3D printing photosensitive resin for jewelry casting and preparation method thereof

A 3D printing and photosensitive resin technology, which is applied in the field of 3D printing materials, can solve the problems of jewelry castings such as rough surface, long-time grinding, and low printing molding rate, so as to achieve good structural precision, reduce processing costs, and ash residue little effect

Active Publication Date: 2021-06-15
惠州市大亚湾华鑫新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the 3D printing photosensitive resin used for jewelry casting on the market currently has a low printing rate and low printing accuracy. It takes a long time to polish, which reduces the processing efficiency and increases the processing cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A 3D printing photosensitive resin for jewelry casting, each component and weight percentage are as follows:

[0026] Polyether acrylate resin 41.8%;

[0027] Polyether monomer 50%;

[0028] Photoinitiator 3%;

[0029] UV absorber 5%;

[0030] Dye 0.15%;

[0031] Inhibitor 0.05%.

[0032] Among them, the polyether acrylate resin is a mixture of polyethoxylated acrylate resin with a degree of polymerization of 10 and polypropoxylated acrylate resin with a degree of polymerization of 30 in a ratio of 1:1; the polyether monomer is ethylene glycol Dimethacrylate and diethylene glycol dimethacrylate are mixed at a ratio of 1:2; the photoinitiator is phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide; UV absorption The agent is 2-hydroxy-4-methoxybenzophenone; the dye is a metal complex dye; the polymerization inhibitor is p-hydroxyanisole.

[0033]The 3D printing photosensitive resin used for jewelry casting is prepared according to the following preparation method:

[...

Embodiment 2

[0036] A 3D printing photosensitive resin for jewelry casting, each component and weight percentage are as follows:

[0037] Polyether acrylate resin 40%;

[0038] Polyether monomer 50%;

[0039] Photoinitiator 6%;

[0040] UV absorber 3.72%;

[0041] Dye 0.08%;

[0042] Inhibitor 0.2%.

[0043] Among them, the polyether acrylate resin is a mixture of ethoxylated polypropoxylated acrylate resin with a degree of polymerization of 20 and propoxylated polyethoxylated acrylate resin with a degree of polymerization of 20 in a ratio of 1:1; the polyether monomer It is made by mixing triethylene glycol dimethacrylate and polyethylene glycol (200) dimethacrylate at a ratio of 1:1; the photoinitiator is 2,4,6-trimethylbenzoyl-dimethacrylate Phenylphosphine oxide; UV absorber is 2-hydroxy-4-n-octyloxybenzophenone; dye is acid dye; polymerization inhibitor is 2,6-di-tert-butyl-p-cresol.

[0044] The 3D printing photosensitive resin used for jewelry casting is prepared according to ...

Embodiment 3

[0047] A 3D printing photosensitive resin for jewelry casting, each component and weight percentage are as follows:

[0048] Polyether acrylate resin 60%;

[0049] Polyether monomer 35.4%;

[0050] Photoinitiator 4%;

[0051] UV absorber 0.5%;

[0052] Dye 0.02%;

[0053] Inhibitor 0.08%.

[0054] The polyether acrylate resin is a polybutoxylated acrylate resin with a degree of polymerization of 30; the polyether monomers are polyethylene glycol (400) dimethacrylate and polyethylene glycol (600) dimethyl Acrylic esters are mixed at a ratio of 1:2; the photoinitiator is 2,4,6-trimethylbenzoylphenylphosphonic acid ethyl ester; the UV absorber is 2-hydroxy-4-n-octyloxydiphenyl Ketone; the dye is an acid dye; the polymerization inhibitor is p-hydroxyanisole.

[0055] The 3D printing photosensitive resin used for jewelry casting is prepared according to the following preparation method:

[0056] Add polyether acrylate resin, polyether monomer, photoinitiator, ultraviolet abs...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a 3D printing photosensitive resin for jewelry casting. The components and weight percentages are as follows: polyether acrylate resin 40%-60%; polyether monomer 30%-50%; photoinitiator 3% to 6%; UV absorber 0.5% to 5%; dye 0.02% to 0.15%; Initiator, ultraviolet absorber, dye and polymerization inhibitor are added into the reaction kettle according to the proportion of the formula, and stirred at a constant temperature of 70 ° C to 80 ° C for 0.5 to 1 hour. After the components are completely dissolved, they can be discharged and filled to obtain the finished product. The 3D printing photosensitive resin for jewelry casting of the present invention has the advantages of fully combustible performance, less residual ash, good jewelry casting effect, reduced polishing time, improved processing efficiency, and reduced processing cost.

Description

technical field [0001] The invention relates to a 3D printing material, in particular to a 3D printing photosensitive resin for jewelry casting. Background technique [0002] 3D printing technology is also called "additive manufacturing technology", which is a technology based on the principle of discrete and accumulation to realize manufacturing through the gradual accumulation of materials. In 3D printing, the computer divides the 3D model of the formed part into slices of a certain thickness, and finally superimposes to form a three-dimensional solid part. This manufacturing technology can realize the manufacture of complex structures that are difficult to process by traditional techniques without traditional tools or models, effectively simplifying the production process and shortening the production cycle. [0003] Light-curing 3D printing technology has the common advantages of shortening the product development cycle, reducing production costs, and realizing personal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F265/06C08F222/14C08F222/20C08F2/48A44C27/00
CPCA44C27/001C08F2/48C08F265/06C08F222/102
Inventor 李文瑜孟令宾黄必威
Owner 惠州市大亚湾华鑫新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap