A kind of in-situ supported foam microporous noble metal catalyst and preparation method thereof

A noble metal catalyst, supported technology, applied in the direction of metal/metal oxide/metal hydroxide catalyst, chemical instrument and method, physical/chemical process catalyst, etc., can solve the problems of restricting wide application, loading, no dispersibility, etc. , to reduce costs

Active Publication Date: 2021-09-21
嘉兴长维新材料科技有限公司 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, since the microstructure of the foam microporous noble metal catalyst is in the shape of three-dimensional "bridged" foam micropores, and generally exists in the form of strips or blocks, there is no good dispersibility, so it is difficult to obtain a catalyst similar to that of noble metal nanoparticles. The method used is loaded on the above carrier
In addition, since bulk or strip-shaped foamed microporous noble metal catalyst materials are generally brittle, it is difficult to process them into specific physical shapes and better mechanical structure stability without a carrier according to the needs of practical applications. catalyst material, thus greatly limiting its further wide application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of in-situ supported foam microporous noble metal catalyst and preparation method thereof
  • A kind of in-situ supported foam microporous noble metal catalyst and preparation method thereof
  • A kind of in-situ supported foam microporous noble metal catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example

[0051] This embodiment provides an example of preparing a foam microporous nickel-platinum catalyst supported in situ, and the preparation method includes the following steps:

[0052] (1) The molecular formula of the selected formula is Zr 45 Ti 15 Ni 22 Pt 8 al 10 According to the formula, the raw materials are weighed, and the alloy melt is obtained after melting. The alloy melt is prepared by the crucible melt drawing method with a diameter of 120 μm and a length of about 50 m. The amorphous phase content is 95% Zr 45 Ti 15 Ni 22 Pt 8 al 10 alloy wire, and further weave the alloy wire into a mesh.

[0053] (2) at room temperature, clip 0.25 gram of Zr prepared in step (1) 45 Ti 15 Ni 22 Pt 8 al 10 Alloy wire mesh, which is submerged in 1L hydrofluoric acid aqueous solution with a concentration of 0.015mol / L for dealloying reaction. During the reaction, Zr, Ti, Al, and most of Ni at the reaction interface will react with hydrofluoric acid and become ions into ...

Embodiment 2

[0059] This embodiment provides an example of preparing a foam microporous gold-platinum alloy catalyst supported in situ, and the preparation method includes the following steps:

[0060] (1) The molecular formula of the selected formula is Zr 55 Ni 24 Au 7 Pt 7 Y 7 According to the formula, the raw materials are weighed, and the alloy melt is obtained after melting, and the alloy melt is prepared by the crucible-type melt drawing method to prepare the Zr 55 Ni 24 Au 7 Pt 7 Y 7 alloy wire, and further weave the alloy wire into a mesh.

[0061] (2) at room temperature, clip 0.3 gram of Zr prepared in step (1) 55 Ni 24 Au 7 Pt 7 Y 7 Alloy wire mesh, which is immersed in 2L of hydrofluoric acid aqueous solution with a concentration of 0.2mol / L for dealloying reaction. During the reaction, Zr, Y, and most of Ni at the reaction interface will react with hydrofluoric acid and become ions into the solution, while the remaining Au, Pt, and a small amount of Ni will form...

Embodiment 3

[0063] Present embodiment provides an example of the foam microporous gold-palladium alloy catalyst that prepares alloy wire (network) support, and this preparation method comprises the steps:

[0064] (1) The molecular formula of the selected formula is Zr 50 co 26 Au 7 PD 7 al 10 According to the formula, the raw materials are weighed, the alloy melt is obtained after melting, and the alloy melt is prepared by the crucible-type melt drawing method to prepare Zr with a diameter of 80 μm and a length of about 100 m. 50 co 26 Au 7 PD 7 al 10 alloy wire.

[0065] (2) at room temperature, clip 0.3 gram of Zr prepared in step (1) 50 co 26 Au 7 PD 7 al 10 Alloy wire, which is immersed in 1L of hydrofluoric acid aqueous solution with a concentration of 0.02mol / L for dealloying reaction. During the reaction, Zr, Al, and most of Co at the reaction interface will react with hydrofluoric acid and become ions into the solution, while the remaining Au, Pd, and a small amount...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
areaaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an in-situ supported foam microporous noble metal catalyst. Taking the amorphous alloy wire (or its weaving) with a cross-sectional area of ​​S0 as the precursor, immersing it in an acid solution, corroding the amorphous alloy at a certain depth below the outer surface of the amorphous alloy wire through a dealloying reaction, thereby obtaining a nanoporous noble metal catalytic layer while retaining a cross-sectional area of ​​S(S

Description

technical field [0001] The invention relates to the technical field of nanometer metal materials, in particular to an in-situ supported foam microporous noble metal catalyst and a preparation method thereof. Background technique [0002] A noble metal catalyst is a noble metal material that can change the rate of a chemical reaction without itself participating in the final product of the reaction. Since the d electron orbitals of noble metal elements are not filled, the surface is easy to adsorb reactants, and the strength is moderate, which is conducive to the formation of intermediate "active compounds", so it has high catalytic activity, and also has high temperature resistance, oxidation resistance, corrosion resistance, etc. Comprehensive excellent properties, is currently the most important catalyst material. [0003] In practical applications, in order to ensure the performance of the catalyst and reduce the amount of noble metal used as much as possible, the most e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/89B01J35/00B01J35/10
CPCB01J23/892B01J23/894B01J23/8946B01J35/0033B01J35/10
Inventor 潘登赵远云付振闯
Owner 嘉兴长维新材料科技有限公司