Zirconium dioxide toughened flaky aluminum oxide-based composite ceramic and preparation method thereof

A technology of flake alumina and composite ceramics, which is applied in the field of composite materials, can solve problems such as poor toughness, achieve the effects of increasing the probability of crack bridging, improving fracture toughness and strength, and saving costs

Active Publication Date: 2018-11-02
GUANGDONG UNIV OF TECH
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a zirconia toughened plate-shaped alumina-based composite ceramic and a preparation method thereof, which s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zirconium dioxide toughened flaky aluminum oxide-based composite ceramic and preparation method thereof
  • Zirconium dioxide toughened flaky aluminum oxide-based composite ceramic and preparation method thereof
  • Zirconium dioxide toughened flaky aluminum oxide-based composite ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0056] Example 1

[0057] (1) Take a certain amount of deionized water and place it in a beaker, add Al 2 O 3 Powder and ZrO 2 2% of the powder mass of polyacrylic acid (PAA) and 1% of polyethylene glycol (PEG), place the beaker on a magnetic stirring device and stir at 60-90°C and 150-250 rpm until all are dissolved;

[0058] (2) Slowly add 20-40g Al to the solution obtained in step (1) 2 O 3 Powder and adjust the pH value of the solution to 10~11;

[0059] (3) Place the beaker in the ultrasonic cleaning machine, and use the paddle-type stirring device to stir at the same time, and slowly add 5-10g ZrO during the ultrasonic coordinated stirring process 2 Powder. After adding, continue ultrasonic and coordinated stirring for 30 minutes to prepare ZTA ceramic slurry;

[0060] (4) Put the ZTA slurry of step (3) in a planetary ball milling tank, and use zirconia balls for planetary ball milling for 2 to 4 hours;

[0061] (5) The ZTA slurry after planetary ball milling is dried using a rot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to zirconium dioxide toughened flaky aluminum oxide-based composite ceramic and a preparation method thereof. The invention discloses a preparation method of the zirconium dioxide toughened flaky aluminum oxide-based composite ceramic. The preparation method comprises the following steps: successively adding a first dispersing agent, Al2O3 powder and ZrO2 powder, mixing, adding a second dispersing agent, sintering to obtain the ZrO2 toughened flaky Al2O3-based composite ceramic, wherein the first dispersing agent is prepared from PAA and PEG; and the second dispersing agent is prepared from AMP and PEG. The preparation method is simple in operation, the preparation cost is reduced, Al2O3 crystal grains in a ZTA composite ceramic matrix has the directional growth, hascertain length-to-diameter ratio, and is of a flaky structure; and by adopting the structure, the probability of the crack deflection and crack bridging in the breaking process can be increased, so that on the premise of not influencing the hardness of the ZTA composite ceramics, the breaking toughness and strength of the ZTA composite ceramic can be significantly improved, and the problems that the shape of the existing ZTA composite ceramic matrix Al2O3 is of an isometric morphology and the toughness is poor can be solved.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a zirconium dioxide toughened plate-shaped alumina-based composite ceramic and a preparation method thereof. Background technique [0002] Alumina (Al 2 o 3 )-based ceramic materials have excellent characteristics such as high temperature resistance, high strength, creep resistance, wear resistance, good insulation, light weight, and oxidation resistance. They are ideal structural ceramic materials and are widely used. With the development of technology and the expansion of application fields, the Al 2 o 3 The performance requirements of base ceramic materials are also increasing day by day. [0003] Al 2 o 3 Ceramic, also known as corundum, has a Mohs hardness of 9, which is extremely hard. But since Al 2 o 3 The high brittleness of ceramics limits its application range. In order to overcome this shortcoming and improve the safety and reliability during use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/10C04B35/622C04B35/634
CPCC04B35/10C04B35/622C04B35/63404C04B35/63488C04B2235/3244
Inventor 林东涛孟凡左飞吕健林华泰
Owner GUANGDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap