Imitation discharge printing process based on glue coating

A mucilage and coating technology, which is applied in dyeing, textiles and papermaking, can solve the problems of large dye color changes, high dye cost, and difficult production, and achieve low fluidity, simple process flow, and low scrap rate. Effect

Inactive Publication Date: 2018-12-28
ZHEJIANG MIZUDA TEXTILE PRINTING & DYEING TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the velvet fabric is printed and dyed by the existing traditional engraving process, because the cost of the dye is high, and the color of the dye changes greatly, it is difficult to control, resulting in the production of engraving and printing on the velvet fabric. rate is not high
Therefore, existing technology exists the problem that production difficulty is big and cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1. The imitation engraving process based on glue coating comprises the following steps:

[0023] In the first step, the gray cloth is treated with resin padding to obtain A cloth;

[0024] In the second step, fabric A is flattened and dried to obtain fabric B;

[0025] The third step is to apply glue to the B cloth to obtain the C cloth;

[0026] The fourth step is to pre-dry the cloth C to obtain the cloth D;

[0027] The fifth step is to dry the D cloth to obtain the E cloth;

[0028] The sixth step is to finish finishing the E fabric to obtain the finished fabric.

[0029] The specific process of resin padding in the first step is as follows: firstly soak the gray cloth in the resin solution to obtain cloth a; then squeeze cloth a to obtain cloth A; the soaking time of the gray cloth is 3-5 seconds, The impregnation temperature is 20-30°C.

[0030] The resin solution includes a resin and a crosslinking agent.

[0031] The concentration of resin is 50-1...

Embodiment 2

[0042] Example 2. The imitation engraving process based on glue coating comprises the following steps:

[0043] In the first step, the gray cloth is treated with resin padding to obtain A cloth;

[0044] In the second step, fabric A is flattened and dried to obtain fabric B;

[0045] The third step is to apply glue to the B cloth to obtain the C cloth;

[0046] The fourth step is to pre-dry the cloth C to obtain the cloth D;

[0047] The fifth step is to dry the D cloth to obtain the E cloth;

[0048] The sixth step is to finish finishing the E fabric to obtain the finished fabric.

[0049] The specific process of resin padding in the first step is as follows: firstly dip the gray cloth in the resin solution to obtain cloth a; then squeeze cloth a to obtain cloth A; the dipping time of the gray cloth is 3 seconds, and the dipping temperature is 20°C.

[0050] The resin solution includes a resin and a crosslinking agent.

[0051] The concentration of the resin was 50 g / L...

Embodiment 3

[0062] Example 3. The imitation engraving process based on glue coating comprises the following steps:

[0063] In the first step, the gray cloth is treated with resin padding to obtain A cloth;

[0064] In the second step, fabric A is flattened and dried to obtain fabric B;

[0065] The third step is to apply glue to the B cloth to obtain the C cloth;

[0066] The fourth step is to pre-dry the cloth C to obtain the cloth D;

[0067] The fifth step is to dry the D cloth to obtain the E cloth;

[0068] The sixth step is to finish finishing the E fabric to obtain the finished fabric.

[0069]The specific process of resin padding in the first step is as follows: firstly dip the gray cloth in the resin solution to obtain cloth a; then squeeze cloth a to obtain cloth A; the dipping time of the gray cloth is 4 seconds, and the dipping temperature is 25°C.

[0070] The resin solution includes a resin and a crosslinking agent.

[0071] The concentration of the resin was 100 g / L...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses an imitation discharge printing process based on a glue coating. The process includes the following steps: the first step of carrying out resin padding treatment on grey clothto obtain a fabric A; the second step of flattening and drying the fabric A to obtain a fabric B; the third step of applying glue to the fabric B to obtain a fabric C; the fourth step of pre-drying the fabric C to obtain a fabric D; the fifth step of drying the fabric D to obtain a fabric E; the sixth step of finishing the fabric E to obtain a finished fabric. The process has the advantages of being able to reduce production difficulty and reduce production cost.

Description

technical field [0001] The invention relates to an engraving process, in particular to an imitation engraving process based on glue coating. Background technique [0002] Engraving and printing technology is the technology of printing on the cloth that has been dyed in advance and can be pulled out. The effect of imitating three-dimensional patterns is good, and it is welcomed by the market. However, when the velvet fabric is printed and dyed by the existing traditional engraving process, because the cost of the dye is high, and the color of the dye changes greatly, it is difficult to control, resulting in the production of engraving and printing on the velvet fabric. The rate is not high. Therefore, the existing technology has the problems of high production difficulty and high cost. Contents of the invention [0003] The object of the present invention is to provide an imitation engraving process based on glue coating. The invention has the characteristics of reducing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/52D06P5/00
CPCD06P1/52D06P5/00
Inventor 杨雪峰
Owner ZHEJIANG MIZUDA TEXTILE PRINTING & DYEING TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com