Bending-resistant pipe material formula

A formula and pipe bending technology, applied in the electrical field, can solve the problems of insufficient toughness and bendability of the threading pipe, and achieve the effect of good toughness and good bendability

Inactive Publication Date: 2018-10-16
NANTONG BOTAI ART PATTERN DESIGN CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The threading pipe is a common tool, mainly used to lay the wires, prevent the softening and leakage of the wires, and protect the wires to a certain extent. The existing threading pipes have insufficient toughness and bendability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0006] A bending-resistant pipe material formula, the raw materials in the formula are composed by weight percentage: PVC65-75%, lead salt stabilizer 11-15%, paraffin wax 11-20%, lubricant 15-25%, stearin Acid 13-19%, light calcium carbonate 15-17%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a bending-resistant pipe material formula. The formula comprises the following raw materials by weight percentage: 65-75% of PVC (polyvinyl chloride), 11-15% of a lead salt stabilizer, 11-20% of paraffin, 15-25% of a lubricant, 13-19% of stearic acid and 15-17% of light calcium carbonate. The bending-resistant pipe material provided by the invention is good in toughness and bending properties.

Description

technical field [0001] The invention relates to a bending-resistant pipe material formula, which belongs to the electrical field. Background technique [0002] The threading pipe is a common tool, which is mainly used to lay the wires, prevent the softening and leakage of the wires, and protect the wires to a certain extent. The existing threading pipes have insufficient toughness and bendability. Contents of the invention [0003] In view of the above-mentioned problems in the prior art, the present invention provides a formulation of a bending-resistant pipe material, which has good toughness and bendability. [0004] In order to achieve the above object, the present invention is achieved through the following technical solutions: a bending-resistant pipe, the raw materials in the formula are composed by weight percentage: PVC65-75%, lead salt stabilizer 11-15%, paraffin wax 11- 20%, lubricant 15-25%, stearic acid 13-19%, light calcium carbonate 15-17%. [0005] Benefi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/06C08K13/02C08K5/09C08K3/26
CPCC08L27/06C08K2003/265C08L2203/18C08L91/06C08K13/02C08K5/09C08K3/26
Inventor 陈霞
Owner NANTONG BOTAI ART PATTERN DESIGN CO LTD