Coating technology for sculellaria barbata seeds

A technology of Scutellaria barbata and seeds, applied in the direction of seed coating/seed dressing, application, organic fertilizer, etc., can solve the problems that the seed effect of Scutellaria barbata is not so ideal, and the coating agent products of Scutellaria barbata are few, etc. Achieve the effects of increasing production and income significantly, improving seed vigor and germination rate

Inactive Publication Date: 2018-11-23
HEFEI SHENWO HORTICULTURE CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, although there are a large number of coating agent products on the market, there are fewer coating agent products for Scutellaria barbata, so the coating agents of the prior art are not so ideal for the seeds of Scutellaria barbata.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Present embodiment relates to a kind of coating technology of Scutellaria barbata seed, comprises the following steps:

[0040] (1) Seed pretreatment: rubbing the surface of Scutellaria barbata seeds;

[0041] (2) Mix and stir 10 parts by weight of pretreated starch, 0.5 parts by weight of plant growth regulator, 1 part by weight of borax, 13 parts of bentonite and 15 parts of chitosan, and then add 100 parts by weight of pure Stir the water to mix evenly, and then microwave activation treatment to obtain the first mixed slurry:

[0042] (3) Put the first mixed slurry and Scutellaria barbata seeds in a mixer at a mass ratio of 1:60, shake and mix evenly, so that the surface of Scutellaria barbata seeds is evenly coated with a layer of the first mixed slurry;

[0043] (4) Stir and mix 13 parts by weight of rice wheat stone, 4 parts by weight of negative ion powder, 20 parts by weight of polylactic acid, 0.3 parts by weight of copper sulfate, 0.1 parts by weight of silve...

Embodiment 2

[0056] Present embodiment relates to a kind of coating technology of Scutellaria barbata seed, comprises the following steps:

[0057] (1) Seed pretreatment: rubbing the surface of Scutellaria barbata seeds;

[0058] (2) Mix and stir 20 parts by weight of pretreated starch, 0.9 parts by weight of plant growth regulator, 2 parts by weight of borax, 19 parts by weight of bentonite and 30 parts of chitosan, and then add 100 parts by weight of pure Stir the water to mix evenly, and then microwave activation treatment to obtain the first mixed slurry:

[0059] (3) Put the first mixed slurry and Scutellaria barbata seeds together in a mixer at a mass ratio of 1:90, shake and mix evenly, so that the surface of Scutellaria barbata seeds is evenly coated with a layer of the first mixed slurry;

[0060] (4) Stir and mix 26 parts by weight of rice wheat stone, 9 parts by weight of negative ion powder, 30 parts by weight of polylactic acid, 0.9 parts by weight of copper sulfate, 0.5 part...

Embodiment 3

[0073] Present embodiment relates to a kind of coating technology of Scutellaria barbata seed, comprises the following steps:

[0074] (1) Seed pretreatment: rubbing the surface of Scutellaria barbata seeds;

[0075] (2) Mix 15 parts by weight of pretreated starch, 0.7 parts by weight of plant growth regulator, 1.5 parts by weight of borax, 16 parts by weight of bentonite and 23 parts of chitosan, and then add 100 parts by weight of pure Stir the water to mix evenly, and then microwave activation treatment to obtain the first mixed slurry:

[0076] (3) Put the first mixed slurry and Scutellaria barbata seeds in a mixer at a mass ratio of 1:75, shake and mix evenly, so that the surface of the Scutellaria barbata seeds is evenly coated with a layer of the first mixed slurry;

[0077] (4) Stir and mix 15 parts by weight of rice wheat stone, 7 parts by weight of negative ion powder, 28 parts by weight of polylactic acid, 0.6 parts by weight of copper sulfate, 0.3 parts by weight ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a coating technology for sculellaria barbata seeds. The coating technology comprises the following steps: firstly, pretreating seeds; secondly, uniformly mixing and stirring pretreated starch, a plant growth regulator, borax, bentonite and chitosan, adding pure water for uniform stirring and mixing and then carrying out microwave activation treatment to obtain first mixed slurry; thirdly, mixing the first mixed slurry with the sculellaria barbata seeds; fourthly, mixing and stirring medical stone, tourmaline, polylactic acid copper sulfate, silver nitrate and azadirachtin emulsion, and adding the pure water and cassava flour to obtain second mixed slurry; fifthly, putting seeds in a seed granulator, and adding the second mixed slurry for shaking until all seeds arecovered with the second mixed slurry; sixthly, uniformly spraying warning coloration on the surfaces of the seeds; seventhly, drying and curing the seeds. The germination rate of the sculellaria barbata seeds prepared by the coating technology for the sculellaria barbata seeds, disclosed by the invention, is obviously improved and the disease resistance is increased.

Description

technical field [0001] The invention belongs to the technical field of Scutellaria barbata cultivation, and in particular relates to a coating process of Scutellaria barbata seeds. Background technique [0002] Scutellaria barbata, aliases: Mountain whip (Chengdu, Sichuan), Scutellaria baicalensis (Puge, Sichuan), Tooth brush grass (Suzhou, Jiangsu), Tianji grass (Yixing, Jiangsu), Scutellaria baicalensis (Nanjing, Jiangsu), Hanxin grass (Guangzhou Flora). It is a perennial herbaceous plant of the genus Scutellaria baicalensis in the Lamiaceae family. The height of half-branch lotus can reach 55 cm. It is densely clustered, with colorful flowers and a long flowering period. It is an excellent flower for decorating grasslands, slopes and roadsides. It is also suitable for planting on the edge of flower beds and flower borders. The potted plants are small and exquisite and can be displayed on the balcony. , window sills, corridors, in front of doors, poolsides and courtyards...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A01C1/06C05G3/00
CPCA01C1/06C05C5/00C05D9/00C05G5/20C05D9/02C05F11/00C05F11/10C05G3/00
Inventor 汪中奇
Owner HEFEI SHENWO HORTICULTURE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com