Stainless steel plant-based water-soluble stamping oil and preparation method thereof

A plant-based, water-soluble technology, applied in the petroleum industry, lubricating compositions, etc., can solve the problems of difficult cleaning of workpieces, difficult removal, oil oxidation, etc., and achieve high production efficiency, easy cleaning, and extended service life.

Inactive Publication Date: 2018-11-23
东莞市伟思化学科技有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is difficult to clean the workpiece after stamping, especially for some heavy-duty stretching. The surface of the workpiece is oxidized due to high temperature, and even the compatible hydrocarbon cleaning agent is not easy to remove

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel plant-based water-soluble stamping oil and preparation method thereof
  • Stainless steel plant-based water-soluble stamping oil and preparation method thereof
  • Stainless steel plant-based water-soluble stamping oil and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The stainless steel plant-based water-soluble stamping oil of the present invention comprises the following components in percentage by weight:

[0030]

[0031] Wherein, the plant modified synthetic ester is sunflower oil modified synthetic ester, the vegetable oil acid agent is oleic acid, the antirust additive is undecane dibasic acid amine salt, and the chlorinated additive is medium-long chain Chlorinated paraffin, the phosphating additive is fatty alcohol ethoxylated phosphate ester, the vulcanization additive is sulfurized olefin, the emulsifier is dimer acid, the alkali is sodium hydroxide, and the coupling agent is di Ethylene glycol monobutyl ether, the water is distilled water.

[0032] The preparation method of above-mentioned stainless steel plant-based water-soluble stamping oil, comprises the following steps:

[0033] S1. Weigh the plant-modified synthetic esters specified in the above formula and add them to the constant temperature stirrer, then add...

Embodiment 2

[0036] The stainless steel plant-based water-soluble stamping oil of the present invention comprises the following components in percentage by weight:

[0037]

[0038] Specifically, the plant-modified synthetic ester is ricinoleic acid ester, the vegetable oil acid agent is tall oil acid, the anti-rust additive is dodecyl dibasic acid amine salt, and the chlorinated additive is chlorinated Fatty acid, the phosphating additive is isobutyl-sec-butyl phosphate, the vulcanization additive is sulfurized fatty acid, the emulsifier is fatty alcohol polyoxyethylene ether, the alkali is sodium hydroxide, and the coupling agent is tripropylene glycol Methyl ether, and the water is deionized water.

[0039] The preparation method of above-mentioned stainless steel plant-based water-soluble stamping oil, comprises the following steps:

[0040] S1. Weigh the plant-modified synthetic ester in the amount specified in the above formula and add it to the constant temperature stirrer, then...

Embodiment 3

[0043] The stainless steel plant-based water-soluble stamping oil of the present invention comprises the following components in percentage by weight:

[0044]

[0045] Specifically, the plant-modified synthetic ester is self-emulsifying ester, the vegetable oil acid agent is ricinoleic acid, the anti-rust additive is sebacic acid amine salt, and the chlorinated additive is medium-long chain chlorinated paraffin, The phosphating additive is fatty alcohol ethoxylated phosphate, the vulcanization additive is vulcanized fat, the emulsifier is Tween 80, the alkali is triethanolamine, and the coupling agent is carbon 16 fatty alcohol. Said water is deionized water.

[0046] The preparation method of above-mentioned stainless steel plant-based water-soluble stamping oil, comprises the following steps:

[0047] S1. Weigh the plant-modified synthetic ester in the amount specified in the above formula and add it to the constant temperature stirrer, then add the vegetable oleic acid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Kinematic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a stainless steel plant-based water-soluble stamping oil, which is prepared from the components in percentage by weight: 20 to 40 percent of plant modified synthetic ester, 5 to 10 percent of vegetable oleic acid, 10 to 20 parts of a rust-inhabiting additive, 15 to 25 percent of a chlorinated additive, 1 to 3 percent of a phosphating additive, 5 to 15 percent of a vulcanizing additive, 5 to 20 percent of an emulsifier, 5 to 20 percent of alkali, 5 to 10 percent of a coupling agent and 8 to 20 percent of water. A formula is blended through a specific process, can form semitransparent diluent with water; a part of materials of the formula adopts reproducible raw materials which is high in biodegradation rate, so that the dependence of the petrifaction material and theinfluence of the petrifaction material on the environment is reduced; due to the product is water-soluable, a work piece after processing is easy to clean by a water-based cleaning agent, so that theservice life of the water-based cleaning agent can be prolonged, the time for cleaning is reduced, the cost of follow-up cleaning is effectively reduced; a stock solution is used, or water can be added to use, so that the good market prospect can be realized. According to the stainless steel plant-based water-soluble stamping oil, the preparation method is simple, the operation is easy, the production efficiency is high and the percent of pass of the product is high.

Description

technical field [0001] The invention relates to the technical field of stamping oil formulations and preparation methods, in particular to a stainless steel plant-based water-soluble stamping oil and a preparation method thereof. Background technique [0002] At present, the stainless steel stamping oils on the market are mainly oily products, and the main components include mineral oil, animal and vegetable oil, polyisobutylene thickener, chlorinated paraffin, phosphating additives, vulcanization additives, etc., according to the thickness of the stainless steel material, degree of deformation, According to conditions such as stamping and drawing depth, a suitable product can be formulated. Most of these products are based on mineral oil, which is a non-renewable resource. It is difficult to clean the workpiece after stamping, especially for some heavy-duty stretching. The surface of the workpiece is oxidized due to high temperature, and even the compatible hydrocarbon cle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M169/04C10M173/00C10N40/24C10N30/12C10N30/04
CPCC10M169/044C10M173/00C10N2030/04C10N2030/12C10N2040/24C10N2040/245C10N2040/247
Inventor 何国锐莫建强
Owner 东莞市伟思化学科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com