Preparation method of antifogging glass
An anti-fog and glass technology, which is applied in the field of preparation of anti-fog glass, can solve the problems of glass surface influence, anti-fog time is not long, etc., and achieve good anti-fog performance and good anti-fog effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0016] A preparation method of anti-fogging glass, comprising the following preparation steps:
[0017] Step 1, put 80 parts by weight of glass powder, 3 parts of nano-alumina, 2 parts of titanium oxide, 1 part of calcium carbonate and 1 part of magnesium boride into a tempering furnace, heat and keep it for 120 minutes, and then pass through the mold Prepared into a glass gob, the heating temperature is 1400°C;
[0018] Step 2, cooling the glass gob to 180°C, and treating the surface with steam for 5 minutes to obtain a steam-treated glass gob, wherein the cooling rate in the process of cooling to 180°C is 2-3°C / min;
[0019] Step 3: Cool down the steam-treated glass gob to 78°C, spray absolute ethanol on the surface in the form of spray, then cool down to room temperature, and wash with deionized water to obtain anti-fogging glass, in which the surface is steam-treated To spray steam onto the glass surface and ensure that the entire surface is evenly steamed.
Embodiment 2
[0021] A preparation method of anti-fogging glass, comprising the following preparation steps:
[0022] Step 1, put 86 parts of glass powder in parts by weight, 4 parts of nano-alumina, 2 parts of titanium oxide, 1 part of calcium carbonate and 1 part of magnesium boride into a tempering furnace, heat and keep it for 130 minutes, and then pass through the mold Prepared into a glass gob, the heating temperature is 1430°C;
[0023] Step 2, cooling the glass gob to 185°C, and treating the surface with steam for 6 minutes to obtain a steam-treated glass gob, wherein the cooling rate is 2-3°C / min during the process of cooling down to 185°C;
[0024] Step 3: Cool down the steam-treated glass gob to 78°C, spray absolute ethanol on the surface in the form of spray, then cool down to room temperature, and wash with deionized water to obtain anti-fogging glass, in which the surface is steam-treated To spray steam onto the glass surface and ensure that the entire surface is evenly steam...
Embodiment 3
[0026] A preparation method of anti-fogging glass, comprising the following preparation steps:
[0027] Step 1, put 90 parts by weight of glass powder, 6 parts of nano-alumina, 3 parts of titanium oxide, 2 parts of calcium carbonate and 2 parts of magnesium boride into a tempering furnace, heat and keep it for 140 minutes, and then pass through the mold Prepared into a glass gob, the heating temperature is 1480°C;
[0028] Step 2, cooling the glass gob to 195°C, and treating the surface with steam for 7 minutes to obtain a steam-treated glass gob, wherein the cooling rate is 2-3°C / min during the process of cooling down to 195°C;
[0029] Step 3: Cool down the steam-treated glass gob to 79°C, spray absolute ethanol on the surface in the form of spray, then cool down to room temperature, and wash with deionized water to obtain anti-fogging glass, in which the surface is treated with steam To spray steam onto the glass surface and ensure that the entire surface is evenly steamed...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology