A kind of method for preparing two-dimensional montmorillonite/cellulose composite filter membrane

A cellulose filter membrane and composite filter technology, which is applied in the field of preparing two-dimensional montmorillonite/cellulose composite filter membrane, can solve the influence of the composition of the filtrate, the weakened adsorption performance of the composite porous adsorption membrane, and the inability to effectively remove heavy metal ions and dyes and other problems, to achieve the effect of easy industrial production and simple preparation method

Active Publication Date: 2021-09-03
TONGJI UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, microfiltration membranes also have certain shortcomings: they cannot effectively remove pollutants such as heavy metal ions and dyes that may pose a threat to people's health in water.
The layered silicate powder used in this patent will permeate into the filtrate during use, thereby affecting the composition of the filtrate; the gradual loss of the silicate powder will also lead to a weakening of the adsorption performance of the composite porous adsorption membrane

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing two-dimensional montmorillonite/cellulose composite filter membrane
  • A kind of method for preparing two-dimensional montmorillonite/cellulose composite filter membrane
  • A kind of method for preparing two-dimensional montmorillonite/cellulose composite filter membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Using solid montmorillonite and pure water as a solvent, a two-dimensional montmorillonite solution with a solid-to-liquid ratio of 10 g / L was prepared, and ultrasonicated in a 90W probe ultrasonic breaker for 10 minutes with an ultrasonic interval of 5 seconds and 5 seconds. The montmorillonite solution after ultrasonication was centrifuged at 8000 rpm for 5 minutes, and the supernatant was taken to obtain a two-dimensional montmorillonite solution with a concentration of 3.35 mg / ml.

[0048] Place the mixed cellulose filter membrane with a pore size of 0.22 microns on the vacuum filter bottle, add 3 ml of two-dimensional montmorillonite solution to the Buchner funnel, turn on the circulating water vacuum pump, and filter out the two-dimensional montmorillonite solution. Water makes the two-dimensional montmorillonite tightly stacked on the surface of the cellulose microporous membrane. After air-drying at room temperature, a two-dimensional montmorillonite / cellulose c...

Embodiment 2

[0054] Choose pure water as a solvent, disperse the freeze-dried solid two-dimensional montmorillonite in an aqueous solution, prepare a 5 mg / ml two-dimensional montmorillonite solution, and ultrasonicate the two-dimensional montmorillonite solution at a power of 100W for 0.5 hours , fully dispersed to form a uniform two-dimensional montmorillonite solution.

[0055] Place the mixed cellulose filter membrane with a pore size of 0.22 microns on the vacuum filter bottle, add 2 ml of two-dimensional montmorillonite solution to the Buchner funnel, turn on the circulating water vacuum pump, and filter out the two-dimensional montmorillonite solution. Water makes the two-dimensional montmorillonite tightly stacked on the surface of the cellulose microporous membrane. After air-drying at room temperature, a two-dimensional montmorillonite / cellulose composite filter membrane was obtained.

[0056] The two-dimensional montmorillonite / cellulose composite filter membrane that this embod...

Embodiment 3

[0058] Using solid montmorillonite and pure water as a solvent, a montmorillonite solution with a solid-to-liquid ratio of 10 g / L was prepared, and the montmorillonite solution was stirred at 500 rpm for 3 days. The stirred montmorillonite solution was centrifuged at 8000 rpm for 5 minutes, and the supernatant was taken to obtain a two-dimensional montmorillonite solution with a concentration of 1 mg / ml.

[0059] Spray the two-dimensional montmorillonite solution evenly on the 0.22 micron cellulose filter membrane, after natural air-drying, spray evenly again, air-dry naturally, repeat the above steps 5 times, and obtain the two-dimensional montmorillonite / cellulose composite accumulated many times filter membrane.

[0060] The two-dimensional montmorillonite / cellulose composite filter membrane that this embodiment prepares filters the Pb of 20 milliliters 50mg / L 2+ Solution, the concentration after filtration is 1mg / L. It shows that the composite membrane has good performan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a two-dimensional montmorillonite / cellulose composite filter membrane, which comprises the following steps: (1) preparing a two-dimensional montmorillonite solution; (2) loading the two-dimensional montmorillonite solution by filtering On the microporous cellulose filter membrane; (3) drying the microporous cellulose filter membrane loaded with two-dimensional montmorillonite to obtain a two-dimensional montmorillonite / cellulose composite filter membrane, the two-dimensional montmorillonite is tightly stacked on The surface of the microporous cellulose membrane forms a negatively charged surface with a certain thickness. Compared with the existing technology, the two-dimensional montmorillonite / cellulose composite filter membrane can effectively remove heavy metal ions and cationic dye pollutants in water. The preparation method of the invention is simple and easy, has good repeatability and low product price, and the obtained two-dimensional montmorillonite / cellulose composite filter membrane can be used to remove pollutants such as heavy metal ions and cationic dyes in water.

Description

technical field [0001] The invention relates to the technical field of liquid membrane separation, in particular to a method for preparing a two-dimensional montmorillonite / cellulose composite filter membrane. Background technique [0002] Water resources are the material basis for human survival. With the development of the world economy, cities are increasing and expanding, and the water demand in various places is increasing, while the amount of available water resources is decreasing. The water resource crisis faced by human beings is intensifying. my country is one of the countries with extremely poor water resources. In recent years, my country's economy has developed rapidly, and the extensive development mode has brought serious water pollution problems, which directly aggravated the water resource crisis. Therefore, how to remove pollutants in water and improve the utilization rate of water resources has become the focus of current research. [0003] Membrane separ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/10B01D71/02B01D69/12B01D67/00C02F1/469C02F101/20C02F101/30
CPCB01D67/0079B01D69/12B01D71/02B01D71/10C02F1/469C02F2101/20C02F2101/308
Inventor 赵美林思劼秦瑶
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com