A kind of method for preparing spinnable pitch from coal tar

A technology of coal tar and pitch, which is applied in the field of preparing spinnable pitch, can solve the problems of high molecular weight and low content, and achieve the effects of high raw material utilization rate, simple preparation process, and narrow molecular weight distribution range

Active Publication Date: 2021-02-23
SHANXI INST OF COAL CHEM CHINESE ACAD OF SCI
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantage is that the content of asphaltenes in asphaltenes is relatively low, accounting for only about 30%
The structure of pre-asphaltenes is similar to that of asphaltenes, and its content in asphaltenes reaches about 70%, but its molecular weight is relatively large, and it is easy to undergo excessive polymerization during direct thermal condensation polymerization to form secondary quinoline insolubles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing spinnable pitch from coal tar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Step 1. Put coal tar in a reaction kettle with a mass of 1500 grams, heat it to 250° C. and distill it under reduced pressure for 2 hours (vacuum degree is 0.08 MPa), and take out the remaining material from the autoclave, which is the heavy component of coal tar. It is 825g.

[0033] Step 2. Add 50g of coal tar heavy fraction and 100g of n-heptane into the Soxhlet extractor, heat to 80°C, extract for 15 hours to obtain extract S1 and raffinate D1, and then use a rotary evaporator to extract S1 Recovery, the residue after solvent recovery is n-heptane soluble matter, and the residue after solvent recovery is placed in a fume hood for ventilation for 3 hours to obtain heavy oil, which is 5g by weighing. The raffinate D1 is baked in an oven to constant weight, put it and 90g toluene into the Soxhlet extractor, heat to 125°C, extract S2 and raffinate D2 after extraction for 12 hours, and then extract the obtained extract S2 Recover with a rotary evaporator, and the residu...

Embodiment 2

[0036] Step 1. Put coal tar in a reaction kettle with a mass of 1500 grams, heat it to 300° C. and distill it under reduced pressure for 2 hours (vacuum degree is 0.08 MPa), and take out the remaining material from the autoclave, which is the heavy component of coal tar. It is 750g.

[0037]Step 2. Put 50g of coal tar heavy fraction and 150g of n-pentane into a Soxhlet extractor, heat to 80°C, extract for 12 hours to obtain extract S1 and raffinate D1, and then use a rotary evaporator for the obtained extract S1 Recovery, the residue after solvent recovery is n-pentane soluble matter, and the residue after solvent recovery is placed in a fume hood for ventilation for 4 hours to obtain heavy oil, which is 5.01g by weighing. The raffinate D1 is baked in an oven to constant weight, put it and 135g xylene into a Soxhlet extractor, heat to 120°C, extract S2 and raffinate D2 after extraction for 14 hours, and then extract the obtained extract S2 is recovered by a rotary evaporator,...

Embodiment 3

[0040] Step 1. Put coal tar in a reaction kettle with a mass of 1500 grams, heat it to 280° C. and distill it under reduced pressure for 2 hours (vacuum degree is 0.08 MPa), and take out the remaining material from the autoclave, which is the heavy component of coal tar. It is 775g.

[0041] Step 2. Add 50g of coal tar heavy fraction and 200g of n-hexane into the Soxhlet extractor, heat to 90°C, extract for 12 hours to obtain extract S1 and raffinate D1, and then recover the obtained extract S1 with a rotary evaporator , the residue after solvent recovery is n-hexane soluble matter, and the residue after solvent recovery is placed in a fume hood to ventilate for 3 hours to obtain heavy oil, which is 5.12g by weighing. The raffinate D1 is baked in an oven to constant weight, put it and 180g of benzene into the Soxhlet extractor, heat to 120°C, extract S2 and raffinate D2 after extraction for 15 hours, and then extract the obtained extract S2 Recover with a rotary evaporator, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

A method for preparing spinnable pitch from coal tar is to distill the coal tar under high temperature and reduced pressure to obtain a heavy component of coal tar; extract the heavy component of coal tar with a primary extraction solvent to obtain a primary extract and a primary raffinate; After the solvent is recovered from the extract, heavy oil is obtained; the primary raffinate is dried and then extracted with a secondary extraction solvent to obtain a secondary extract and a secondary raffinate; the solvent is recovered from the secondary extract to obtain asphaltenes; The first-level raffinate is extracted with the third-level extraction solvent to obtain the third-level extract and the third-level raffinate; the third-level extract recovers the solvent for supply to obtain pre-asphaltenes; asphaltenes and pre-asphaltenes are uniformly mixed and put into a fixed-bed reactor Spinnable pitch was prepared by thermal condensation polymerization. The invention has the advantages of simple process, easy solvent recovery, low cost and high yield.

Description

technical field [0001] The invention belongs to a method for preparing spinnable pitch of pitch carbon fiber, in particular to a method for preparing spinnable pitch with coal tar as raw material. Background technique [0002] Pitch-based carbon fiber is a special fiber with a carbon content greater than 92% obtained by refining, spinning, pre-oxidizing, and carbonizing petroleum pitch or coal pitch. Due to its excellent thermodynamic properties, it is widely used in military and civilian fields. [0003] Coal tar heavy fraction is an organic mixture with complex composition and structure mainly composed of aromatic hydrocarbons. The series of products such as light oil and heavy fraction obtained from its deep processing are the basic raw materials for synthetic plastics, synthetic fibers and other industries. Among them, heavy oil and asphaltene (a mixture of asphaltenes and pre-asphaltenes) are important components of coal tar heavy components. Heavy oil is a heavy disti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10C3/08C10C3/06
CPCC10C3/06C10C3/08
Inventor 左萍萍申文忠曲世杰牛宏贤李充梅
Owner SHANXI INST OF COAL CHEM CHINESE ACAD OF SCI