetic power-PU resin layer to the surface of the magnetic power-PU resin layer to allow the magnetic powder to be irregularly presented on the surface of the magnetic power-PU resin layer.

Description

technical field [0001] The invention relates to a daily necessities, in particular to a magnetic powder health-care vamp and a manufacturing method thereof. Background technique [0002] In the traditional shoemaking industry, ink printing technology is usually used on the upper of sports shoes. The pattern printed by ink is a flat pattern, which does not have support and protection functions, but can only be used for decoration, and the pattern does not have a three-dimensional effect. [0003] There are two main methods for processing the three-dimensional patterns on the upper of the shoe: one is pasting by hot-melt, and pasting the three-dimensional pattern of the upper on the upper layer of the shoe after hot-melting or by sewing Sewing the prepared pattern on the shoe upper layer cloth, this method has complicated manufacturing process, low production efficiency and affects the aesthetic feeling of the entire shoe upper appearance. [0004] The other is to print the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A43B23/02A43B1/00B29D35/12C08L75/04A61N2/08
CPCA43B1/0054A43B23/0205A61N2/06B29D35/126C08L75/04
Inventor 饶蓉饶尚阳戴积长
Owner 泉州冠拓鞋材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com